CN104893046A - 一种耐油耐磨橡胶 - Google Patents
一种耐油耐磨橡胶 Download PDFInfo
- Publication number
- CN104893046A CN104893046A CN201510342867.XA CN201510342867A CN104893046A CN 104893046 A CN104893046 A CN 104893046A CN 201510342867 A CN201510342867 A CN 201510342867A CN 104893046 A CN104893046 A CN 104893046A
- Authority
- CN
- China
- Prior art keywords
- rubber
- oil
- produces
- resistant
- cyclohexyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐油耐磨橡胶，其成分中含有下列物质：端羧基液态丁腈橡胶、丁腈1041、辛基酚醛树脂、氧化锌、硬脂酸、N-环己基-N-苯基对苯二胺、2,2,4-三甲基1,2-二氢化喹啉、炭黑N660、邻苯二甲酸二丁酯、N-环己基-2-苯并噻唑次磺酰胺、二硫化二苯并噻唑、二硫化四甲基秋兰姆、硫磺。与现有技术相比，本发明在40℃C液体中48小时后,体积溶胀＜50%，耐油耐磨性能较好，本发明适用于海洋排吸油胶管内衬层中。
Description
技术领域
本发明涉一种橡胶，具体说是一种用于海洋排吸油胶管内衬层的耐油耐磨橡胶。
背景技术
海洋排吸油胶管内衬层是输导原油或液体石油产品的工作面，对所用橡胶的耐油性能有一定要求，要求这种橡胶置于40℃的C液体中40h，体积膨胀率不超过60%；同时需要耐磨。目前传统的普通橡胶的耐油耐磨性能达不到这个要求，因而不能用于海洋排吸油胶管内衬层的制造。
发明内容
为了克服上述问题，本发明的目的是提供一种耐油耐磨橡胶，这种橡胶置于40℃的C液体中40h，体积膨胀率不超过50%，耐油耐磨性能好，可以满足海洋排吸油胶管内衬层的性能要求。
本发明的目的通过以下技术方案实现：
一种耐油耐磨橡胶，含有以下质量分的物质：
端羧基液态丁腈橡胶 70-80
丁腈（1041）橡胶 50-60
辛基苯酚树脂 5-10
氧化锌 4-8
硬脂酸 1.5-3.0
N-环己基-2-苯并噻唑次磺酰胺 0.5-1.5
二硫化二苯并噻唑 0.1-0.5
二硫化二甲基秋兰姆 0.1-0.5
N-异丙基-N′-苯基对苯二胺 1-3
2,2,4-三甲基1,2-二氢化喹啉 1-3
炭黑N660 50-85
邻苯二甲酸二丁酯 5-10
硫磺 1-3
本发明的橡胶制备方法与现有的制备方法相同。
本发明与现有技术相比，置于40℃的C液体中40h，体积膨胀率不超过50%，耐油耐磨性能好。本发明可以满足海洋排吸油胶管内衬层的性能要求。
具体实施方式
下面结合实施例对本发明做详细说明。
实例1
一种用于海洋排吸油胶管内衬层的耐油耐磨橡胶，含有以下质量分的物质：
端羧基液态丁腈橡胶 70
丁腈（1041）橡胶 50
辛基苯酚树脂 5.5
氧化锌 5
硬脂酸 1.5
N-环己基-2-苯并噻唑次磺酰胺 1.0
二硫化二苯并噻唑 0.6
二硫化二甲基秋兰姆 0.2
N-异丙基-N′-苯基对苯二胺 1.2
