CN105601157B - 一种用于普通硅酸盐水泥的早强防水剂 - Google Patents
一种用于普通硅酸盐水泥的早强防水剂 Download PDFInfo
- Publication number
- CN105601157B CN105601157B CN201510963751.8A CN201510963751A CN105601157B CN 105601157 B CN105601157 B CN 105601157B CN 201510963751 A CN201510963751 A CN 201510963751A CN 105601157 B CN105601157 B CN 105601157B
- Authority
- CN
- China
- Prior art keywords
- parts
- portland cement
- waterproofing agent
- morning
- strong waterproofing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种用于普通硅酸盐水泥的早强防水剂，按照重量份数比包含以下组分原料：硫酸钙100‑300份、甜菜碱5‑10份、氢氧化钠100‑300份、硬脂酸5‑10份、脂肪酸钠0.5‑1份，卵磷脂0.2‑0.5份、氢化松香0.2‑0.6份、羧甲基纤维素钠0.2‑0.4份。本发明早强防水剂无毒无污染，不会产生对人体或环境有毒有害的物质或气体，使用过程中较为绿色、环保；同时，本发明早强防水剂能快速的促进普通硅酸盐水泥早期强度，而且防水性能极佳。
Description
技术领域
本发明涉及一种早强防水剂，特别涉及一种用于普通硅酸盐水泥的早强防水剂。
背景技术
混凝土早强剂是外加剂发展历史中最早使用的外加剂品种之一。到目前为止，人们已先后开发除氯盐和硫酸盐以外的多种早强型外加剂，如亚硝酸盐，铬酸盐等；以及有机物早强剂，如三乙醇胺、甲酸钙、尿素等。并且在早强剂的基础上，生产应用多种复合型外加剂，如早强减水剂、早强防冻剂和早强型泵送剂等。早强剂尽管生产和应用历史较长，但随着人们对氯离子、硫酸根离子、硝酸根离子和碱金属离子等对混凝土性能和长期稳定性潜在危害的认识程度的加深，以及大掺量矿渣粉或粉煤灰混凝土的开发，在早强剂方面还需做大量的工作。早强剂主要作用是增加水泥和水的反应速度，缩短水泥的凝结、硬化时间，促进混凝土早期强度的增长。防水剂可以提高混凝土的抗渗性能，使混凝土的质量吸水量率减少，耐久性也明显提高。现有技术中的早强防水剂因添加的成分，虽能强化早强防水剂的作用，但是同时也对人体造成伤害或者环境造成污染。而现今致力研究一种对人体伤害小、环保、绿色、高效的早强剂防水剂，从而满足有早强和防水要求的工程。
公开于该背景技术部分的信息仅仅旨在增加对本发明的总体背景的理解，而不应当被视为承认或以任何形式暗示该信息构成已为本领域一般技术人员所公知的现有技术。
发明内容
本发明的目的在于提供一种用于普通硅酸盐水泥的早强防水剂，从而克服现有技术中使用对人体、环境有伤害或影响的添加剂作为早强防水剂的缺点。
为实现上述目的，本发明提供的技术方案如下：
一种用于普通硅酸盐水泥的早强防水剂，按照重量份数比包含以下组分原料：硫酸钙100-300份、甜菜碱5-10份、氢氧化钠100-300份、硬脂酸5-10份、脂肪酸钠0.5-1份，卵磷脂0.2-0.5份、氢化松香0.2-0.6份、羧甲基纤维素钠0.2-0.4份。
优选的是，所述的氢化松香为0.3-0.4份。
优选的是，所述的氢化松香为粒度为150-250目的粉末。
