CA1214754A - Process for forming integral spindle-axle tubes - Google Patents

Abstract

PROCESS FOR FORMING INTEGRAL SPINDLE-AXLE TUBES
ABSTRACT OF DISCLOSURE

A process for cold forming integral spindle-axle tubes includes placing a tubular blank within an open ended die having an extrusion die throat, and pushing the blank through the die throat with a punch. The punch is formed with a ram portion that applies pressure to the blank for moving it axially through the throat. The punch also has an extension closely fitted within the blank so that as the punch pushes the tube axially, the blank is extruded between the die throat and the extension to form a thin wall tube. After the blank is partially extruded, the punch is removed and a second blank is inserted. This second blank is then located between the punch ram portion and the trailing end of the first blank so that further movement of the punch causes the second blank to push the first blank through the die throat. At that time, a second punch extension, of smaller diameter than the first one, is arranged within the throat so that an inwardly thickened ring-like annular section is extruded within the extruded tube, at a distance from the trailing end of the tube. The die movement continues until the first extension is aligned within the throat and the trailing end portion of the extruded tube is completed. Thereafter, the steps are repeated to form additional extruded tubes. Each extruded tube has its trailing end portion and thickened ring section swaged radially inwardly first, until its outside diameter is less than the outside diameter of the tube, and secondly, until the inside diameter of the thinner wall trailing end portion is formed to the same internal diameter as that of the thickened section to thereby provide the integral spindle-axle tube.

Description

75~

215.082 PROCl~SS FOR FORMING INTEGRAL SPINDLE-AXLE TUEES

BACKGROUNl:) OF I~VENTION

This invention relates to Q process for forming an integral or one piece sxle tube and spindle. Axle-spindle assemblies of this type are useful as so-called full-float axles for trucks and the like.

Truck axles have been formed by welding together an extruded axle tube and a separate spindle of the type which has a central bore and varying wall thicknesses along its length. An example of this type of eonstruction is shown in my prior Patent No. 3,837,~05 issued September 24, 1974 for a "Process for Cold Forming a Metal Tube with Qn Inwardly Thickened End"O

The process disclosed in Patent No. 39837,205 involves extruding a blank through a tubular die using a punch or ram to force the blank through the die. Extensions or steps formed on the punch produce a thickened end portion on the extruded tube. My more recent patents Nos. 4,277,969 issued July 14, 1981 and 4,301,672 issued November 24, 1981 disclose methods by which rin~like or annular thickened portions are formed within the tube during extrusion of the blank by the movement of the punch through the die.

However, in the past, it has not been feasible to form the spindle of the axle integr~l with the axle tube in Qn extrusion type of process such as disclosed in my above-mentioned pQtents. Axles have been made with integral spindles through forging processes which produce a one-piece unit but the use of forging is relatively expensive Qnd the metallurgical structures produced are not as desirable as those obtained through my above-mentioned extrusion processes.

Thus, the process of this Rpplic~tion relates to the forming of an axle tube through, first an extrusion process and thereafter, Q simplified step for converting a portion of the extrusion into an integral spindle, thereby elimin~ting the prior two-piece welded together, construction and the prior forging systems.

~4~75i~

~15.082 SUMMARY OF INVENTION

The invention herein contemplates cold forming or extruding a tubular blank by pushing it through a die throat with a ram type of punch which is formed with a mandrel like extension or insert that fits within the blank and the die throat. The mandrel extension is formed with multiple steps or sections of successively decreasing diameter. Thus, as the ram punch pushes the blank through the die throat, different diameter mandrel-like sections are aligned within the die throat to produce different wall thicknesses. By properly arranging the punch extensions, a ring-like or annular~ radially inwardly extending thickened section is formed within the extruded tube at a short distance from one end of the tube. After the extrusion, the thickened portion with the adjacent tube end portion are swaged to a smaller externQl diameter than the O.D. of the thin wall tube. Following this, ~ second swaging s~ep reduces the diameter of the tube end portion to form a substantially uniform diameter bore thrDugh it and the thickened portion. Thus, through the swaging operations, the extruded end of the tube is converted into a spindle shape which is integral with the axle.

The tube is formed of a suitable steel materinl which is selected to provide the necessary strength and metallurgical characteristics. Since the foregoing process is performed cold, that is, at room temperature, the metallurgical structure resulting from the extrusion and swaging steps does not require further heat treating ~nd the metallurgical structure is better thsn either a machined or forged tube. Further, such heat as may be generated during the extrusion or swflging steps is very low, such as in the order of around 3û0 degrees F or less and thus, has no adverse effect upon the metallurgical structure of the piece.

