CN105543607A - 一种合金材料 - Google Patents
一种合金材料 Download PDFInfo
- Publication number
- CN105543607A CN105543607A CN201510961369.3A CN201510961369A CN105543607A CN 105543607 A CN105543607 A CN 105543607A CN 201510961369 A CN201510961369 A CN 201510961369A CN 105543607 A CN105543607 A CN 105543607A
- Authority
- CN
- China
- Prior art keywords
- parts
- alloy material
- dioxide
- powder
- silicon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种合金材料，其按重量份比其由以下组分组成：碳化钨粉45～65份；镍粉？15～35份；铜粉15～35份；二氧化钴15～24份；二氧化硅5～8份；氟硅酸钾1～3份。本发明提供的合金材料通过原料创新使其具有极强的耐磨性能和耐腐蚀性能，从而能够适用于制备应用于具有腐蚀性和耐磨损度要求高的环境的部件，具有广阔的市场前景。
Description
技术领域
本发明涉及合金材料领域，尤其涉及一种耐磨性能极好的特种合金材料。
背景技术
合金材料通常是通过在主材料适量地加入一种或几种合金元素，使合金的组织结构发生变化，从而使合金具有各种不同的特殊性能。随着生产力的不断发展，工业用特种合金材料的使用需求不断提高，现有的特种合金已渐渐无法满足市场的需求。
发明内容
本发明的目的在于提供一种合金材料，旨在提供一种具有良好耐磨性能的合金材料。
本发明的技术方案如下：
一种合金材料，其中，按重量份比其由以下组分组成：
碳化钨粉45～65份；
镍粉15～35份；
铜粉15～35份；
二氧化钴15～24份；
二氧化硅5～8份；
氟硅酸钾1～3份。
所述的合金材料，其中，按重量份比其由以下组分组成：
碳化钨粉50份；
镍粉20份；
铜粉20份；
二氧化钴18份；
二氧化硅6份；
氟硅酸钾2份。
所述的合金材料，其中，所述镍粉和铜粉的添加量比例为1:1。
所述的合金材料，其中，所述二氧化钴和二氧化硅的添加比例为3:1。
有益效果：本发明提供一种合金材料，该合金材料通过原料创新使其具有极强的耐磨性能和耐腐蚀性能，从而能够适用于制备应用于具有腐蚀性和耐磨损度要求高的环境的部件，具有广阔的市场前景。
具体实施方式
为使本发明的目的、技术方案及优点更加清楚、明确，以下对本发明进一步详细说明。
本发明提供一种合金材料，其中，按重量份比其由以下组分组成：
碳化钨粉45～65份；
镍粉15～35份；
铜粉15～35份；
二氧化钴15～24份；
二氧化硅5～8份；
氟硅酸钾1～3份。
其中，较佳实施例中，所述镍粉和铜粉的添加量比例为1:1。
并且，优选的是，所述二氧化钴和二氧化硅的添加比例为3:1。
下面通过实施例进一步阐述本发明的技术方案。
实施例1
所述的合金材料，其中，按重量份比其由以下组分组成：
碳化钨粉50份；
镍粉20份；
铜粉20份；
二氧化钴18份；
二氧化硅6份；
氟硅酸钾2份。
实施例2
所述的合金材料，其中，按重量份比其由以下组分组成：
碳化钨粉65份；
镍粉35份；
铜粉35份；
二氧化钴24份；
二氧化硅8份；
氟硅酸钾1份。
本发明提供一种合金材料，该合金材料通过原料创新使其具有极强的耐磨性能和耐腐蚀性能，从而能够适用于制备应用于具有腐蚀性和耐磨损度要求高的环境的部件，具有广阔的市场前景。
应当理解的是，本发明的应用不限于上述的举例，对本领域普通技术人员来说，可以根据上述说明加以改进或变换，所有这些改进和变换都应属于本发明所附权利要求的保护范围。
Claims (4)
1.一种合金材料，其特征在于，按重量份比其由以下组分组成：
碳化钨粉45～65份；
镍粉15～35份；
铜粉15～35份；
二氧化钴15～24份；
二氧化硅5～8份；
氟硅酸钾1～3份。
2.根据权利要求1所述的合金材料，其特征在于，按重量份比其由以下组分组成：
碳化钨粉50份；
镍粉20份；
铜粉20份；
二氧化钴18份；
二氧化硅6份；
氟硅酸钾2份。
3.根据权利要求1所述的合金材料，其特征在于：所述镍粉和铜粉的添加量比例为1:1。
4.根据权利要求1所述的合金材料，其特征在于：所述二氧化钴和二氧化硅的添加比例为3:1。