CA1040567A - Process for producing mesophase pitch - Google Patents

Abstract

PROCESS FOR PRODUCING MESOPHASE PITCH

ABSTRACT OF THE DISCLOSURE

An improved process for producing pitch which is transformed, in part, to a liquid crystal or so-called "mesophase" state. According to the process, the meso-phase content of the pitch is formed while agitating the pitch so as to produce a homogeneous emulsion of the immiscible mesophase and non-mesophase portions of the pitch. Mesophase pitches prepared in this manner have been found to possess a lesser amount of high molecular weight molecules in the mesophase portion of the pitch and a lesser amount of low molecular weight molecules in the non-mesophase portion of the pitch, and thus a smaller differential between the average molecular weights of the mesophase and non-mesophase portions of the pitch, than mesophase pitches having the same meso-phase content which have been prepared in the absence of such agitation.

Description

`
~L04~)S1~7 :
BACKGROU~D OF THE INVENTION

1. Field of the Invention m is invention relates to an lmproved process for producing carbon fibers from pitch which has been transformed, in part, to a liquid crystal or so-called "mesophase" state. More particularly, this invention relates to an improved process for producing carbon fi-bers from pitch of this type wherein the mesophase con-tent of the pitch has been formed while agitating the ` ;
pitch so as to produce a homogeneous emulsion of the im-miscible mesophase and non-mesophase portions of the pitch.
. .

2. Description of the Prior Art As a result of the rapidly expanding growth of ` ;
the aircraft, space and missile industries in recent years, a need was created for materials exhibiting a unique and ; ~.. .
extraordinary combination of physical properties. Thus, materials characterized by high strength and stiffness, ~;
and at the same time of light weight, were required for use in such applications as the fabrîcation of aircraft structures, re-entry vehicles, and space vehicles, as well as in the preparation of marine deep-submergence pres-sure vessels and like structures. Existing technology was incapable of supplying such materials and the search to satisfy this need centered about the fabrication of composite articles.
One of the most promlsing materials suggested ~. .

~`,"; ,, ' : - .;
1g~41~S67 for use in composite form was high strength, high modulus ; carbon textiles, which were introduced into the market place at the very time this rapid growth in the aircraft, ;
space and missle industries was occurring. Such textiles have been incorporated in both plastic and metal matrices `i`
to produce composites having extraordinary high-strength-and high-modulus-to-weight ratios and other exceptional properties. However, the high cost of producing the high-strength, high-modulus carbon textiles employed in such composites has been a major deterrent to their widespread , use, in spite of the remarkable properties exhibited by such composites.
One recently proposed method of providing high-modulus, high-strength carbon fibers at low cost is described in United States patent 4,005,183, en-titled "High Modulus, High Strength Carbon Fibers Pro-duced From Mesophase Pitch". Such method comprises first `
spinning a carbonaceous fiber from a carbonaceous pitch which has been transformed, in part~ to a liquid crystal or so-called "mesophasel' state, then thermosetting the fiber so produced by heating the fiber in an oxygen-con-taining atmosphere for a time sufficient to render it in-fusible, and finally carbonizing the thermoset fiber by heating in an inert atmosphere to a temperature suffi-ciently elevated to remove hydrogen and other volatiles and produce a substantially all-carbon fiber. The carbon fibers produced in this manner have a highly oriented -,~, .

,j . .

.' ',~

~ 4alS67 structure characterized by the presence of carbon crystal-lites preferentially aligned parallel to the fiber axis, and are graphitizable materials which when heated to . ;.
graphitizing temperatures develop the three-dimensional order characteristic of polycrystalline graphite and graph~tic-like properties associated therewith, such as - high density and low electrical resistivity. At all i stages of their development from the as-drawn condition to the graphitized state, the fibers are characterized by the presence of large oriented elongated graphitizable ;~
domains preferentially aligned parallel to the iber axis.
When natural or synthetic pitches having an aro-matic base are heated under quiescent conditions at a temperature of about 350C.-500~C., either at constant tem-perature or with gradually increasing temperature, small insoluble liquid spheres begin to appear in the pi~ch and gradually increase in size as heating is continued. When examined by electron diffraction and polarized light tech-niques, these spheres are shown to consist of layers of oriented molecules aligned in the same d~rection. As these spheres continue to grow in size as heating is con-tinued, they come in contact with one another and gradu- ' ally coalesce with each other to produce large masses of aligned layers. As coalescence continues, domains of aligned molecules much larger than those of the original ... .. .
spheres are fonmed. These domains come together to form a bulk mesophase wherein the transition from one . .. . ..
~4-.. ..

lL~4~S67 oriented domain to another sometimes occurs smoothly and continuously through gradually curving lamellae and some-- - times through more sharply curving lamellae. The differ- -ences in orientation between the domains create a complex ;
array of polarized light extinction contours in the bulk mesophase corresponding to various types of linear dis-continuity in molecular alignment. The ultimate size of the oriented domains produced is dependent upon the vis-cosity, and the rate of increase of the viscosity, of -the mesophase from which they are formed, which, in turn are dependent upon the particular pitch and the heating rate. In certain pitches, domains having sizes in excess of two hundred microns up to in excess of one thousand mi-crons are produced. In other pitches, the viscosity of the mesophase is such that only limited coalescence and structural rearrangement of layers occur, so that the ul- `
timate domain size does not exceed one hundred microns.
The highly oriented, optically anisotropic, in-soluble material produced by treating pitches in this man- r~
ner has been given the term "mesophase", and pitches con-taining such material are known as "mesophase pitches". `
~uch pitches, when heated above their softening points 3 are mixtures of two essentially immiscible liquids, one the optically anisotropic, oriented mesophase portion, and the other the isotropic non-mesophase portion. The term "mesophase" is derived from the Greek "mesos" or "inter-mediate" and indicates the pseudo-crystalline nature of this ~ ..