2,2,4-三甲基1,2-二氢化喹啉 1.2
炭黑N660 70
邻苯二甲酸二丁酯 6.0
硫磺 1.2
其中，端羧基液态丁腈橡胶是美国Emerald端羧基液态丁腈橡胶；丁腈（1041）橡胶为台湾南帝产1041丁腈橡胶；辛基酚醛树脂为无锡宾王化工厂产；氧化锌为扬州振中锌业有限公司产；硬脂酸为印尼PALMATA 1801公司产；N-异丙基-N′-苯基对苯二胺为南京化学工业有限公司生产；2,2,4-三甲基1,2-二氢化喹啉为天津科迈化工有限公司生产；N-环己基-2-苯并噻唑次磺酰胺由天津拉勃助剂公司生产；二硫化二苯并噻唑由天津拉勃助剂公司生产；炭黑N660为江西黑猫炭黑股份有限公司生产；邻苯二甲酸二丁酯为苏州市金运化工有限公司生产；硫磺为镇江润旺化工公司生产。
以上配方制作的橡胶置于40℃的C液体中40h，体积膨胀率为40%。耐油耐磨性能好。
实施例2
又一种用于海洋排吸油胶管内衬层的耐油耐磨橡胶，含有以下质量分的物质：
端羧基液态丁腈橡胶 80
丁腈（1041）橡胶 60
辛基苯酚树脂 5.3
氧化锌 5
硬脂酸 1.6
N-环己基-2-苯并噻唑次磺酰胺 1.1
二硫化二苯并噻唑 0.5
二硫化二甲基秋兰姆 0.3
N-异丙基-N′-苯基对苯二胺 1.3
2,2,4-三甲基1,2-二氢化喹啉 1.3
炭黑N660 75
邻苯二甲酸二丁酯 6.0
硫磺 1.2
以上配方制作的橡胶置于40℃的C液体中40h，体积膨胀率为42%。
Claims (4)
1.一种耐油耐磨橡胶，其特征在于：该耐油耐磨橡胶含有以下质量分的物质：
端羧基液态丁腈橡胶 70-80
丁腈1041橡胶 50-60
辛基苯酚树脂 5-10
氧化锌 4-8
硬脂酸 1.5-3.0
N-环己基-2-苯并噻唑次磺酰胺 0.5-1.5
二硫化二苯并噻唑 0.1-0.5
二硫化二甲基秋兰姆 0.1-0.5
N-异丙基-N′-苯基对苯二胺 1-3
2,2,4-三甲基1,2-二氢化喹啉 1-3
N-环己基硫代二甲酰亚胺 0.1-0.3
炭黑N660 50-85
邻苯二甲酸二丁酯 5-10
硫磺 1-3。
2.根据权利要求1所述的耐油耐磨橡胶，其特征在于：端羧基液态丁腈橡胶是美国Emerald端羧基液态丁腈橡胶；丁腈橡胶为台湾南帝产1041丁腈橡胶；辛基酚醛树脂为无锡宾王化工厂产。
3.根据权利要求1所述的耐油耐磨橡胶，其特征在于：氧化锌为扬州振中锌业有限公司产；硬脂酸为印尼PALMATA 1801公司产；N-异丙基-N′-苯基对苯二胺为南京化学工业有限公司生产；2,2,4-三甲基1,2-二氢化喹啉为天津科迈化工有限公司生产；N-环己基-2-苯并噻唑次磺酰胺由天津拉勃助剂公司生产；二硫化二苯并噻唑由天津拉勃助剂公司生产；炭黑N660为江西黑猫炭黑股份有限公司生产；邻苯二甲酸二丁酯为苏州市金运化工有限公司生产；硫磺为镇江润旺化工公司生产。
4.根据权利要求1所述的耐油耐磨橡胶，其特征在于：该耐油橡胶含有以下质量分的物质：
端羧基液态丁腈橡胶 70
丁腈（1041）橡胶 50
辛基苯酚树脂 5.3
氧化锌 5
硬脂酸 1.6
N-环己基-2-苯并噻唑次磺酰胺 1.1
二硫化二苯并噻唑 0.5
二硫化二甲基秋兰姆 0.3
N-异丙基-N′-苯基对苯二胺 1.3
2,2,4-三甲基1,2-二氢化喹啉 1.3
炭黑N660 75
邻苯二甲酸二丁酯 6.0
硫磺 1.2。