CN104059273A - 一种白色薄膜专用聚乙烯着色母料及其制备方法 - Google Patents

一种白色薄膜专用聚乙烯着色母料及其制备方法 Download PDF

Info

Publication number
CN104059273A
CN104059273A CN201410266626.7A CN201410266626A CN104059273A CN 104059273 A CN104059273 A CN 104059273A CN 201410266626 A CN201410266626 A CN 201410266626A CN 104059273 A CN104059273 A CN 104059273A
Authority
CN
China
Prior art keywords
parts
polyethylene
special
low
white
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410266626.7A
Other languages
English (en)
Inventor
高川
郭玲
孙潜
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lan-Star (chengdu) New Material Co Ltd
Original Assignee
Lan-Star (chengdu) New Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lan-Star (chengdu) New Material Co Ltd filed Critical Lan-Star (chengdu) New Material Co Ltd
Priority to CN201410266626.7A priority Critical patent/CN104059273A/zh
Publication of CN104059273A publication Critical patent/CN104059273A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种白色薄膜专用聚乙烯着色母料，由以下按照重量份数计的原料组成：树脂20～38份，聚乙烯蜡5～10份，白油0.5～1.5份，硬脂酸锌0.5～1.5份，钛白粉10～35份，重质碳酸钙25～40份；所述的树脂为低密度高压聚乙烯和线性低密度的混合物，其比例为5～8:3。其制备方法为：称取混合树脂、钛白粉、重质碳酸钙、聚乙烯蜡、硬脂酸锌和白油后依次加入高速混料机中，充分混合；混合好后转移至双螺杆挤出机，熔融挤出后冷却、烘干、造粒后包装。本发明应用于塑料工业，具有分散性好、耐热性高、生产成本低，同时提高薄膜制品的机械性能和印刷性能，具有较强的价格和质量优势。