"` ' 104~67 highly-oriented, optically anisotropic material.
Carbonaceous pitches having a mesophase content of from about 40 per cent by weight to about 90 per cent ~
by weight are suitable for spinning into fibers which can ~-subsequently be converted by heat treatment into carbon fibers having a high Young's modulus of elasticity and high tensile strength. In order to obtain the desired fibers from such pitch, however, it is not only necessary that such amount of mesophase be present, but also that it form, under quiescent conditions, a homogeneous bulk mesophase having large coalesced domains, i.e., domains of aligned molecules in excess vf two hundred microns up to in excess of one thousand microns in size. Pitches which form stringy bulk mesophase under quiescent condi-tions, having small oriented domains, rather than large coalesced domains, are unsuitable. Such pitches form `-mesophase having a high viscosity which undergoes only limited coalescense, insufficient to produce large co- ` -. ~ . .
alesced domains having sizes in excess of two hundred mi-crons. Instead, small oriented domains of mesophase ag- ;

glomerate to produce clumps or stringy masses wherein the ; ultimate domain size does not exceed one hundred microns.

Certain pitches ~hich polymerize very rapidly are of this -type. Likewise, pitches which do not form a homogeneous ! bulk mesophase are unsuita~le. The latter phenom~enon is ;~ caused by the presence of infusible solids (which are ; either present in the original pitch or which develop on ~ ~ 9332-1 ~

" ` 1.0~05~7 heating) which are enveloped by the coalescing mesophase and serve to interrupt the homogeneity and uniformity of the coalesced domains, and the boundaries between them.
Another requirement is that the pitch be non-thixotropic under the conditions employed in the spinning of the pitch into fibers, i.e., it must exhibit a New~onian -~or plastic flow behavior so that the flow i9 uniEorm and - well behaved. When such pitches are heated to a tempera-ture where they exhibit a viscosity of from about 10 poises ~ -10 to about 200 poises, uniform fibers may be readily spun ~ -therefrom Pitches, on the other hand, which do not ex-hibit Newtonian or plastic flow behavior at the tempera-ture of spinning, do not permit uniform fibers to be spun therefrom which can be converted by further heat treatment into caxbon fibers having a high Y~ung's modulus of elas-ticity and high tensile strength.
~ Carbonaceous pitches having a mesophase content ; of from about 40 per cent by weight to about 90 per cent by weight can be produced in accordance with known tech-20 niques, as disclosed in aforementioned United States patent 4,005,183, by heating a carbonaceous pitch in an inert atmosphere at a temperature above about 350C.
for a time sufficient to produce the desired quantity of mesophase. By an inert atmosphere is meant an atmosphere which does not react with the pitch under the heating con-ditions employed, such as nitrogen, argon, xenon, helium, ~ ~
and the like. The heating period required to produce `:
~ , 9332-1 ~

' ~ . ;'~ .,' ,: ' ` ~04~)567 ~ ~
the desired mesophase content varies with the particular pitch and ~emperature employed, with longer heating periods required at lower temperatures than at higher temperatures.
At 350~C., the minimum temperature generally required to produce mesophase, at least one week of heating is usually necessary to produce a mesophase content of about 40 per ; cent. At temperature of from 400C. to 450C., conver-sion to mesophase proceeds more rapidly, and a 50 per cent mesophase content can usually be produced at such tempera-tures within about 1-40 hours. Such temperatures are generally employed for this reason. Temperatures above about 500C. are undesirable, and heating at this tempera-ture should not be employed for more than about 5 minutes to avoid conversion of the pitch to coke. ;
As the pitch is heated to a temperature suffi-ciently elevated to produce mesophase, the more volatile `~
low molecular weight molecules present therein are slowly volatilized from the pitch. As heating is continued above ,, ', .: . ~ .
a temperature at which mesophase is produced, the more reactive higher molecular weight molecules polymerize to fonm still higher molecular weight molecules, which then orient themselves to form mesophase. As aforementioned, - this mesophase first appears in the fonm of small liquid ;~
spheres which gradually increase ~n size and coalesce with each o~her as heating is continued to form larger masses of mesophase. These coalesced masses have a den~
sity greater than that of the non-mesophase portion of ~ ~ .

-8- ~

~ ~04056~ ~
the pitch, and9 as a result, tend to settle to the bottom of the reaction vessel as polymerization proceeds, while the lighter non-mesophase portion of l:he pitch tends to rise to the upper portlon of the vessel. After these co-alesced masses of mesophase form and settle to the bottom of the reac~ion vessel, the molecules therein, which are of higher molecular weight than the molecules which com-prise the non-mesophase portion of the pitch, continue to polymerize with each other to produce molecules of even higher molecular weight. At the same time, the unoriented molecules ln the non-mesophase portion of the pitch at the top of the reaction vessel likewise continue to polymerize to produce molecules of higher molecular weight, some of which orient themselves to produce mesophase, and some of which remain unoriented. As more and more mesophase is formed by the polymerization of the more reactive higher molecular weight molecules, it continues to gradually co-alesce ~d settle to the bottom of the reaction vessel, Ieaving the lower molecular weight molecules behind in the isotropic portion of the pitch at the upper portion of the reaction vessel.
This tendency of the immiscible mesophase and non-mesophase por~ions of the pitch to separate into two fractions during preparation of the mesophase is thus seen -to result in the productlon of a pitch having a high average molecular weight in the mesophase portion of the pitch and a low average molecular weight in the non-meso-~ 9332 -1 ' ' '. :;:
4~S67 ` :::
phase portion of the pitch. This uneven molecular weight distribution has been found to have an adverse effect on the rheology and spinnabil~ty of the pitch, evidently be-cause of a low degree of compatlbility between the very high molecular weight fraction of the mesophase portion of the pitch and the very low molecular weight fraction of the non-mesophase portion of the pitch. The very high molecular weight material in the mesophase portion of the pitch can only be adequately plastic;zed at very high tem-peratures where the tendency of the very low molecular -~eight molecules in the non-mesophase portion of the pitch to volatilize is greatly increased. As a result, when such pitches are heated to a temperature where they have a viscosity suitable for spinning and attempts are made to produce fibers therefrom, excessive expulsion of ;
volatiles occurs which greatly interferes with the process-ability of the pitch into fibers of small and uniform ~;
diameter. For these reasons~ means have been sought for producing pitches having a narrower molecular weight distribution so as ~o impart more favorable rheological properties to the pitch.
: ' ,"
SUMMARY OF THE INVENTION

