CN104046204A - 抗碱封闭底漆 - Google Patents
抗碱封闭底漆 Download PDFInfo
- Publication number
- CN104046204A CN104046204A CN201410225919.0A CN201410225919A CN104046204A CN 104046204 A CN104046204 A CN 104046204A CN 201410225919 A CN201410225919 A CN 201410225919A CN 104046204 A CN104046204 A CN 104046204A
- Authority
- CN
- China
- Prior art keywords
- powder
- parts
- alkali
- ether
- resistant sealing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗碱封闭底漆，包括以下重量份的原料：苯丙乳液5-15、环氧乳液30-40、消泡剂0.1-0.2、PH值调节剂0.1-0.2、新戊二醇二缩水甘油醚0.5-1、成膜助剂0.6-1、丙二醇1-2、分散剂0.1-0.2、增稠剂0.2-0.6、卡波姆1-3、沉淀硫酸钡4-8、玉石粉3-5、超细高岭土5-10、复合纳米粉5-10。本发明采用苯丙乳液、环氧乳液、复合纳米粉等复配使用，提高了渗透性及附着力，达到了极佳的封闭效果，使用超细粉提高了底漆的抗碱性，不易分层，提高了其储存性。
Description
技术领域
本发明涉及一种抗碱封闭底漆，属于建筑涂料技术领域。
背景技术
抗碱封闭底漆有抗碱，防霉，渗透性能，能有效封闭底漆，防止墙体水分及碱性物质析出造成漆膜脱落，促进和增加在底材上的附着力，提高整体涂层的品质持久性。但目前多数抗碱封闭底漆，渗透效果不佳，导致附着力差，影响饰面系统的整体寿命。
发明内容
本发明的目的为了解决现有技术中存在的缺陷，提供一种渗透力强，封闭效果好的的抗碱封闭底漆。
为了达到上述目的，本发明采用如下技术方案：
一种抗碱封闭底漆，包括以下重量份的原料：苯丙乳液5-15、环氧乳液30-40、消泡剂0.1-0.2、PH值调节剂0.1-0.2、新戊二醇二缩水甘油醚0.5-1、成膜助剂0.6-1、丙二醇1-2、分散剂0.1-0.2、增稠剂0.2-0.6、卡波姆1-3、沉淀硫酸钡4-8、玉石粉3-5、超细高岭土5-10、复合纳米粉5-10；
所述复合纳米粉的制备方法如下：(1)按重量比5-10：4-8:3-6称取伊利石、六环石和绢云母，混合均匀，820-880℃煅烧1-2h，冷却至室温，粉碎成纳米粉体，过筛；(2)过筛后的粉末加水制成浓度为40-50％的悬浮液，再加入相当于悬浮液重量4-8％的聚苯乙烯磺酸钠、3-5％的三乙醇胺、1.5-2.5％的柠檬酸、2-3％的三聚磷酸钠和3-6％的聚二烯丙基二甲基氯化铵，3000-4000rpm高速研磨0.5-1h，过滤，洗涤，烘干；(3)将步骤(2)烘干后的粉末分散于2-3倍量的85％乙醇溶液中，加入相当于混合液重量15-20％的正硅酸乙酯、5-10％的乙烯基三乙氧基硅烷、3-6％的聚乙烯吡咯烷酮、2-4％的鞣酸和1-3％的纳米锌粉，超声分散20-30min，然后用醋酸或氨水调节pH值至4-5，加热至70-80℃，搅拌1-2h，过滤，洗涤，烘干；(4)将步骤(3)烘干后的粉末分散于2-3倍量的的乙酸丁酯和二甲苯等体积混合溶液中，氮气保护下升温至80-90℃，加入相当于混合液重量10-15％的甲基丙烯酸甲酯、8-12％的丙烯酸、5-10％的苯乙烯、4-8％的马来 酸酐、3-6％的二乙烯基苯、0.5-1％的过氧化苯甲酰，搅拌1-2h，过滤，洗涤，烘干即可。
所述的消泡剂为上海长风化工厂生产，型号为S-220。
所述的分散剂为上海长风化工厂生产，型号为DP-150。
所述的增稠剂为上海长风化工厂生产，型号为T-17。
所述的PH值调节剂选自2-氨基-2-甲基-1-丙醇、氨水、三乙醇胺、二乙醇胺、氢氧化钠、碳酸氢钠中的一种。
所述的成膜助剂选自乙二醇单甲醚、乙二醇单乙醚、乙二醇单丁醚、二乙二醇单丙醚、三乙二醇单乙醚、丙二醇单甲醚、丙二醇苯醚、乙二醇苯醚、十二碳醇酯种的一种。
本发明比现有技术有以下优点：本发明采用苯丙乳液、环氧乳液、复合纳米粉等复配使用，提高了渗透性及附着力，达到了极佳的封闭效果，使用超细粉提高了底漆的抗碱性，不易分层，提高了其储存性。
具体实施方式
下面结合具体实施例对本发明进行详细说明。
实施例1
