CN105837159A - 一种高性能中性瓷砖粘结材料 - Google Patents
一种高性能中性瓷砖粘结材料 Download PDFInfo
- Publication number
- CN105837159A CN105837159A CN201610155259.2A CN201610155259A CN105837159A CN 105837159 A CN105837159 A CN 105837159A CN 201610155259 A CN201610155259 A CN 201610155259A CN 105837159 A CN105837159 A CN 105837159A
- Authority
- CN
- China
- Prior art keywords
- bonding material
- tile bonding
- performance
- tile
- magnesium oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高性能中性瓷砖粘结材料，属于建筑化工材料技术领域。它包含的各组分及其重量百分比为：磷酸二氢氨10.0‑16.0%，氧化镁9.6‑30.0%，石英砂46.95‑61.25%，偏高岭土7.5‑15.0%，三聚磷酸钠1.2‑1.35%。它可用于各类墙地砖的粘结，具有早期强度发展快、粘结力强等优点；并且凝结硬化后呈中性，不会对玻璃质的马赛克造成腐蚀。
Description
技术领域
本发明涉及一种高性能中性瓷砖粘结材料，属于建筑化工材料技术领域。
背景技术
瓷砖作为一种装饰材料，被广泛地应用于建筑物的内外墙以及地面等部位的装饰装修工程中。然而，由于施工技术和粘结材料本身等问题，经常会出现瓷砖脱落而造成一些安全事故。如此同时，一些极富装饰性的高档马赛克也开始在建筑工程中的应用，由于其特殊的质感和颜色要求，在施工以及后期使用过程中务必要做到无损伤、无污染等技术要求。而目前，市场上出现的各类瓷砖粘结剂主要以硅酸盐水泥作为胶凝材料，辅以聚合物粉末和各类添加剂配制而成。如专利公开号：CN104310910A，专利名称：一种瓷砖粘结剂，该专利以普通硅酸盐水泥为胶凝材料，配以石英砂、可在分散乳胶粉、木质纤维、纤维素醚、减水剂和早强剂构成，通过配方优化，改善瓷砖粘结剂的抗滑移性和粘结性能。又如专利公开号：CN103224354A，专利名称：一种新型瓷砖粘结剂及其制备方法，该专利是将硅酸盐水泥、粉煤灰和石英砂三种骨料与羟丙基甲基纤维素、木质纤维两种辅料进行混合搅拌而成，具有成本低、良好的保水和粘结性能等。
从这些专利产品看，大多以硅酸盐水泥作为胶凝材料，其碱性较高，长时间使用容易出现泛碱现象，在瓷砖表面或者其间隙产生色彩沉积，极大影响装饰的美观性，更为重要的是当装饰表面为马赛克等玻璃类材质时，其碱性将对其产生严重腐蚀作用，使其表面丧失装饰效果，甚至脱落。此外，一些形体较大的文化砖也开始在墙体上进行粘贴施工，由于传统的硅酸盐水泥体系的瓷砖粘结剂其凝结硬化时间较长且粘结强度有限，难以满足这类工程施工及粘结强度性能需求。因此，急需开发一种高效能的快速凝结硬化中性无污染的瓷砖粘结材料。
发明内容
本发明所要解决的技术问题在于：提供一种高性能中性瓷砖粘结材料，它解决了普通瓷砖粘结剂的粘结强度低，施工速度慢，且凝结硬化后呈碱性，会对玻璃质的马赛克造成腐蚀。
本发明所要解决的技术问题采取以下技术方案来实现：
一种高性能中性瓷砖粘结材料，它包含的各组分及其重量百分比为：磷酸二氢氨10.0-16.0%，氧化镁9.6-30.0%，石英砂46.95-61.25%，偏高岭土7.5-15.0%，三聚磷酸钠1.2-1.35%。
作为优选实例，所述磷酸二氢氨为工业级，纯度98%以上。