In accordance with the present invention, it has now been discovered that mesophase pitches having im~
proved rheological and spinning characteristics can be pre-pared by agitating the pitch during formation of ~:he meso- ~;
...
-10- ~:

933~1 - , 10~0567 phase so as to produce a homogeneous emulsion ~f the im-miscible mesophase and non-mesophase portions of the pitch. -Mesophase pitches prepared in this manner have been found to possess a smaller differential between the number aver-age molecular weights of the mesophase and non-mesophase portions of the pitch than mesophase p~tches having the same mesophase content which have been prepared in the ab-sence of such agitation. The attendant rheological and ~
spinning properties accompanying this narrower molecular ~;
weight distribution has been found to substantially facili-tate the processability of the pitch into fibers of small , and uniform diameter.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

The agitation employed in the process of the present invention should be sufficient to effectively intermix the immiscible mesophase and non-mesophase por-tions of the pitch. Such agitation can readily be effected by conventional means, e.g., by stirring or rotation of the pitch.
When mesophase pitches ha~ing a mesophase content of at least 40 per cent by weight are prepared under qui-escent conditions, i.e., in the absence of agitation, more than 80 per cent of the molecules in the mesophase portion of the pitch have a molecular weight in excess of 4000, while the remaining molecules have a number average molecu-lar weight of from 1400 to 2800. At the same time~ the , .. . ,, . ~ . ... . ... ...... .... . . , .. ,., .. .,, ... , . . , ... . _ .......... . ... .... " , .. .. . . .
.. ...

:

: ~ ~04~67 molecules in the non-mesophase portion of the pitch have a number average molecular weight of less than 800, with in excess of 25 per cent of such molecules having a molecu-lar weight of less than 600. In general, t~e higher the mesophase eontent of the pitch, the broader the molecular weight distribution. As aforementioned9 the lack of com-patibility between the very low molecular weight fraction ; of the non-mesophase portion of the pitch and the very high molecular weight fraction of the mesophase portion of the pitch adversely affects the rheology and spinnability -of the pitch.
On the other hand, mesophase pitches prepared . . .
under the conditions o the invention, i.e., by agitating the pitch during formation of the mesophase=so as to pro-duce a homogeneous emulsion of the immiscible mesophase and non-mesophase portions of the pitch, have been found . .
to possess a smaller differential between the number aver-age molecular weights of the mesophase and non-mesophase ~.
portions of the pitch, and, therefore, improved rheologi- ~;
cal and spinning characteristics which substantially fa-cilitate the processability of such pitches into fibers of small and uniform diameter. Thus, such pitches have , been found to possess a lesser amount of high molecular weight molecules in the mesophase portion of the pitch and a lesser amount of low molecular weight molecules in the non-mesophase portion of the pitch, and to have a lower number average molecular weight ln the mesophase portion - . _v ~ . . ., . . .:.
: ~ . . . . .. . .. .

10~(~56~ :
of the pitch and a higher number average molecular weight in the non-mesophase portion of the pitch, than mesophase pitches having the same mesophase content which have been prepared in the absence of agita~ion.
When mesophase pitches are prepared in accordance with the invention by agitating the pitch during formation `
.. . of the mesophase, less than 50 per cent of the molecules in the mesophase portion of the pitoh have a molecular :. weight in excess of 4000, while the remaining lecules have a number verage molecular weight of from 1400 to 2800.
The molecules in the non-mesophase portion of such pitches have a number average molecular weight of from 800 to 1200, with less than 20 per cent of such molecules having a lecular weight of less than 600. Usually from 20 per .
cent to 40 per cent of the molecules in the mesophase por- -~
tion of the pitch have a molecular weight in excess of 4000, while the remaining molecules have a number average molecu-lar weight of from 1400 to 2600. The molecules in the non-mesophase portion of the pitch usually have a number aver-age molecular weigh~ of from 900 to 1200, with from 10 per eent to 16 per cent of such molecules having a molecu-lar weight of less than 600. When mesophase pitches are ; prepared without agitation, on the other hand, more than 80 per cent of the molecules in the mesophase portion of the pitch have a molecular weight in excess of 4000, while in excess of 25 per cent of tha molecules i~ the non-mesophase portion of the pitch have a molecular weight .. , ~.
. .

