CN104311896B - 一种钢丝绳芯输送带用高强度、高耐磨h型覆盖胶 - Google Patents
一种钢丝绳芯输送带用高强度、高耐磨h型覆盖胶 Download PDFInfo
- Publication number
- CN104311896B CN104311896B CN201410539024.4A CN201410539024A CN104311896B CN 104311896 B CN104311896 B CN 104311896B CN 201410539024 A CN201410539024 A CN 201410539024A CN 104311896 B CN104311896 B CN 104311896B
- Authority
- CN
- China
- Prior art keywords
- parts
- strength
- wear resistance
- carbon black
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种钢丝绳芯输送带用高强度高耐磨H型覆盖胶，由以下组分按照重量份数制备而成：天然橡胶50‑60份，顺丁橡胶BR900040‑50份，炭黑50‑60份，硫化活性剂4‑7份，芳烃油4‑8份，碳五树脂2‑4份，防护蜡2份，防老剂1‑3份，充油不溶性硫磺1.3‑2.5份，硫化促进剂1‑2.5份，防焦剂CTP 0.1‑0.3份。本发明的有益效果是：本发明从拉伸性能、耐磨性能及加工性能等方面综合考虑，通过优化H型覆盖胶的配方体系，特别是合理并用了碳五树脂，适当降低芳烃油的用量，使硫化胶能够达到显著的改善效果，兼具高拉伸强度及高耐磨性能，既满足了强划裂条件下对高拉伸强度的要求，同时，又使输送带的使用寿命大幅延长，提高了产品的技术含量和附加值。
Description
技术领域
本发明涉及输送带覆盖胶技术领域，特别涉及一种钢丝绳芯输送带用高强度高耐磨H型覆盖胶。
背景技术
H型覆盖胶是适合于在强划裂工作条件下应用的钢丝绳芯输送带，因此对拉伸强度要求较高，而输送带覆盖胶的耐磨性能好坏也是影响使用寿命的重要因素。随着钢丝绳输送带使用条件的日益苛刻，为保证其使用性能及寿命，用户对兼具高拉伸强度及高耐磨性能的H型覆盖胶的需求越来越迫切。《普通用途钢丝绳芯输送带H型覆盖胶的研制》一文公开了一种高拉伸强度的H型覆盖胶的配方，从其样品性能测试结果来看，拉伸强度和耐磨性虽然均超过国家标准的要求，但其耐磨性仍不高。整体来看，目前H型覆盖胶的拉伸性能尚可，而耐磨性能不很理想，严重影响了输送带的使用寿命。
发明内容
针对现有技术中存在的问题，本发明为满足普通钢丝绳芯输送带的更苛刻的使用条件，延长其使用寿命，提供一种兼具高拉伸强度及高耐磨性能的H型覆盖胶及其制备方法。
具体的技术方案如下：
一种钢丝绳芯输送带用高强度高耐磨H型覆盖胶，由以下组分按照重量份数制备而成：
天然橡胶50-60份，顺丁橡胶BR9000 40-50份，炭黑50-60份，硫化活性剂4-7份，芳烃油4-8份，碳五树脂2-4份，防护蜡2份，防老剂1-3份，充油不溶性硫磺1.3-2.5份，硫化促进剂1-2.5份，防焦剂CTP 0.1-0.3份。
在上述方案的基础上，所述的一种钢丝绳芯输送带用高强度高耐磨H型覆盖胶，由以下组分按照重量份数制备而成：
天然橡胶55份，顺丁橡胶BR9000 45份，炭黑50份，硫化活性剂4份，芳烃油6份，碳五树脂2份，防护蜡2份，防老剂2份，充油不溶性硫磺2份，硫化促进剂1.6份，防焦剂CTP 0.2份。
在上述方案的基础上，所述天然胶为3号烟片胶和/或20号标准胶。
在上述方案的基础上，所述炭黑为炭黑N134、炭黑N220和炭黑N234中的一种或几种的组合。
在上述方案的基础上，所述硫化活性剂为氧化锌和硬脂酸的组合物，两者的重量比为：2∶1～3∶1。
在上述方案的基础上，所述防老剂为防老剂6PPD、防老剂TMQ，防老剂BLE中的一种或几种。