作为优选实例，所述氧化镁为重烧氧化镁，其溶解度常数为5-25，颗粒粒径320目。
作为优选实例，所述石英砂粒径在60-100目。
作为优选实例，所述偏高岭土为低温煅烧高岭土，颗粒粒径320目。
作为优选实例，所述三聚磷酸钠为食品级，纯度大于90%，含水量小于0.5%的粉末。
本发明的有益效果是：它可用于各类墙地砖的粘结，具有早期强度发展快、粘结力强、且凝结硬化后呈中性，不会对玻璃质的马赛克造成腐蚀。
具体实施方式
为了对本发明的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
一种高性能中性瓷砖粘结材料，它包含的各组分及其重量百分比为：磷酸二氢氨10.0-16.0%，氧化镁9.6-30.0%，石英砂46.95-61.25%，偏高岭土7.5-15.0%，三聚磷酸钠1.2-1.35%。磷酸二氢氨为工业级，纯度98%以上。氧化镁为重烧氧化镁，其溶解度常数为5-25，颗粒粒径320目。石英砂粒径在60-100目。偏高岭土为低温煅烧高岭土，颗粒粒径320目。三聚磷酸钠为食品级，纯度大于90%，含水量小于0.5%的粉末。
本发明的制备方法是：按配方比例称取所需的重烧氧化镁、磷酸二氢氨、三聚磷酸钠、偏高岭土和石英砂，在搅拌机中充分搅拌均匀，形成产品，进行装袋。施工现场使用时，根据基层材料和性能要求，加入材料重量16-20%的拌和水在搅拌机中充分搅拌2-3分钟，然后进行施工。
实施例1
本实施例中各组分及其重量百分比为：磷酸二氢氨16.0%，氧化镁9.6%，石英砂58.55%，偏高岭土14.4%，三聚磷酸钠1.2% 。
上述组分按前述制备方法进行充分混合均匀制成瓷砖粘结材料。
实施例2
本实施例中各组分及其重量百分比为：磷酸二氢氨12.5%，氧化镁 30.0%，石英砂47.4%，偏高岭土7.5%，三聚磷酸钠2.25%。
上述组分按前述制备方法进行充分混合均匀制成瓷砖粘结材料。
实施例3
本实施例中各组分及其重量百分比为：磷酸二氢氨14.5%，氧化镁21.25%，石英砂46.95%，偏高岭土15.0%，三聚磷酸钠1.8%。
上述组分按前述制备方法进行充分混合均匀制成瓷砖粘结材料。
实施例4
本实施例中各组分及其重量百分比为：磷酸二氢氨10.0%，氧化镁15.0%，石英砂61.25%，偏高岭土12.0%，三聚磷酸钠1.35%。
上述组分按前述制备方法进行充分混合均匀制成瓷砖粘结材料。
对以上实施例构成的粘结材料参照《陶瓷墙地砖胶粘剂》（JG/T 547-2005）检验产品性能。效果和参数如下：
根据试验结果可以看出，与硅酸盐基的瓷砖粘结剂相比，本发明的粘结材料具有非常高的粘结强度，超出了几倍，可以用于一些石材的粘结。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (6)
1.一种高性能中性瓷砖粘结材料，其特征在于：它包含的各组分及其重量百分比为：磷酸二氢氨10.0-16.0%，氧化镁9.6-30.0%，石英砂46.95-61.25%，偏高岭土7.5-15.0%，三聚磷酸钠1.2-1.35%。
2.根据权利要求1所述一种高性能中性瓷砖粘结材料，其特征在于：所述磷酸二氢氨为工业级，纯度98%以上。
3.根据权利要求1所述一种高性能中性瓷砖粘结材料，其特征在于：所述氧化镁为重烧氧化镁，其溶解度常数为5-25，颗粒粒径320目。
4.根据权利要求1所述一种高性能中性瓷砖粘结材料，其特征在于：所述石英砂粒径在60-100目。
5.根据权利要求1所述一种高性能中性瓷砖粘结材料，其特征在于：所述偏高岭土为低温煅烧高岭土，颗粒粒径320目。
6.根据权利要求1所述一种高性能中性瓷砖粘结材料，其特征在于：所述三聚磷酸钠为食品级，纯度大于90%，含水量小于0.5%的粉末。