~332-1 ~ ~ 5~7 :
of less than 600. The molecules in the non-mesophase por-tion of the pitch have a number averag~e molecular weight of less than 800, while the number average molecular weight of the molecules inlthe mesophase portion of the pltch which do not have a molecular weight in excess of 4000 is : .
from 1400 to 2800.
. While any temperature above about 350C. up to .: .
about 500~C. can be employed to convert the precursor :
pitch to mesophase, it has been found that heating at ele- i~
vated temperatures adverseLy alters the molecular weight distribution of both the mesophase and non-mesophase por- . .
tions of the pitch, and that improved rheological and spin-ning characteristics are not obtained at such elevated temperatures. Thus, heating at elevated temperatures tends -to increase the amount of high molecular weight molecules in the mesophase portion of the pitch. At the same time, heating at such temperatures also results in an increased amount of low molecular weight molecules in the non-meso-phase portion of the pitch. As a result, mesophase pltches of a given mesophase content prepared at elevated tem-peratures in relatively short periods of time have been .~ :
~ found to have a higher average molecular weight in the ~ .:
mesophase portion of the pitch and a lower average molecu~
lar weight in the non-mesophase portion of the pitch, ``
than mesophase pitches of like mesophase content prepared :
at more moderate temperatures over re extended periods.
Therefore, in order to maximize reduction of thle differen- .

. .

. , -, , - . . "., , . :

~ C~4~)~67 tial between the number average molecular weights of the mesophase and non-mesophase portions of the p~tch, and produce pitches having the most desirable rheological and spinning characteristics, the mesophase is produced at a temperature of from 380C. to 440C., most preferably - from 380C. to 410C., so as to produce a mesophase con-tent of from 50 per cent by weight to 65 per cent by weight.
Usually from 2 hours to 60 hours of heating are required at such temperatures to produce the desired amount of meso-phase. Mesophase pitches prepared under these conditions have been found to possess a smaller d~fferential be-- tween the number average molecular weights of the mesophase and non-mesophase portions of the pitch, than mesophase pitches having the same mesophase content which have been prepared at more elevated temperatures in shorter periods of time. Thus, such pitches possess a lesser Rmount of high molecular weight molecules in the mesophase portion - of the pitch and a lesser amount of low molecular weight molecules in the non-meQophase portion of the pitch, and have a lower number average molecular weight in the meso-phase portion of the pitch and a higher number average molecular weight in the non-mesophase portion of the pitch, than mesophase pitches having the same mesophase content which have been prepared at more elevated tem-peratures in shorter periods of time.
Another means of lessening the amount of low molecular weight molecules in the non-mesophase portion of .~ '''' ,.
~ -15- <
' , . .
: ~04~567 the pitch and raising the average molecular weight thereof, comprises su~jecting the pitch to reduced pressure during formation of the mesophase, or passing an inert gas through the pitch at such time. Such procedure has also been found to substantially reduce the time required to - produce a pitch of a given mesophase content at a given temperature.
As aforementioned, as a carbonaceous pitch is heated to a temperature sufficiently elevated to produce mesophase, the more volatile low molecular weight mole-cules present therein are slowly volatilized from the pltch. As heating is con~inued above a temperature at which mesophase is produced, the more reactive higher :
molecular weight molecules polymerize to form Btill higher ; molecular weight molecules, wh~ch then orient themselves to form mesophase. While the less reactive lower molecu~
lar weight molecules which have not been volatilized can also polymerize, they often form hydrogenated andtor sub- ` -stituted polymerization by-products having a molecular weight below about 600 which do not orient to form meso-phase. Although these low molecular weight polymerization by-products are gradually volatilized as heating of the pitch is continued9 the presen~e of large amounts of these by-products during much of the time that the pitch is being converted to mesophase has been found to impede the formation of mesophase by the more reactive molecules, and, as a result, to considerably lengthen the time neces--16- ;

. .. . . .
,..... ~. , . ., . , . . , : . . .

.:
.. ~

sary to produce a pitch of a given mesophase content. Fur-,~.............................................................................. .
ther, because of their small size and low aromaticity, these polymerization by-products are not readily compatible with the larger, higher molecular weight, more aromatic molecules present in the mesophase portion of the pitch, and the lack of compatibility between these high and low molecular weight molecules adversely affects the rheology ~ and spinnability of the pitch. As pointed out previously, ::, the very high molecular weight fraction of the mesophase portion of the pitch can only be adequately plasticized ; at very high temperatures where the tendency of the very low molecular weight molecules in the non-mesophase por-tion of the pitch to volatilize is greatly increased, and when pitches having large amounts of such materials are heated to a temperature where they have a viscosity suit-able for spinning and attempts are made to produce fibers ~ ~herefrom, excessive expulsion of volatiles occurs which ; greatly interferes with the processability of the pitch into fibers of small and uniform diameter.
By subjecting the pitch to reduced pressure dur-ing formation of the mesophase, or passing an inert gas through the pitch at such time, advantage may be taken of the differences in molecular weight and volatility between the mesophase-fonming molecules present in the pitch and -- those low molecular weight components and polymerlzation by-products which do not form mesophase to effect removal of the undesira~le more volatile low molecular weight ~;~
" ''' ;; '`

-17- ~

.,' ', 9332-~

materials and mor~r~pVi~y convert the pitch to mesophase.
Those molecules which do not convert to mesophase are of lower molecular weight than the higher molecular weight ~`
.~ ... .
mesophase-forming molecules and, ~acilitated by the .... .
vacuum present during conversion of the pitch to meso-phase, or the inert gas purgë, are preferentially volatil-ized from the pitch during formation of the mesophase, allowing the pitch to obtain a given mesophase content `;
. ` , . . .
in substantially shorter periods of time. Mesophase ;
pitches having a mesophase content of from about 50 per cent by weight to about 65 per cent by weight can be pre~
pared in this manner, at a given temperature, at a rate ,` `
of up to more than twice as fast as that normally required in the absence of such treatment, i.e., in periods of time as little as less than one-half of that normally required when mesophase is produced in the absence of reduced pres-sure or without an inert gas being passed through the pitch. Generally, the time required to produce a pitch of a given mesophase content is reduced by at least 25 per cent, usually from 40 per cent to 70 per cent, when the mesophase is prepared under vacuum as described, or while passing an inert gas through the pitch as described, - ;
as opposed to when it is prepared under identical condi- x tions but in the absence of such treatment. ;
Removal of the more volatile components of the ..~. ~, ;'J pitch which do not convert to mesophase is effected by subjecting t~e pitch to a pressure of less than about 100 . . .