Description

一种白色薄膜专用聚乙烯着色母料及其制备方法
技术领域
本发明涉及一种聚乙烯着色母料及其制备方法，特别涉及一种白色薄膜专用聚乙烯着色母料及其制备方法，属于塑料添加剂领域。
背景技术
白色薄膜应用范围很广，根据不同白度、厚度和分散性可用于不同领域如：农地膜、超市购物袋、食品包装袋等。2012年全年全国塑料薄膜产量为1089.35万吨，同比增长7.61%，其中白色薄膜占多数，生产白色薄膜需要添加的着色母料需求量也随之增大。常规生产白色薄膜一般是将树脂、钛白粉、分散剂、偶联剂等经高速混料机混合后，直接熔融挤出，冷却，干燥，造粒。薄膜加工领域中使用普通白色母料会会带来两个问题：1、因混料不均或熔融不充分而导致分散性不好；2、生产成本高；3、母料耐热性不好，导致薄膜制品发黄。
国家知识产权局于2004年4月7日公开了公开号为CN1487012的中国发明专利“高浓度聚烯烃白色母粒及其制备方法”。该专利公开了一种高浓度聚烯烃白色母粒，由颜料、塑料助剂和载体树脂组成，其特征在于：所说的塑料助剂包含低分子聚乙烯蜡、硬脂酸锌、光亮润滑剂、增容增量剂、偶联剂和液体石蜡，其组分重量百分比为：颜料 50～80%，低分子聚乙烯蜡 5～10%，硬脂酸锌 1～2%，光亮润滑剂0.5～1%，增容增量剂0.5～1%，偶联剂0.5～7%，液体石蜡1～5%，载体树脂10～40%。因为颜料在运输过程中会聚集在一起，形成团聚体、凝聚体。特别是颜料比例大时，虽然可制得高浓度的白色母料，但其应用于薄膜生产时，分散性会受到严重影响，并且生产成本较高。
碳酸钙具有改善塑料制品某些性能以扩大其应用范围的作用，在塑料加工中他们可以减少树脂收缩率，控制粘度。具体来说有以下优点：1、提高塑料制品尺寸的稳定性，在塑料制品中起到一种骨架的作用；2、改善塑料加工性能：改变塑料的流变性能，特别是经过表面处理的碳酸钙，不但可以提高制品的硬度，提高制品的表面光泽和表面平整性，还可以减少塑料制品的收缩率、线膨胀系数、蠕变性能，为加工成型创造条件；3、提高塑料制品的耐热性；4、可提高某些制品的电镀性能、印刷性能；5、降低塑料制品的成本，普通轻质碳酸钙和重质碳酸钙价格均远远低于树脂，添加碳酸钙后，不仅可使性能提高，还能减少树脂用量，节约成本。综上，碳酸钙作为塑料添加剂具有提高薄膜制品表面光泽度、印刷性能、电镀性能及降低生产成本的优势。
发明内容
为了解决上述技术问题，本发明提供一种提高薄膜制品表面光泽度、印刷性能、电镀性能、耐热性的白色薄膜专用聚乙烯着色母料及其制备方法。
本发明的技术方案为：
一种白色薄膜专用聚乙烯着色母料，由以下按照重量份数计的原料组成：树脂20～38份，聚乙烯蜡5～10份，白油 0.5～1.5份，硬脂酸锌0.5～1.5份，钛白粉 10～35份，重质碳酸钙25～40份；所述的树脂为低密度高压聚乙烯和线性低密度的混合物，其比例为5～8:3。
优选地，所述的一种白色薄膜专用聚乙烯着色母料，由以下按照重量份数计的原料组成：树脂25～35份，聚乙烯蜡 6～9份，白油0.8～1.2份，硬脂酸锌 0.8～1.2份，钛白粉 15～30份，重质碳酸钙 30～38份；所述的树脂为低密度高压聚乙烯和线性低密度的混合物，其比例为5～7:3。
进一步优选，所述的一种白色薄膜专用聚乙烯着色母料，由以下按照重量份数计的原料组成：树脂30份，聚乙烯蜡8份，白油1份，硬脂酸锌 1份，钛白粉 25份，重质碳酸钙35份；所述的树脂为低密度高压聚乙烯和线性低密度的混合物，其比例为6:3。
优选地，所述的聚乙烯蜡为固态低分子聚乙烯蜡，其分子量为：2000～3000。
优选地，所述的钛白粉为金红石型钛白粉，其二氧化钛的含量≥93%。
优选地，所述的重质碳酸钙为超细重质碳酸钙，其粒径为：0.02um～0.1 um。
一种白色薄膜专用聚乙烯着色母料的制备方法，包含以下步骤：称取所需的所有原材料，称重误差±0.5%； 将称好的混合树脂、钛白粉、重质碳酸钙、聚乙烯蜡、硬脂酸锌和白油依次加入高速混料机中，高速混料机搅拌桨的转速为475～950r/min，先低速运行5～8min，然后高速运行25～30min，再低速运行5～10min；将混好的料转移至双螺杆挤出机，双螺杆挤出机的主机转速为200～250 r/min，熔融挤出后冷却、烘干、造粒后包装。
与现有技术相比，本发明的有益效果是：通过对原材料树脂、聚乙烯蜡、钛白粉和碳酸钙选择，使其在相互排斥作用减到最小，制得的白色薄膜专用聚乙烯着色母料具有分散性好、耐热性高、生产成本低，同时提高薄膜制品的机械性能、电镀性能和印刷性能，具有较强的价格和质量优势。
具体实施方式
实施例1
一种白色薄膜专用聚乙烯着色母料，由以下按照重量份数计的原料组成：树脂20份，聚乙烯蜡5份，白油 0.5份，硬脂酸锌 0.5份，钛白粉 10份，重质碳酸钙25份；所述的树脂为低密度高压聚乙烯和线性低密度的混合物，其比例为5:3。
其制备方法包含以下步骤：分别称好上述原材料后，将称好的混合树脂、钛白粉、重质碳酸钙、聚乙烯蜡、硬脂酸锌和白油依次加入高速混料机中，先将转速控制在475 r/min低速运行5min，然后将转速控制在850 r/min高速运行25min，再将转速控制在600 r/min低速运行5min；将混好的料转移至主机转速为200 r/min的双螺杆挤出机，熔融挤出后丝料穿过冷却水槽进行冷却，并通过风机将丝料表面的水滴吹干后，进入造粒机进行造粒，制得产品。
实施例2
一种白色薄膜专用聚乙烯着色母料，由以下按照重量份数计的原料组成：树脂 38份，聚乙烯蜡10份，白油 1.5份，硬脂酸锌 1.5份，钛白粉35份，重质碳酸钙40份；所述的树脂为低密度高压聚乙烯和线性低密度的混合物，其比例为8:3。
所述的聚乙烯蜡为固态低分子聚乙烯蜡，其分子量为：2000～3000。
所述的钛白粉为金红石型钛白粉，其二氧化钛的含量≥93%。
其制备方法为包括以下步骤：分别称好上述原材料后，将称好的混合树脂、钛白粉、重质碳酸钙、聚乙烯蜡、硬脂酸锌和白油依次加入高速混料机中，先将转速控制在500r/min低速运行8min，然后将转速控制在850 r/min高速运行30min，再将转速控制在600 r/min低速运行10min；将混好的料转移至主机转速为250r/min的双螺杆挤出机，熔融挤出后丝料穿过冷却水槽进行冷却，并通过风机将丝料表面的水滴吹干后，进入造粒机进行造粒，制得产品。
实施例3
一种白色薄膜专用聚乙烯着色母料，由以下按照重量份数计的原料组成：树脂30份，聚乙烯蜡8份，白油1份，硬脂酸锌1份，钛白粉 25份，重质碳酸钙35份。所述的树脂为低密度高压聚乙烯和线性低密度的混合物，其比例为6:3。
所述的聚乙烯蜡为固态低分子聚乙烯蜡，其分子量为：2000～3000。
所述的钛白粉为金红石型钛白粉，其二氧化钛的含量≥93%。
其制备方法包括以下步骤：分别称好上述原材料后，将称好的混合树脂、钛白粉、重质碳酸钙、聚乙烯蜡、硬脂酸锌和白油依次加入高速混料机中，先将转速控制在500r/min低速运行6min，然后将转速控制在800 r/min高速运行28min，再将转速控制在550r/min低速运行8min；将混好的料转移至主机转速为250r/min的双螺杆挤出机，熔融挤出后丝料穿过冷却水槽进行冷却，并通过风机将丝料表面的水滴吹干后，进入造粒机进行造粒，制得产品。