使用上述用于普通硅酸盐水泥的早强防水剂时，早强防水剂：普通硅酸盐水泥成1-3:100重量比。
与现有技术相比，本发明具有如下有益效果：
本发明用于普通硅酸盐水泥的早强防水剂无毒无污染，不会产生对人体或环境有毒有害的物质或气体，使用过程中较为绿色、环保；同时，本发明用于普通硅酸盐水泥的早强防水剂能快速的促进普通硅酸盐水泥早期强度，而且防水性能极佳。
具体实施方式
下面结合具体实施方式进行详细描述，但应当理解本发明的保护范围并不受具体实施方式的限制。
实施例1
以g为单位，称取以下组分原料：硫酸钙200g、甜菜碱7g、氢氧化钠200g、硬脂酸8g、脂肪酸钠0.7g，卵磷脂.0.4g、粒度为250目的氢化松香粉末0.4g、羧甲基纤维素钠0.3g、芸香甙0.01g，将上述各原料混合搅拌均匀，即得用于普通硅酸盐水泥的早强防水剂，备用。
称取普通硅酸盐水泥200g，石英沙子50g，所述的石英沙子使用前用质量浓度50％的碱水浸泡5h，粉煤灰5g，萘磺酸盐甲醛缩合物高效减水剂10g，直径为10-15mm的碎石头50g，上述制备所得4g用于普通硅酸盐水泥的早强防水剂。将称取所得普通硅酸盐水泥、石英沙子、粉煤灰、萘磺酸盐甲醛缩合物高效减水剂、碎石头放入搅拌机中加水进行混合搅拌10min，在拌和普通硅酸盐水泥过程中加入上述称取所得用于普通硅酸盐水泥的早强防水剂，继续搅拌8min，即得普通硅酸盐水泥混合物，将所得普通硅酸盐水泥混合物在标准养护条件下进行养护并根据《普通混凝土力学性能试验标准》GB/T50081－2002及《砂浆、混凝土防水剂》JC474－1999试验规范，检测得混凝土l、3、7d的抗压强度和28d的抗压强度，以及28d龄期普通硅酸盐水泥混合物质量吸水量率。
质量吸水量率的测试：将28d龄期的普通硅酸盐水泥混合物放入烘箱中，在80℃下烘48h，烘干后称取试件质量并记下，在自然条件下将试件冷却至室温，然后放入水中，试件在水面上下的尺寸各50mm并保持水面高度不变，48h后用拧干的抹布擦干试件表面，称取饱和吸水后试件的质量，将饱和吸水的试件质量减去干试件的质量即为质量吸水量率。
上述实施例中所得数据如表1中数据所示。
实施例2
以g为单位，称取以下组分原料：硫酸钙100g、甜菜碱5g、氢氧化钠100g、硬脂酸5g、脂肪酸钠0.5g，卵磷脂0.2g、粒度为150目的氢化松香粉末0.2g、羧甲基纤维素钠0.2g，将上述各原料混合搅拌均匀，即得用于普通硅酸盐水泥的早强防水剂，备用。
称取普通硅酸盐水泥200g，石英沙子50g，所述的石英沙子使用前用质量浓度50％的碱水浸泡6h，粉煤灰5g，萘磺酸盐甲醛缩合物高效减水剂10g，直径为10-15mm的碎石头50g，上述制备所得2g用于普通硅酸盐水泥的早强防水剂。将称取所得普通硅酸盐水泥、石英沙子、粉煤灰、萘磺酸盐甲醛缩合物高效减水剂、碎石头放入搅拌机中加水进行混合搅拌15min，在拌和普通硅酸盐水泥过程中加入上述称取所得用于普通硅酸盐水泥的早强防水剂，继续搅拌5min，即得普通硅酸盐水泥混合物，将所得普通硅酸盐水泥混合物在标准养护条件下进行养护并根据《普通混凝土力学性能试验标准》GB/T50081－2002及《砂浆、混凝土防水剂》JC474－1999试验规范，检测得混凝土l、3、7d的抗压强度和28d的抗压强度，以及28d龄期普通硅酸盐水泥混合物质量吸水量率。
质量吸水量率的测试与实施例1中相同。
上述实施例中所得数据如表1中数据所示。
实施例3