.. ` . ' .
~ : .

933~1 ., , 40S6'7 millimeters Hg, preferably less than 30 millimeters ~g, or by passing an inert gas through the pitch, during prepara-- tion of the mesophase, at a rate of at least 0.5 scfh. per ~ pound of pitch, preferably at a rate of 0.7 scfh. to 5.0 ,. .
scfh. per pound of pitch. Any inert gas which does not re-act with the pitch under the heating conditions employed ; can be used to facilitate removal of these components.
Illustrative of such gases are nitrogen, argon, xenon~
helium, steam and the like.
Mesophase pitches produced in accordance with the invent~on usually exhibit a viscosity of from 10 poises to 200 poises at a temperature of from 320C. to 440C., and can readily be spun into fibers o~ small and uniform diameter at such temperatures with little evolution of volatiles; Because of their excellent rheological proper- -ties, such pitches are eminently suitable for spinning ; carbonaceous fibers which may subsequently be converted by heat treatment into fibers having a high Young's modulus of elasticity and high tensile strength.
The degree to which the pitch has been converted to mesophase can readily be determined by polarized light microscopy and solubility examinations. Except for cer-tain non-mesophase insolubles present in the original ;~
pitch or which, in some instances, develop on heating~ the ;
non-mesophase portion of the pitch is readily soluble in ~;
organic solvents such as quinoline and pyridine, while ~' "- ' .

:
-19- ,~ ,:
,.'' ~.... . .
......... . ... .. . . . . . .

- ~ .'. , .
l 4~567 the mesophase portion is essentially insoluble. In the case of pitches which do not develop non-mesophase in-solubles when heated, the insoluble content of the heat treated pitch over and above the insoluble content of the pitch before i~ has been heat treated corresponds essen-tially to the mesophase content. In the case of pitches ;;~
which do develop non-mesophase insolubles when heated, the ; -,~ . ;.. . .
insvluble content of the heat treated pitch over and above ;~
- the insoluble content of the pitch before it has been heat treated is not solely due to the conversion of the pitch ; to mesophase, but alfio represents non-mesophase insolubles which are produced along with the mesophase during the heat treatment. Pitches which contain infusible non-meso-phase insolubles (either present in the original pitch or developed by heating) in amounts sufficient to prevent the development of homogeneous bulk mesophase are unsuitable for use in the present invention, as noted above. Gen- `-; erally, pitches which contain in excess of about 2 per cent by weight of such infusible materials are unsuitable. The presence or absence of such homogeneous bulk mesophase re-gions, as well as the presence or absence of infusible non-mesophase insolubles, can be visually observed by polarized . ~ .
(1) The per cent of quinoline insolubles {Q.I.) of a given pitch is determined by quinoline extraction at 75C. The per cent of pyridine insolubles (P. I.) is determined by Soxhlet extraction in boiling pyridine ~115C ).
~2) The ~nsoluble content of the untreated pitch is gen-erally less than 1 per cent (except for certain coal tar pitches) and con~ists largely of coke and carbon black -found in the original pitch.
..
~ -20-. . .. . . .. . . . . . . . . .. . . ... . .. . .. .... . ...... ..... . .. .. . ... ..

.

~04~567 - light microscopy examination o the pitch (see, e.g., Brooks, J. D., and Taylor, G. H., "The Formation of Some Graphitizing Carbons," ChemistrY and Physics of Carbon, Vol. 4, Marcel Dekker, Inc., New York, 1968, pp. 243-268;
and Dubois, J., Agache, C., and White, J. L., "The Car-- bonaceous Mesophase Formed in the Pyrolysis of Grap~itizable Organic Materialsj" Metallography 3, pp. 337-369, 1970).
The amounts of each of these materials may also be visually estimated in this manner.
Conventional molecular weight analysis techniques can be employed to determine the molecular weight character-istics of the mesophase pitches produced in accordance with the present invention. In order to permit molecular weight determinations to be conducted independently on both the mesophase and non-mesophase portions of the pitch, the two phases may be conveniently separated through thP use of a suita~le organic solvent. As noted above, except for certain non-mesophase insolubles present in the original pitch or which, in some instances, develop on heating, the non-meso-A 20 phase portion of the pitch is readily soluble in organic solvents such as quinoline and pyridine, while the mesophase `;
portion is essentially insoluble.( ) After separation of ;~ the two phases with a solvent in this manner, the non- `
mesophase portion of the pitch may be recovered from ~he solvent by vacuum distillation of the solvent.
~ ~.. . ..
.. .

(3) me non-mesophase portion of the pitch may readily be separated from the mesophase portion by extraction with -~
quinoline at 75~C. or by Soxhlet extraction in boiling pyridine.

"~ .

~4~S67 One means which has been employed to determine the number average molecular weight of the mesophase pitches produced in accordance with the present lnvention involves the use of a vapor phase osmometer. ~he utilization of in-struments of this type for molecular weight determinations has been described by A. P. Brady et al. (Brady, A. P., Huff, H., and McGain, J. W., J. Phys. & Coll. Chem. 55, 304, ~1951)). The osmometer measures the difference in electrical resistance between a sensitive reference thermis-tor in contact wlth a pure solvent, and a second thermis-tor in contact wlth a solution of said solvent having dis-solved therein a known concentration of a material whose molecular weight is to be detenmined. The difference in electrical resistance between the two thermistors i5 caused ~ -by a difference in temperature between the thenmistors which is produced by the different vapor pressures of the solvent and the solution. By comparing this value with the ;~
differences in resistance obtained with said solvent and standard solutions of said solvent containing known con-centrations of compounds of known molecular weights, it is possible to calculate the molecular weight of the solute material. A drop of pure solvent and a drop of a solution ;
of said solvent having dissolved therein a known concentra-tion of the material whose molecular weight is being de- -termined are suspended side by side on a reference thermistor and sample thenmistor, respectively, contained in a closed thermostated chamber saturated ~ith solvent ;;. . . . ~ .. . .

