CN104403400B - 一种抗裂腻子及其使用方法 - Google Patents
一种抗裂腻子及其使用方法 Download PDFInfo
- Publication number
- CN104403400B CN104403400B CN201410829007.4A CN201410829007A CN104403400B CN 104403400 B CN104403400 B CN 104403400B CN 201410829007 A CN201410829007 A CN 201410829007A CN 104403400 B CN104403400 B CN 104403400B
- Authority
- CN
- China
- Prior art keywords
- parts
- glue
- powder
- coalescents
- putty
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种抗裂腻子及其使用方法，所述的抗裂腻子包含胶液和粉料，所述的胶液主要成分包括丙烯酸乳液、消泡剂、成膜助剂、防冻剂、羟丙基甲基纤维素、无机泥胶和水，所述的粉料主要成分包括水泥、重钙、灰钙、石英砂、超短纤维和木质纤维，本发明使用时，胶液和粉料按照质量分数3:5混合。该抗裂腻子具有粘结强度高，拉伸强度高，动态抗开裂性指标达到R型指标，密度小，涂布量大，抗裂效果好特点。
Description
技术领域
本发明属于建材领域，尤其涉及一种抗裂腻子及其使用方法。
背景技术
腻子是平整墙体表面的一种装饰凝材料，是一种厚浆状涂料，是涂料粉刷前必不可少的一种产品。涂施于底漆上或直接涂施于物体上，用以清除被涂物表面上高低不平的缺陷。采用少量漆基、大量填料及适量的着色颜料配制而成，所用颜料主要是铁红、炭黑、铬黄等，填料主要是重碳酸钙、滑石粉等。腻子可填补局部有凹陷的工作表面，也可在全部表面刮除，通常是在底漆干透后，施涂于底漆表面，要求附着性好、烘烤过程中不产生裂纹。目前，建筑墙体的装饰普遍使用传统的腻子粉，该腻子粉用白乳胶、107 胶、钛白粉等制成，这种材料存在附着力差、不耐水、使用寿命短等缺点，并且墙体表面易卷皮、掉渣、龟裂、脱粉等。
发明内容
为了解决以上技术难题，本发明提供一种粘结强度高，拉伸强度高，动态抗开裂性指标达到R型指标，密度小，涂布量大，抗裂效果好，施工性能好的抗裂腻子。
为实现上述目的，本发明采用如下技术方案：
一种抗裂腻子包含胶液和粉料，其中所述的胶液主要成分包括丙烯酸乳液、消泡剂、成膜助剂、防冻剂、羟丙基甲基纤维素、无机泥胶和水，所述的粉料主要成分包括水泥、重钙、灰钙、石英砂、超短纤维和木质纤维。
优选的，所述的胶液包含下列主要成分的重量份数为丙烯酸乳液35 -40份，消泡剂0.3 -1份，成膜助剂0.5 -1份，防冻剂0.9 -1.5份，羟丙基甲基纤维素8-20份，无机泥胶8-20份，水20-70份；所述的粉料包含下列主要成分的重量份数为水泥30 -35份，重钙35 -40份,灰钙15 -20份,石英砂30 -35份,超短纤维2-10份，木质纤维4-18份。
一种抗裂腻子，包括胶液与粉料，其主要成分的重量份数可以有以下各种优选方案：
方案一
本发明所述的胶液包含主要成分的重量份数如下：丙烯酸乳液40份，消泡剂1份，成膜助剂1份，防冻剂1.5份，羟丙基甲基纤维素20份，无机泥胶20份，水70份；所述的粉料主要成分的重量份数如下：水泥35份，重钙40份，灰钙20份，石英砂35份，超短纤维10份，木质纤维18份。
方案二
本发明所述的胶液包含主要成分的重量份数如下：丙烯酸乳液35份，消泡剂0.3份，成膜助剂0.5份，防冻剂0.9份，羟丙基甲基纤维素10份，无机泥胶10份，水35份；所述的粉料主要成分的重量份数如下水泥30份，重钙35份，灰钙15份，石英砂30份，超短纤维7份，木质纤维12份。
方案三
本发明所述的胶液主要成分的重量份数如下：丙烯酸乳液38份，消泡剂0.5份，成膜助剂0.8份，防冻剂1.2份，羟丙基甲基纤维素15份，无机泥胶15份，水53份；所述的粉料主要成分的重量份数如下：水泥32份，重钙38份，灰钙18份，石英砂32份,超短纤维5份，木质纤维9份。