抗碱底漆有以下重量份的原料配置而成：苯丙乳液5、环氧乳液30、消泡剂0.1、PH值调节剂0.1、新戊二醇二缩水甘油醚0.5、成膜助剂0.6、丙二醇1、分散剂0.1、增稠剂0.2、卡波姆1、沉淀硫酸钡4、玉石粉3、超细高岭土5、复合纳米粉5。
所述复合纳米粉的制备方法如下：(1)按重量比10：8:6称取伊利石、六环石和绢云母，混合均匀，880℃煅烧1h，冷却至室温，粉碎成纳米粉体，过筛；(2)过筛后的粉末加水制成浓度为50％的悬浮液，再加入相当于悬浮液重量8％的聚苯乙烯磺酸钠、5％的三乙醇胺、2.5％的柠檬酸、3％的三聚磷酸钠和6％的聚二烯丙基二甲基氯化铵，4000rpm高速研磨0.5h，过滤，洗涤，烘干；(3)将步骤(2)烘干后的粉末分散于3倍量的85％乙醇溶液中，加入相当于混合液重量20％的正硅酸乙酯、10％的乙烯基三乙氧基硅烷、6％的聚乙烯吡咯烷酮、4％的鞣酸和3％的纳米锌粉，超声分散30min，然后用醋酸或氨水调节pH值至4-5，加热至80℃，搅拌1-2h，过滤，洗涤，烘干；(4)将步骤(3)烘干后的粉末分散于 3倍量的的乙酸丁酯和二甲苯等体积混合溶液中，氮气保护下升温至90℃，加入相当于混合液重量15％的甲基丙烯酸甲酯、12％的丙烯酸、10％的苯乙烯、8％的马来酸酐、6％的二乙烯基苯、1％的过氧化苯甲酰，搅拌2h，过滤，洗涤，烘干即可。
实施例2
抗碱底漆有以下重量份的原料配置而成：苯丙乳液10、环氧乳液35、消泡剂0.15、PH值调节剂0.15、新戊二醇二缩水甘油醚0.8、成膜助剂0.9、丙二醇1.5、分散剂0.15、增稠剂0.3、卡波姆2、沉淀硫酸钡6、玉石粉4、超细高岭土8、复合纳米粉7。
复合纳米粉的制备方法同实施例1。
实施例3
抗碱底漆有以下重量份的原料配置而成：苯丙乳液15、环氧乳液40、消泡剂0.2、PH值调节剂0.2、新戊二醇二缩水甘油醚1、成膜助剂1、丙二醇2、分散剂0.2、增稠剂0.6、卡波姆3、沉淀硫酸钡8、玉石粉5、超细高岭土10、复合纳米粉10。
复合纳米粉的制备方法同实施例1。
上述实施例得到的抗碱封闭底漆符合行业使用要求，附着力佳，储存时间长，具有良好的施工性。性能测试结果如下表所示：
Claims (6)
1.一种抗碱封闭底漆，其特征在于，包括以下重量份的原料：苯丙乳液5-15、环氧乳液30-40、消泡剂0.1-0.2、PH值调节剂0.1-0.2、新戊二醇二缩水甘油醚0.5-1、成膜助剂0.6-1、丙二醇1-2、分散剂0.1-0.2、增稠剂0.2-0.6、卡波姆1-3、沉淀硫酸钡4-8、玉石粉3-5、超细高岭土5-10、复合纳米粉5-10；
所述复合纳米粉的制备方法如下：（1）按重量比5-10：4-8:3-6称取伊利石、六环石和绢云母，混合均匀，820-880℃煅烧1-2h，冷却至室温，粉碎成纳米粉体，过筛；（2）过筛后的粉末加水制成浓度为40-50%的悬浮液，再加入相当于悬浮液重量4-8%的聚苯乙烯磺酸钠、3-5%的三乙醇胺、1.5-2.5%的柠檬酸、2-3%的三聚磷酸钠和3-6%的聚二烯丙基二甲基氯化铵，3000-4000rpm高速研磨0.5-1h，过滤，洗涤，烘干；（3）将步骤（2）烘干后的粉末分散于2-3倍量的85%乙醇溶液中，加入相当于混合液重量15-20%的正硅酸乙酯、5-10%的乙烯基三乙氧基硅烷、3-6%的聚乙烯吡咯烷酮、2-4%的鞣酸和1-3%的纳米锌粉，超声分散20-30min，然后用醋酸或氨水调节pH值至4-5，加热至70-80℃，搅拌1-2h，过滤，洗涤，烘干；（4）将步骤（3）烘干后的粉末分散于2-3倍量的的乙酸丁酯和二甲苯等体积混合溶液中，氮气保护下升温至80-90℃，加入相当于混合液重量10-15%的甲基丙烯酸甲酯、8-12%的丙烯酸、5-10%的苯乙烯、4-8%的马来酸酐、3-6%的二乙烯基苯、0.5-1%的过氧化苯甲酰，搅拌1-2h，过滤，洗涤，烘干即可。
2.根据权利要求1所述的抗碱封闭底漆，其特征在于，所述的消泡剂为上海长风化工厂生产，型号为S-220。
3.根据权利要求1所述的抗碱封闭底漆，其特征在于，所述的分散剂为上海长风化工厂生产，型号为DP-150。
4.根据权利要求1所述的抗碱封闭底漆，其特征在于，所述的增稠剂为上海长风化工厂生产，型号为T-17。
5.根据权利要求1所述的抗碱封闭底漆，其特征在于，所述的PH值调节剂选自2- 氨基-2- 甲基-1- 丙醇、氨水、三乙醇胺、二乙醇胺、氢氧化钠、碳酸氢钠中的一种。
6.根据权利要求1所述的抗碱封闭底漆，其特征在于，所述的成膜助剂选自乙二醇单甲醚、乙二醇单乙醚、乙二醇单丁醚、二乙二醇单丙醚、三乙二醇单乙醚、丙二醇单甲醚、丙二醇苯醚、乙二醇苯醚、十二碳醇酯种的一种。