~2~

215.082 An object of this invention is tc provide a method for cold forming, out of a single tubular blank, Q one-piece or integral spindle-axle tube construction wherein the spindle may have varying wall thicknesses as compared with the relatively thin wall of the axle tube.

Another object of this invention is to produce a rela~ively light-weight spindle-tube construction which is relatively inexpensive, b~t with improved metallurgical characteristics as compered to other systems including welding of separate tubes and spindles together.

These and other objects and advantages of this invention will become epparent upon reading the following description of which the attached drawings form a part.

~Z~

215.082 DESCRIPTION OF DRAWINGS
.

Fig. 1 is a cross~ection~l, elevational view of an integral spindle-axle tube of this invention.

Fig. 2 is a partially cross-sectioned, extruded tube prior to forming the spindle portion thereonO

Fig. 3 schematically illustrates one of the swaging steps for forming the spindle, and Fig.4 schematically illustrates the second swaging step in forming the spindle.

Fig. 5 schematically illustrates the spindle construction and indicates the area where bore machining can be performed.

lFigs. 6 - 13, inclusive, schematically illustrate the successive steps in extruding the axle tube.

Fig. 14 is a modification, showing the use of a plmch having an additional extension or insert section.

Fig. 15 is a cross-sectional, perspective view, of an extruded tube resulting from the steps illustrated in Figs. 8 -13.

Fig. 16 is a fragmentary, crossffectional9 perspective view of the spindle end portion of an extruded tube produced through the modified punch of Fig. 14.

215.082 DETAILED DESCRIPTION
_ Fig. 1 illustrates, in cross-section, a full-float axle tube 10 formed by the process of this invention. The tube which i5 m~de of suitable steel, includes an integral spindle 11 formed by an end portion 13 and an adjacent radially inward, thickened annular or rin~like section 14. The tube itself is formed o~ a relatively thin wall 15, whieh may be provided with an inwardly thickened opposite nd 16.

The outer surfaces of the spindle portion may be suitably machined for carrying bearings or other elements. Likewise, the spindle bore and the tube thickened end 16 may be machined for c~acting with other elements such QS bearings, inserts and the like.

Significantly, the entire tube~pindle assembly is made of a one-piece, cold formed extrusion which is swaged to produce the different, desired wall thicknesses. These w~ll thicknesses are predetermined to provide enough stock for machining purposes where desired, or for increasing strengths or the rigidity of portions of the asse!nbly.

Referring to Figs. 6 - 13, the method for forming the tube starts with a tubular shaped die 20 which has an open inlet end 21, an outlet end 22, and a restricted die throat 23. The die may be either vertically or horizontally arranged, depending upon the type of press equipment used with the die. That is, the die is mounted upon the press bed of a conventional press, which is not shown here as it forms no part of the invention.

A blank 24 which is formed of a relatively thick wallt short tube, is placed within the die 20, QS illustrated in Fig. 6. Then A punch 25 is inserted within the die.

75~

215.082 The punch 25 is provided with an outer ram section 26 which has an ~nnular ram shoulder 27 th~t engages the free end of the blank. In addition, the punch is provided with a series of extensions or inserts, similar to mandrels The first extension 28 is relatively large. The second or middle extension 29 is of a smaller diameter and in turn, the third extension 30 is the sm~llest.

When the press is actuated, the punch moves axially of the die, in the direction of the die throat. This positions the second or middle extension 29 within the die throat. Hence, the slowly moving extension 29 creates an annular space relative to the die throat through which the lead portion oE the blank is extruded due to the pressure of the annular shoulder 27. Such lead portion corresponds to the axle tube thickened end 16.

Fig. 7 shows the movement of the ram to produce the lead portion 16. Next, as shown in Pig. 8, continued movement of the punch causes the first or larger extension section 28 to move into the die throat. Purther extrusion is between the extension section 28 and the die throat which produces the thin wall 15 of the tube. During the extrusion, the extruded wall moves muchmore rapidly than does the punch so that the overall tube length is considerablygreater than the length of the extension section 28.

When the punch reaches the point where the thin wall section 11 is completely extruded, the punch is stopped. This leaves an unextruded trailing end portion within the die as shown in Fig. 9. At this point, the punch 25 is removed from the die and from the blank. A second blank 24a is inserted within the dis as illustrated in Fligo 10~ This second blank, being arranged in end to end contact with the partislly extruded first blank beneath it, now functions as if it were a portion of the punch.

-" lL`2~'75i'~

215.082 The punch 25 is replaced or reinserted in the die RS shown in Fig. 11. Its ram forming annular shoulder 27 cont~cts the trailing end of the second blank so thst movement of the punch now pushes the second blank, which acting like an extension of the rsm shoulder 27, pushes agairLst the tr~iling end of the partially extruded blank beneath it.