以g为单位，称取以下组分原料：硫酸钙300g、甜菜碱10g、氢氧化钠300g、硬脂酸10g、脂肪酸钠1g，卵磷脂0.5g、粒度为200目的氢化松香粉末0.6g、羧甲基纤维素钠0.4g，将上述各原料混合搅拌均匀，即得用于普通硅酸盐水泥的早强防水剂，备用。
称取普通硅酸盐水泥200g，石英沙子50g，所述的石英沙子使用前用质量浓度50％的碱水浸泡5h，粉煤灰5g，萘磺酸盐甲醛缩合物高效减水剂10g，直径为10-15mm的碎石头50g，上述制备所得6g用于普通硅酸盐水泥的早强防水剂。将称取所得普通硅酸盐水泥、石英沙子、粉煤灰、萘磺酸盐甲醛缩合物高效减水剂、碎石头放入搅拌机中加水进行混合搅拌5min，在拌和普通硅酸盐水泥过程中加入上述称取所得用于普通硅酸盐水泥的早强防水剂，继续搅拌10min，即得普通硅酸盐水泥混合物，将所得普通硅酸盐水泥混合物在标准养护条件下进行养护并根据《普通混凝土力学性能试验标准》GB/T50081－2002及《砂浆、混凝土防水剂》JC474－1999试验规范，检测得混凝土l、3、7d的抗压强度和28d的抗压强度，以及28d龄期普通硅酸盐水泥混合物质量吸水量率。
质量吸水量率的测试与实施例1中相同。
上述实施例中所得数据如表1中数据所示。
对比实施例1
以g为单位，称取以下组分原料：硫酸铝30g、脂肪酸盐10g、三乙醇胺1g、无水硫酸钠20g，将上述各原料混合搅拌均匀，即得早强防水剂，备用。
称取普通硅酸盐水泥200g，细度模数为2.8的中砂90g，粉煤灰4g，萘磺酸盐甲醛缩合物高效减水剂10g，碎石50g。将称取所得普通硅酸盐水泥、中砂、粉煤灰、萘磺酸盐甲醛缩合物高效减水剂、碎石放入搅拌机中加水进行混合搅拌15min，在拌和普通硅酸盐水泥过程中加入上述制备所得早强防水剂，继续搅拌8min，即得普通硅酸盐水泥混合物，将所得普通硅酸盐水泥混合物在标准养护条件下进行养护并根据《普通混凝土力学性能试验标准》GB/T50081－2002及《砂浆、混凝土防水剂》JC474－1999试验规范，检测得混凝土l、3、7d的抗压强度和28d的抗压强度，以及28d龄期普通硅酸盐水泥混合物质量吸水量率。
质量吸水量率的测试与实施例1中相同。
上述实施例中所得数据如表1中数据所示。
表1
由表1中可以看出，本发明用于普通硅酸盐水泥的早强防水剂在1-7d抗压强度与对比实施例1相比强度增大，到28d的时候，差距更大，说明本发明用于普通硅酸盐水泥的早强防水剂能大大促使水泥早期强度；而且本发明产品质量吸水量率与对比实施例1相比，本发明产品质量吸水量率更低，防水效果极其明显。
前述对本发明的具体示例性实施方案的描述是为了说明和例证的目的。这些描述并非想将本发明限定为所公开的精确形式，并且很显然，根据上述教导，可以进行很多改变和变化。对示例性实施例进行选择和描述的目的在于解释本发明的特定原理及其实际应用，从而使得本领域的技术人员能够实现并利用本发明的各种不同的示例性实施方案以及各种不同的选择和改变。本发明的范围意在由权利要求书及其等同形式所限定。
Claims (4)
1.一种用于普通硅酸盐水泥的早强防水剂，其特征在于，按照重量份数比包含以下组分原料：硫酸钙100-300份、甜菜碱5-10份、氢氧化钠100-300份、硬脂酸5-10份、脂肪酸钠0.5-1份，卵磷脂0.2-0.5份、氢化松香0.2-0.6份、羧甲基纤维素钠0.2-0.4份。
2.根据权利要求1所述用于普通硅酸盐水泥的早强防水剂，其特征在于：所述的氢化松香为0.3-0.4份。
3.根据权利要求1所述用于普通硅酸盐水泥的早强防水剂，其特征在于：所述的氢化松香为粒度为150-250目的粉末。
4.如权利要求1所述的早强防水剂用于普通硅酸盐水泥，其特征在于：早强防水剂：普通硅酸盐水泥成1-3:100重量比。