优选的，所述的成膜助剂为智索成膜助剂，成膜助剂又称聚结助剂，能促进高分子化合物塑性流动和弹性变形，改善聚结性能，能在较广泛施工温度范围内成膜的物质，是一种易消失的增塑剂。
优选的，所述的防冻剂为乙二醇防冻剂，防冻剂能使混凝土在负温下硬化，并在规定养护条件下达到预期性能的外加剂，它是一种能在低温下防止物料中水分结冰的物质，所述的防冻剂，为市售常规品，所述的防冻剂易溶于水，故在运输、贮存过程中注意防潮，防水，所述的防冻剂采用防潮编织袋包装，每袋净重50kg±0.5kg。
优选的，所述的超短纤维是直径为3mm的纤维，纤维技术与混凝土技术相结合，可研制出能改善混凝土性能，提高土建工程质量的钢纤维以及合成纤维，木质纤维可以提高系统抗腐蚀性，提高施工或预制件的精度，具有很强的防冻和防热能力，改善混凝土的耐久性，抗老化性，提高系统的稳定性、强度、密实度和均匀度，具有优良的保温、隔热、隔声、绝缘和透气性能。
优选的，所述的水泥颗粒大小为50-200目，水泥作为一种重要的胶凝材料，广泛应用于土木建筑、水利、国防等工程。
优选的，所述的灰钙颗粒大小为300-400目，所述的重钙颗粒大小为300-400目，本发明重钙是由天然碳酸盐矿物如方解石、大理石、石灰石磨碎而成。在涂料和塑料行业，“重钙”就是方解石粉，主要成分是重质碳酸钙，通常用作填料，作填充剂起到增加产品的体积，降低生产成本。具有化学纯度高、惰性大、不易化学反应、热稳定性好、在400℃以下不会分解、白度高、吸油率低、折光率低、质软、干燥、不含结晶水、硬度低磨耗值小、无毒、无味、无臭、分散性好等优点。
优选的，所述的石英砂颗粒大小为80-120目，本发明所述的石英砂主要矿物成分是SiO2，它是一种非金属矿物质，是一种坚硬、耐磨、化学性能稳定的硅酸盐矿物，可提高涂料的耐酸性，石英砂的颜色为乳白色、半透明状和透明状，莫氏硬度7，石英砂是重要的工业矿物原料，非化学危险品，广泛用于玻璃、铸造、陶瓷及耐火材料、冶炼硅铁、冶金熔剂、冶金、建筑、化工、塑料、橡胶等工业。
此外，本发明还提供了抗裂腻子的使用方法，包括以下步骤：
（1）原料混合：胶液和粉料按照质量份数3:5进行混合，先将胶液倒入容器中，一边搅拌一边加粉料，搅拌均匀无粉团，静置十分钟后施工；
（2）清理墙面：严重粉化墙面先用草酸清洗，再用清水冲洗干净，保证墙面充分干燥，保证基层含水率小于10%，墙面pH值小于10。
（3）刮腻子：用批嵌工具批刮腻子,每次批嵌厚度1-3mm，每遍腻子的用量为1-5kg/m²,待腻子实干后方进行下一道腻子的批嵌，批嵌最后一道腻子时如有接茬，及时用羊毛刷蘸水梳理平整,为使墙面达到所要求的平整度，用刮尺水平方向和竖直方向刮涂，腻子表干后立即选用100-150#砂纸打磨并除去表面灰尘，腻子实干后进行下道工序施工。
本发明是以性能优异的丙烯酸乳液为主要成膜物质，采用巴斯夫助剂、智索成膜助剂和乙二醇防冻剂等助剂为辅料,优质颜填料和轻质无机矿物填料物理混合而成的胶液和粉料腻子，具有粘结强度高，拉伸强度高，动态抗开裂性指标达到R型指标，密度小，涂布量大，抗裂效果好，施工性能好的特性，适用于各种建筑物墙面和外保温配套系统涂装工程。
具体实施方式
本发明结合下面实施例来予以阐明。
实施例1
一种抗裂腻子包含胶液和粉料，所述的胶液包含下列主要成分的重量份数为丙烯酸乳液40份，巴斯夫助剂1份，智索成膜助剂1份，乙二醇防冻剂1.5份，羟丙基甲基纤维素20份，无机泥胶20份，水70份，将上述成分均匀混合；所述的粉料包含下列主要成分的重量份数为水泥35份，重钙40份，灰钙20份，石英砂35份，直径为3mm纤维10份，木质纤维18份，将上述成分均匀混合。
实施例2
一种抗裂腻子包含胶液和粉料，所述的胶液包含下列主要成分的重量份数为丙烯酸乳液35份，巴斯夫助剂0.3份，智索成膜助剂0.5份，乙二醇防冻剂0.9份，羟丙基甲基纤维素10份，无机泥胶10份，水35份，将上述成分均匀混合；所述的粉料包含下列主要成分的重量份数为水泥30份，重钙35份，灰钙15份，石英砂30份，直径为3mm纤维7份，木质纤维12份，将上述成分均匀混合。
实施例3
一种抗裂腻子包含胶液和粉料，所述的胶液包含下列主要成分的重量份数为丙烯酸乳液38份，巴斯夫助剂0.5份，智索成膜助剂0.8份，乙二醇防冻剂1.2份，羟丙基甲基纤维素15份，无机泥胶15份，水53份，将上述成分均匀混合；所述的粉料包含下列主要成分的重量份数为水泥32份，重钙38份，灰钙18份，石英砂32份，直径为3mm纤维5份，木质纤维9份，将上述成分均匀混合。