Because of the positioning of the second blank 24a within the die, the third or smallest extension section 30 of the punch is located within the die throat~ as shown in Fig. 12. Consequently, movement of the punch results in the flow of metal around the third extension section 30 which, acting like a mandrel, produces an inwardly enlarged ring-like formation 14a.

As the punch continues moving, as shown in ~igs. 12 and 13, the thickened portion 14a is completed and then further movement results in the middle extension 29 entering the die throat. Because of the positioning of the middle extension, the tr~iling end portion of the tube forms a wall portion 13a which is of the same thickness as the opposite thickened end portion 16.

When ithe extruded tube is completed, it is removed from the die.
Its shape is illustrated in Fig. 15. ThereElfter, the cycle is repeated over and over again.

Although the punch, with its several different diameter extensions, produces different thickness wall sections near the trailing end of the tube, the punch can be modified by using more or le~s extensions to correspondingly produce more or less different wall thickness areas. For example, as shown in Fig. 14, an additional punch section 32 is provided which, in turn, produces another thicker interior wall section 34 as illustrated in Fig. 16.
Thus, the spindle m&y be provided with more or less stepped sections as required.

7S~

215.082 The axle tube spindle formed at the conclusion of the step illustrated in Fig. 13 is illustrated in Fig. 15. The tube and spindle are of a uniform external diameter. Thus, to form the narrower diameter spindle sections, the swaging steps are performed.

Fig/ 2 illustrates, in an enlarged view, the spindle portion as formed on the tube during the extrusion. As shown in Fig. 3, a mandrel 40 is inserted in the tube end. The mandrel may be supported by an appropriate support wh;ch is schematically illustrated as 41. Then, conventionsl swaging hammers 42 are applied to the exterior, as schematically illustrated in Fig. 3, to reduce the O~Do of the end portion of the tube. Here, the O.D. of the annular thickened section and the thinner wall end portion are the same, but of a smaller diameter than the remainder of the tube.

Next, a seeond swaging step, using swaging hammers 44, is performed upon the thinn2r end portion to reduce its O.D. but to produce an l.D.which is the same as the LD. of the annular thicker section. This provides the spindle bore.

As shown in Fig. 5, the spindle bore may be machined, if necessary, to produce its final accuracy. Sufficient stock may be provided for machining the interior of the bore to its final wall surface as illustrated schematically by the dotted line 45.

If an additional wall thickness portion is desired in the spindle, such as is produced in the extrusion illustrated in Fig. 16, another swaging step can be performed to produce the stepped exterior of the spindle and the single diameter bore.

215.082 Although the swaging step is illustrated as utilizing Q mandrel to form the spindle bore, the mandrel can be eliminated, in which the case, the bore can be made accurate by machining.

The extrusion steps are pr~fersbly conducted cold9 that is, at rsom temperature, as mentioned above. Thus, all that is necessary to extrude the blank, which is precut to si~e, may be the applicat;on of a coating of a lubricant, such as a phosphate to facilitate extrusion. Thus, preparation for the extrusion steps is minimal. Likewise, the swaging steps and the handling of the material during the swaging is minimal so as to reduce time and labor in formingthe completed one-piece axle~pindle.

Having fully described an operative embodiment of this invention, I now claim:

Claims (6)

1. A process for extruding an integral spindle and axle tube, comprising the steps of:

positioning a relatively short, tubular blank within an open ended, tubular die having an inlet end through which the blank is inserted and an opposite extrusion end formed by an annular, inwardly extending, continuous shoulder forming a die extrusion throat through which the blank is extruded, and with the throat diameter being larger than the inner diameter of the blank;

inserting a punch into the die inlet end, with the punch closely fitted within the die and having an annular shoulder engaged against the free end of the blank, and having a first punch extension closely fitted within the interior wall of the blank, and having a second punch extension of a smaller diameter than the blank interior diameter extended through part of the blank and die throat, and having a third punch extension, which is formed on the punch co-axial with and extending from the second punch extension, but of a smaller diameter than the second punch extension, with the punch shoulder and punch extensions being located co-axially with each other and also with the blank and die throat, and with the second punch extension being located between the first and third punch extensions;

next, moving the punch towards the die throat so that the punch shoulder rams the blank towards the die throat, and simultaneously aligns its second punch extension within the die throat to thereby extrude the lead end of the blank through the annular space between said second punch extension and the die throat to thereby form one thickened end of the metal tube;

continuing moving the punch so that the first punch extension aligns with the die throat to thereby extrude the blank through the annular space between the first punch extension and the throat to form a relatively thin wall metal tube middle portion;