在上述方案的基础上，所述硫化促进剂为促进剂CBS、促进剂DCBS、促进剂TBBS、促进剂NOBS、促进剂DPG、促进剂M和促进剂DM中的一种或几种的组合。
本发明的有益效果是：本发明从拉伸性能、耐磨性能及加工性能等方面综合考虑，通过优化H型覆盖胶的配方体系，特别是合理并用了碳五树脂，适当降低芳烃油的用量，使硫化胶能够达到显著的改善效果，兼具高拉伸强度及高耐磨性能，既满足了强划裂条件下对高拉伸强度的要求，同时，又使输送带的使用寿命大幅延长，提高了产品的技术含量和附加值。
具体实施方式
以下实施例仅用于对本发明做进一步的描述，并不是用来限制本发明的范围。
实施例1
一种钢丝绳芯输送带用高性能H型覆盖胶，配方按以下重量份组成(每份1000g)：3号烟片胶50份，顺丁橡胶BR9000 50份，炭黑N134 50份，氧化锌3份，硬脂酸1.5份，芳烃油6份，碳五树脂2份，防老剂6PPD 2份，防护蜡2份，不溶性硫磺IS-HS7020 2.2份，促进剂TBBS0.8份，促进剂DM 0.5份，防焦剂CTP 0.1份。
上述组分按照一般的两段混炼工艺制备混炼胶。
实施例2
一种钢丝绳芯输送带用高性能H型覆盖胶，配方按以下重量份组成(每份1000g)：天然橡胶SMR20 55份，顺丁橡胶BR9000 45份，炭黑N234 55份，氧化锌4份，硬脂酸2份，芳烃油5份，碳五树脂3份，防老剂6PPD 1份，防老剂BLE 1.5份，防护蜡2份，不溶性硫磺IS-HS7020 2.4份，促进剂NOBS 1.2份，防焦剂0.1份。
上述组分按照一般的两段混炼工艺制备混炼胶。
实施例3
一种钢丝绳芯输送带用高性能H型覆盖胶，配方按以下重量份组成(每份1000g)：
配方按重量份组成：天然橡胶STR20 60份，顺丁橡胶BR9000 40份，炭黑N134 50份，氧化锌4份，硬脂酸1.5份，芳烃油6份，碳五树脂2份，防老剂6PPD 1.5份，防老剂TMQ1.5份，防护蜡2份，不溶性硫磺IS-HS7020 2.5份，促进剂CBS 0.8份，促进剂DM 0.3份，防焦剂0.2份。
上述组分按照一般的两段混炼工艺制备混炼胶。
天然橡胶SMR20和天然橡胶STR20均为20号标准胶
将上述实施例1、实施例2、实施例3制备的H型覆盖胶进行性能测试，测试结果数据和现有产品(市场优级品)的数据对比如下表1所示。
表1性能测试结果
通过对比，可以看到，本发明制得的产品与现有产品相比，硫化特征变化较小；在保持较高拉伸强度的同时，耐磨性能大大提高，有利于输送带覆盖胶使用寿命的延长。
上述参照实施例对覆盖胶及其制备方法进行的详细描述，是说明性的而不是限定性的，可按照所限定范围列举出若干个实施例，因此在不脱离本发明总体构思下的变化和修改，应属本发明的保护范围之内。
Claims (2)
1.一种钢丝绳芯输送带用高强度高耐磨H型覆盖胶，其特征在于：由以下组分按照重量份数制备而成：
天然橡胶50-60份，顺丁橡胶BR9000 40-50份，炭黑50-60份，硫化活性剂4-7份，芳烃油4-8份，碳五树脂2-4份，防护蜡2份，防老剂1-3份，充油不溶性硫磺1.3-2.5份，硫化促进剂1-2.5份，防焦剂CTP 0.1-0.3份；
所述天然胶为3号烟片胶和/或20号标准胶；
所述炭黑为炭黑N134、炭黑N220和炭黑N234中的一种或几种的组合；
所述硫化活性剂为氧化锌和硬脂酸的组合物，两者的重量比为：2∶1～3∶1；
所述防老剂为防老剂6PPD、防老剂TMQ，防老剂BLE中的一种或几种；
所述硫化促进剂为促进剂CBS、促进剂DCBS、促进剂TBBS、促进剂NOBS、促进剂DPG、促进剂M和促进剂DM中的一种或几种的组合。
2.根据权利要求1所述的一种钢丝绳芯输送带用高强度高耐磨H型覆盖胶，其特征在于：由以下组分按照重量份数制备而成：
天然橡胶55份，顺丁橡胶BR9000 45份，炭黑50份，硫化活性剂4份，芳烃油6份，碳五树脂2份，防护蜡2份，防老剂2份，充油不溶性硫磺2份，硫化促进剂1.6份，防焦剂CTP 0.2份。