Claims (9)

1.一种白色薄膜专用聚乙烯着色母料，其特征在于由以下按照重量份数计的原料组成：树脂20～38份，聚乙烯蜡5～10份，白油 0.5～1.5份，硬脂酸锌0.5～1.5份，钛白粉 10～35份，重质碳酸钙25～40份；所述的树脂为低密度高压聚乙烯和线性低密度的混合物，其比例为5～8:3。
2.根据权利要求1所述的一种白色薄膜专用聚乙烯着色母料，其特征在于：由以下按照重量份数计的原料组成：树脂25～35份，聚乙烯蜡 6～9份，白油0.8～1.2份，硬脂酸锌 0.8～1.2份，钛白粉 15～30份，重质碳酸钙 30～38份；所述的树脂为低密度高压聚乙烯和线性低密度的混合物，其比例为5～7:3。
3.根据权利要求1所述的一种白色薄膜专用聚乙烯着色母料，其特征在于：由以下按照重量份数计的原料组成：树脂30份，聚乙烯蜡8份，白油1份，硬脂酸锌 1份，钛白粉 25份，重质碳酸钙35份；所述的树脂为低密度高压聚乙烯和线性低密度的混合物，其比例为6:3。
4.根据权利要求1所述的一种白色薄膜专用聚乙烯着色母料，其特征在于：所述的聚乙烯蜡为固态低分子聚乙烯蜡，其分子量为：2000～3000。
5.根据权利要求1所述的一种白色薄膜专用聚乙烯着色母料，其特征在于：所述的钛白粉为金红石型钛白粉，其二氧化钛的含量≥93%。
6.根据权利要求1所述的一种白色薄膜专用聚乙烯着色母料，其特征在于：所述的重质碳酸钙为超细重质碳酸钙，其粒径为：0.02um～0.1 um。
7.根据权利要求1～6任一项所述的一种白色薄膜专用聚乙烯着色母料的制备方法，其特征在于：包含以下步骤：称取所需的所有原材料，称重误差±0.5%；将称好的混合树脂、钛白粉、重质碳酸钙、聚乙烯蜡、硬脂酸锌和白油依次加入高速混料机中，高速混料机搅拌桨的转速为475～950r/min，先低速运行5～8min，然后高速运行25～30min，再低速运行5～10min；将混好的料转移至双螺杆挤出机，双螺杆挤出机的主机转速为200～250 r/min，熔融挤出后冷却、烘干、造粒后包装。
8.根据权利要求7所述的一种白色薄膜专用聚乙烯着色母料的制备方法，其特征在于：所述的高速混料机搅拌桨的转速为：475～950r/min。
9.根据权利要求7所述的一种白色薄膜专用聚乙烯着色母料的制备方法，其特征在于：所述的双螺杆挤出机的主机转速为：200～250 r/min。
CN201410266626.7A 2014-06-16 2014-06-16 一种白色薄膜专用聚乙烯着色母料及其制备方法 Pending CN104059273A (zh)