then removing the punch from the die, and inserting a second tubular blank within the die in full end to end contact with the trailing end of the partially extruded blank;

reinserting the punch in the die with its punch shoulder engaging the trailing end of the second blank, and with the punch first extension closely fitted within the second blank, so that the punch second extension is aligned with but spaced from the die throat, and the third punch extension is positioned within the die throat;

moving the punch in the direction of the die throat to extrude a portion of the first, partially extruded, blank through the annular space between the die throat and third punch extension to form a relatively thick ring section adjacent the trailing end of the partially extruded blank, and thereafter proceeding with the step of moving the punch so that the second punch extension moves within the die throat and the second blank pushes the remainder of the first, partially extruded, blank through the annular space between the second punch extension and the die throat to form an inwardly thickened end portion on the trailing end of the first blank, and also, simultaneously extrudes an inwardly thickened end portion on the leading end of the second blank;

then removing the extruded first blank and continuing and repeating the cycle on the second and successive blanks;

on each removed extruded blank, swaging radially inwardly, to a uniform outside diameter which is less than the extruded tube external diameter, both the thick ring section and the tube trailing end portion, i.e., the portion located between the thick ring section and the trailing end of the tube;

then swaging radially inwardly only said tube trailing end portion until its internal diameter is about the same as the thick ring section internal diameter and its outside diameter is less than the thick ring section outside diameter, to thereby form an integral spindle and axle tube.

2. A process as defined in claim 1, and including inserting a mandrel within the thick ring section and the trailing end portion prior to swaging for thereby forming the internal diameter upon the mandrel.

3. A process for extruding an integral spindle and axle tube, comprising the steps of:

positioning a relatively short, tubular blank within an open ended, tubular die having an inlet end through which the blank is inserted and an opposite extrusion end forming a die extrusion throat through which the blank is extruded, with the throat diameter being larger than the inner diameter of the blank;

inserting a punch into the die inlet end, with the punch closely fitted within the die and having an annular shoulder engaging against the free end of the blank and having a punch extension closely fitted within the interior wall of the blank;

moving the punch towards the die throat so that the punch shoulder rams the blank towards the die throat, and simultaneously aligns the punch extension within the die throat to thereby extrude the blank through the annular space between said punch extension and the die throat to form a relatively thin wall metal tube;

stopping the punch movement before extruding the trailing end portion of the blank through the die throat;

removing the punch from the die, and inserting a second tubular blank within the die in end to end contact with the trailing end of the partially extruded blank;

inserting a punch in the die with its annular punch shoulder engaging the trailing end of the second blank, and with the punch extension closely fitted within the second blank, and with the punch having a smaller diameter extension-like insert aligned with, but spaced from the die throat;

moving the punch in the direction of the die throat to extrude a portion of the first, partially extruded, blank through the annular space between the die throat and the punch insert to form a relatively thick, inwardly extending, ring section spaced longitudinally inwardly of the trailing end of the partially extruded blank, and thereafter proceeding with the step of moving the punch so that the punch extension moves within the die throat and the second blank pushes the remainder of the first, partially extruded, blank through the annular space between the second punch extension and the die throat to extrude the tube trailing end portion on the trailing end of the first blank, and also, simultaneously extrudes the leading end of the second blank;

then removing the extruded tube formed from the first blank and continuing and repeating the cycle on the second and successive blanks;

swaging the thick ring section and tube trailing end portion of each extruded tube radially inwardly to a uniform outside diameter which is less than the tube external diameter;

then swaging radially inwardly only said tube trailing end portion until its internal diameter is approximately the same as the internal diameter of the thick ring section, and its outside diameter is less than the outside diameter of the thick ring section, to thereby form an integral spindle and axle tube.

4. A process as defined in claim 3, and including inserting a mandrel within the thick ring section and the trailing end portions of each tube prior to swaging the tube for thereby forming the internal diameter therein.

5. A method for forming integral spindles, having more than one wall thickness, and thin wall axle tubes, comprising:

extruding a uniform external diameter thin wall elongated tube of substantially uniform wall thickness, with an annular radially inwardly extending thickened section located near, but longitudinally spaced a distance from, one end of the tube;

swaging radially inwardly, to a uniform outside diameter which is less than the tube external diameter, both the thickened section and the tube end portion, i.e., the portion located between the thickened section and the tube end;

then swaging radially inwardly only said tube end portion until its internal diameter is about the same as the thickened section internal diameter and its outside diameter is less than the thickened section outside diameter, to thereby form an integral spindle and axle tube.

6. A method as defined in claim 5, and including the step of inserting a mandrel within the thickened section and tube end portion at least prior to the second swaging step, for forming a uniform internal diameter therein.