: ' .

104Q567 ~ ~
vapor, and the resistance of the two thermistors is mea-- sured and the difference between the two recorded. Since a solution of a given solvent will always have a lower va-por pressure than the pure solvent, a differential mass transfer occurs between the two drops and the solvent vapor phase, resulting in greater overall condensation on (and less evaporation from) the solution drop than on the sol-vent drop. This difference in mass transfer causes a tem-porary temperature difference between the two thenmlstors (due to differences in loss of heat of vaporization be-tween the two drops) which is proportional to the differ-ence in vapor pressure between the two drops. Since the .;. .,;
difference in vapor pressure between the two drops, and hence the difference in temperature and resistance, (~ R), between the two thermistors depends solely upon the number of molecules of the solute material dissolved in the sol-vent, and i8 independent of the chemical composition of the molecules, the mole fraction of solute in the solution, (N), .. . .. .
;;
can be determined from a plot of ~R vs. N for such solvent and solutions of such solvent containing known concentra-tions of compounds of known molecular weight.(4) ~ R and `~

N bear a direct linear relationship to each other, and ``
; ~ . .
from a detexmination of N it is possible to calculate the ~4) By the mole fraction of a given material in a solution3 (N), is meant the number of moles of such material in the ~;
solution divided by the number of moles of such material in the solution plus the numbex of moles of the solvent.
, ,` . ':

' ,:

~ i4~67 calibratlon constant, (K), for the solvent employed from the formula:

K = - N

Having determined the value of K, the molecular weight of the material may be determined from the formula: ;

~ = (K - ~R) M y W x _ wherein ~ is the molecular weight of the material upon which the determination is being made, K is the calibration constant for the solvent employed, ~R is the difference in resistance between the two thermistors, ~ is the molecular weight of the 601vent, Wy is the weight of the solvent~ and Wx is the weight of the material whose molecular weight is being determined. Of coursej having once determined the ~
value of the calibration constant of a given solvent, (K), ~`
the molecular weight of a given material may be determined directly from the formula.
While the molecular weight of the soluble portion of the pitch can be determined directly on a solution thereof9 in order to determine the molecular weight of the ~nsoluble portion, it is necessary that it first be solu-bilized, e.g., by chemical reduction of the aromatic bonds of such material with hydrogen. A suitable means for solubilizing coals and carbons by reduction of the aromat-! iC bonds of these materials has been described by 10~3567 J. D. Brooks et al. (Brooks, J. D.; and Silberman, H., "The Chemical Reduction of Some Cokes and Chars"~ Fuel 41, pp. 67-69, 1962). This method involves the use of hydro-gen generated by the reaction o lithiumiwith ethylene-diamine, and has been found to effectively reduce the aro-matic bonds of carbonaceous materials without rupturing carbon-carbon bonds. Such method has been suitably em-ployed to solubilize the insoluble portion of the pitches prepared in accordance with the invention.
Another means which has been employed to determine the molecular weight characteristics of the mesophase pitches produced in accordance with the present invention is gel permeation chromatography (GPC). This technique has been described by L. R. Snyder (Snyder, L. R., "Determination ~ `
of Asphalt Molecular Weight Distributions by Gel Permeation `~
Chromatography", Anal. Chem. 41, pp. 1223-1227, 1969). A ~ ;
gel permeation chromatograph is employed to fractionate a solution of polymer or polymer related molecules of various sizes, and the molecular weight distribution of the sample i8 determined with the aid of a detection system which is linearly responsive to solute concentration, such as a dif-ferential refractometer or a differential ultraviolet ab-sorption spectrometer. As in the case of the vapor phase osmometry technique, in order to permit molecular weight determinations to be conducted independently on both the mesophase and non-mesophase portions of the pitch, the two phases must first be separated through the use of a suitable '` ' ' -25- :

;

4~ S6~
organic solvent. Again, while the molecular weight of the soluble portion of the pitch can be determined directly on a solution thereof, ~n order to determine the molecular weight of the insoluble portion, it is necessary that it . first be solubilized.
Fractionation of the sample whose molecular weight distribution is being determined is effected by dissolving the sample in a suitable solvent and passing the solution through the chromatograph and collecting measured fractions of the solution which elute through the separation column of the chromatograph. A given volume of solvent is required to pass molecules of a given molecular size through the chromatograph, so that each fraction of solution which elutes from the chromatograph contains molecules of a given molecu-lar size. The fractions which flow through the column first contain the higher molecular weight molecules, while the fractions which take the longest time to elute through the column contain the lower molecular weight molecules.
After the sample has been fractionated, the con-centration of solute in each fraction is determined by means of a suitable detection system, such as a differential re-fractometer or a differential ultraviolet absorption spec- ~ -trometer. When a differential refractometer is employed, the refractive index of each fraction is automatically com-pared to that of the pure solvent by means of two photo-electric cells which are sensitive to the intens:Lty of light passing through such fractions and solvent, and the differ-...

~ - . . ...,~ . .. .
.