实施例4
如以上3个具体实施例所述的抗裂腻子的使用方法，包括以下步骤：
（1）原料混合：胶液和粉料按照质量分数3:5进行混合，先将胶液倒入容器中，一边搅拌一边加粉料，搅拌均匀无粉团，静置十分钟后施工；
（2）清理墙面：严重粉化墙面先用草酸清洗，再用清水冲洗干净，保证墙面充分干燥，保证基层含水率小于10%，墙面pH值小于10。
（3）刮腻子：用批嵌工具批刮腻子,每次批嵌厚度1-3mm，每遍腻子的用量为1-5kg/m²,待腻子实干后方进行下一道腻子的批嵌，批嵌最后一道腻子时如有接茬，及时用羊毛刷蘸水梳理平整,为使墙面达到所要求的平整度，用刮尺水平方向和竖直方向刮涂，腻子表干后立即选用100-150#砂纸打磨并除去表面灰尘，腻子实干后进行下道工序施工。
将实施例1 至3 所得瓷砖胶粘剂进行性能测定，具体结果如下：
需要注意的是，以上实施例仅为说明本发明的技术思想，不能以此限定本发明的保护范围，凡是按照本发明提出的技术思想，在技术方案基础上所做的任何改动，均落入本发明的保护范围之内。
Claims (7)
1.一种抗裂腻子，其特征在于：包含胶液和粉料，其中所述的胶液主要成分包括丙烯酸乳液、消泡剂、成膜助剂、防冻剂、羟丙基甲基纤维素、无机泥胶和水，所述的粉料主要成分包括水泥、重钙、灰钙、石英砂、超短纤维和木质纤维；所述的胶液包含下列主要成分的重量份数为丙烯酸乳液35 -40份，消泡剂0.3 -1份，成膜助剂0.5 -1份，防冻剂0.9 -1.5份，羟丙基甲基纤维素8-20份，无机泥胶8-20份，水20-70份；
所述的粉料包含下列主要成分的重量份数为水泥30 -35份，重钙35 -40份，灰钙15-20份，石英砂30 -35份，超短纤维2-10份，木质纤维4-18份。
2.根据权利要求1所述的抗裂腻子，其特征在于：所述的胶液包含下列主要成分的重量份数为丙烯酸乳液40份，消泡剂1份，成膜助剂1份，防冻剂1.5份，羟丙基甲基纤维素20份，无机泥胶20份，水70份；
所述的粉料包含下列主要成分的重量份数为水泥35份，重钙40份，灰钙20份，石英砂35份，超短纤维10份，木质纤维18份。
3.根据权利要求1所述的抗裂腻子，其特征在于：所述的胶液包含下列主要成分的重量份数为丙烯酸乳液35份，消泡剂0.3份，成膜助剂0.5份，防冻剂0.9份，羟丙基甲基纤维素10份，无机泥胶10份，水35份；所述的粉料包含下列主要成分的重量份数为水泥30份，重钙35份，灰钙15份，石英砂30份，超短纤维7份，木质纤维12份。
4.根据权利要求1所述的抗裂腻子，其特征在于：所述的胶液包含下列主要成分的重量份数为丙烯酸乳液38份，消泡剂0.5份，成膜助剂0.8份，防冻剂1.2份，羟丙基甲基纤维素15份，无机泥胶15份，水53份；所述的粉料包含下列主要成分的重量份数为水泥32份，重钙38份，灰钙18份，石英砂32份, 超短纤维5份，木质纤维9份。
5. 根据权利要求1至4任一所述的抗裂腻子，其特征在于：所述的成膜助剂为智索成膜助剂，所述的消泡剂为巴斯夫助剂，所述的防冻剂为乙二醇防冻剂，所述的超短纤维是直径为3mm的纤维。
6.根据权利要求1至4任一所述的抗裂腻子，其特征在于：所述的水泥颗粒大小为50-200目，所述的重钙颗粒大小为300-400目，所述的灰钙颗粒大小为300-400目，所述的石英砂颗粒大小为80-120目。
7.一种如权利要求1至6 任一所述的抗裂腻子的使用方法，其特征在于：其使用方法包括以下步骤：
（1）原料混合：胶液和粉料按照质量份数3:5混合，先将胶液倒入容器中，一边搅拌一边加粉料，搅拌均匀无粉团，静置十分钟后施工；
（2）清理墙面：严重粉化墙面先用草酸清洗，再用清水冲洗干净，保证墙面充分干燥，保证基层含水率小于10%，墙面pH 值小于10；
（3）刮腻子：用批嵌工具批刮腻子, 每次批嵌厚度1-3mm，每遍腻子的用量为1-5kg/m,待腻子实干后方进行下一道腻子的批嵌，批嵌最后一道腻子时如有接茬，及时用羊毛刷蘸水梳理平整, 为使墙面达到所要求的平整度，用刮尺水平方向和竖直方向刮涂，腻子表干后立即选用100-150# 砂纸打磨并除去表面灰尘，腻子实干后进行下道工序施工。