` 9332 -1 ~

.
~ O 4~ 5~ 7 ences in signal intensities between the two cells are auto-ma~ically plotted against the cum~lative elution volume of the solution. Since the magnltude of these d~fferences in signal intensity is linearly relatecl to the concentra-tion by weight of solute molecules present, the relative con-centration by weight of molecules in each fraction can be de- ;~
termined by dividing the differential signal intensity for that fraction by the total integrated differential signal intensity of all the fractions. This relative concentration may be graphically depicted by a plot of the difEerential signal intensity for each fraction against the cumulative elution volume of the sample.
The molecular weight of the molecules in each fraction can then be determined by standard techniques~
e.g., by the osmometry techniques described above. Since most conventional pitches are composed of similar types of lecular species, once the molecular weights of the various fractions of a particular sample have been determined, that sample may be used as a standard and the molecular weights of the fractions o subsequent samples can be determined from the known molecular weights of like fractions of the standard. Thus, molecular weight determinations need not be repeatedly made on each fraction of each sample, but may be obtained from the molecular weights determined for like fractions of the standard. For convenience, a molecu- -lar weight distribution curve depicting the relatlonship of ~he molecular weight to the elution volume of the -27- ;
,:

.; . ~.

4~567 . standard may be prepared by plotting the molecular weights determined for the standard fractions against the cumula-tive elution volume of the standard. The molecular weights of the molecules of the various chromatographic fractions of any given sample can then be directly read from this curve. As aforementioned, the relative concentration by - weight o~ solute molecules in each fraction can be detenmined by differential refractive index measurements.
To facilitate the molecular weight determinations9 the differential signal intensities and elution volume values obtained on a given sample, together with previously `
determined molecular weight data relating to the various chromatographic fractions of a standard pitch, can be proce~sed by a computer and transcribed into a complete molecu~ar weight distribution analysis. By thls procedure~
complete printouts are routinely provided of number average molecular weight (Mn), welght average molecular weight ~ ), ~;
molecular weight distribution parameter (MW/Mn), as well as a compilation of molecular weight and percentage by weight of solute present in each chromatographic fraction of a sample.
Aromatic base car~onaceous pitches having a car- `
bon content of from about 92 per cent by weight to about 96 per cent by weight and a hydrogen content of from about 4 per cent by weight to about ~ per cent by weight are generally suitable for producing m~sophase pitches which can be employed to produce fibers capable of being heat .... . ... . .... . . . .. . . . .. .. . .. . . .. . . . .
, :~
9332-1 ~

1(~4~1567 treated to produce fibers having a high Young's modulus of elasticity and a high tensile strength. Elements other than carbon and hydrogen, such as oxygen, sulfur and nîtro-gen, are undesirable and should not be present in excess of about 4 per cent by weight. The presence of more than :~
such amount of extraneous elements may disrupt the forma-tion of carbon crystallites during subsequent heat treat-ment and prevent the development of a graphitic-like struc-ture within the fibers produced from these materials. In addition, the presence of extraneous elements reduces the carbon content of the pitch and hence the ultimate yield of carbon fiber. When such extraneous elements are presen~
in amounts of from about 0.5 per cent by weight to about 4 per cent by weight, the pitches generally have a carbon con-tent of from about 92-95 per cent by weight, the balance being hydrogen.
Petroleum pitch, coal tar pitch and acenaphthylene pitch, which are well-graphitizing pitches, are preferred starting materials for producing the mesophase pitches which are employed to produce the fi~ers of the instant ~nvention.
Petroleum pitch, of course, is the residuum carbonaceous material obtained from the distillation of crude oils or the catalytic cracking of petroleum distillates. Coal tar -pitch is similarly ob~ained by the distillation of coal.
Both of the materials are commercially available natural pitches in which mesophase can easily be produced, and are preferred for this reason. Acenaphthylene pitch, on the ' , ', , .

-29- ~

" . .

. ~
~46~56i7 ::
other hand, is a synthetic pitch which is preferred because of its ability to produce excellent fibers. Acenaphthylene pitch can be produced by the pyrolysis of polymers of acenaphthylene as described by Edstrom et al. ~n U. S.
Patent 3,574,653.
Some pitches, such as fluoranthene pitch, poly-merize very rapidly when heated and fail to develop large coalesced domains of mesophase and are, therefore, not suit-able precursor mater~als. Likewise, pitches having a high infusible non-mesophase insoluble content in organic sol-vents such as quinoline or pyridine, or those which develop ~ ;
a high infusible non-mesophase insoluble content when heated, should not be employed as starting materials, as explained above, because these pitches are incapable of developing the homogeneous bulk mesophase necessary ~o produce highly oriented carbonaceous fibers capable of being converted by heat treatment into carbon fibers having a high Young's modulus of elasticity and high tensile strength. For this reason, pitches having an infusible quinoline-insoluble or pyridine-insoluble content of more than about 2 per cent by weight (determined as described above) should not be employed, or should be filtered to remove this material before being heated to produce mesophase. Preferably, such pitches are filtered when they contain more than about 1 per cent by ``
weight of such infusible, insoluble material. ~ost pe-troleum pitche~ and synthetic pitches have a low infusible, insoluble content and can be used directly without such ... ... , .. .... .. .. . .. . . .. . . . ... . ~ ,.,, . ,. .... ... .. . . ... .. . . ~

.

~^'` '~'.
:~)4~567 ~ filtration. Most coal tar pitches, on the other hand, have .
a high infusible, ~nsoluble content and require filtration before they can be employed.
As the pitch is heated at a temperature between 380~C. and 440C. to produce mesophase, the pitch will, of course, pyrolyze to a certain extent and the composition of the pitch will be altered, depending upon the tempera-ture, the heating time, and the composition and structure of the starting n~terial. Generally, however, after heating a carbonaceous pitch for a time sufficient to produce a meso-phase content of from about 50 per cent by weight to about 65 per cent by weight, the resulting pitch will contain a carbon content of from about 94-96 per cent by weight and a hydrogen content of from about 4-6 per cent by weight. When -such pitches contain elements other than carbon and hydro- ; ~-; gen in amounts of from about O.S per cent by weight to about 4 per cent by weight, the mesophase pitch will generally -have a carbon content of from about 92-95 per cent by weight, .
the balance being hydrogen.
After the desired mesophase pitch has been pre-; pared, it is spun into f~bers by conventional techniques, e.g., by melt spinning, ~entrifugal spinning, blow spinning, or in any other known manner. As noted above, in order to obtain highly oriented carbonaceous fibers capable of being heat treated to produce carbon fibers having a high Young's , ~ . .. .
modulus of elasticity and high tensile strength, the pitch mus~, under quiescent conditions, form a homogeneous bulk . .

~" :

,~ .. . ... . .

' 1~4~S67 -mesophase having large coalesced domains, and be nonthixo-tropic under the conditions employed ~n the spinning. Fur-.
ther, in order to ob~ain uniform fibers from such pitch, the pitch should be agitated lmmediately prior to spinning so as to effectively intermix the immiscible mesophase and non-mesophase portions of the pitch.
The temperature at which the pitch is spun depends, of course, upon the temperature at which the pitch exhibits a suitable viscoslty. Since the softening temperature of the pitch, and its viscosity at a given temperature, in-creases as the mesophase content and molecular weight of the pitch increases, the mesophase content and molecular weight should not be permitted to rise to a point which raises the softening point of the pitch to excessive levels. Pitches prepared in accordance with the invention and containing a mesophase content of about 50 per cent by weight usually have a viscosity of about 200 poises at about 320C. and about 10 poises at about 400C., while pitches containing a mesophase content of about 65 per cent by weight exhibit ~-similar viscosities at about 370C. and 440C., respectively.
Within this viscosity range, fibers may be conveniently spun from such pitches at a rate of from about 50 feet per minute to about 1000 feet per minute and even up to about 3000 feet per minute. Preferably, the pitch employed ex-hibits a viscosity of from abou~ 30 poises to about 150 poises at temperatures of from about 340C. to about 380C.
At ~uch viscosity and tempe~ature, un~form fibers having ~ r `
~(~4~567 ~ `:
d~ameters of from about 5 microns to about 25 microns can be easily spun. As previously mentioned, however, ~n or-der to obtain the desired fibers, it is important that the pitch be non-thixotropic and exhibit Newtonian or plastic flow behavior during the spinning of the flbers.
The carbonaceous fibers produced in this manner are highly oriented graphitizable materials having a high degree of preferred orientation of their molecules parallel to the fiber axis. By "graphitizable" is meant that these fibers are capable of being converted thermally (usually `
by heating to a temperature in excess o about 2500C., e.g., from about 2500C. to about 3000C.) to a structure having the three-dimensional order characteristic of polycrystalline graphite.
The fibers produced in this manner, of course, have the same chemical composition as the pitch from which ;
they were drawn, and like such pitch contain from about 50 per cent by weight to about 65 per cent by weight mesophase.
When examined under magnification by polarized light micros-copy techniques, the fibers exhibit textural variations which `
give them the appearance of a "mini-composite". Large elongated anisotropic domains, having a fibrillar-shaped ;
appearance, can be seen distributed throughout the fiber.
These anisotropic domains are highly oriented and prefer-entially aligned parallel to the fiber axis. It is believed that these anisotropic domains, which are elongated by the ~hear forces exerted on the pitch during spinning oE the 933~1 ~0~0~67 ~ -fibers, are not composed entirely of mesophase, but are also made up of non- mesophase. Evidently, the non-mesophase is oriented, as well as drawn lnto elongated domains, dur-ing spinning by these shear forces and the orienting ef-fects exerted by the mesophase domains as they are elongated.
Isotropic regions may also be present, although they may not be visible and are difficult to differentiate from those anisotropic regions which happen to show extinction. Charac-teristically, the oriented elongated domains have diameters in excess of 5000 A9 generally from about 10,000 A to about 40,000 A, and because of their large size are easily ob-served when examined by conventional polarized light micros-copy techniques at a magnif~cation of 1000. (The maximum re-solving power of a standard polarized light microscope hav-ing a magnification factor of 1000 is only a few tenths of a micron [1 micron = 10,000 A] and anisotropic domalns hav-ing di~ensions of 1000 ~ or less cannot be detected by this technique.) Because of the thermoplastic nature of the car-bonaceous fibers produced in accordance with the instant invention, it is necessary to thermoset these fibers before they can be carbonized. Thenmosetting of the fibers is - readily effected by heating the fibers in an oxygen-con-taining atmosphere for a time sufficient to render them infusible. The oxygen-containing atmosphere employed may be pure oxygen or ~n oxygen-rich atmosphere. Most con-veniently, air is employed as the oxidiæing atmosphere.

' `' :, ~ S 67 The time required to effect thermosetting of the fibers w~ll, of course, vary with such factors as the par-ticular oxidizing atmosphere, the temperature employed, the diameter of the fibers, the particular pitch from which the fibers are prepared, and the mesophase content and molecular weight distribution of such pitch. Generally, however, ~ -thermosetting of the fibers can be effected in relatively short periods of time, usually in from about 5 minutes to about 60 minutes.
The temperature employed to effect thermosetting of the fibers must, of course, not exceed the temperature at which the fibers will soften or distort. The maximum tem-perature which can be employed will thus depend upon the -particular pitch from which the fibers were spun, and the mesophase content and molecular weight distribution of sueh pitch. The higher the mesophase content and the higher the average molecular weight of the pitch, the higher will be its softening temperature, and the higher the temperature which can be employed to effect thermosetting of the fibers.
At higher temperatures, of course, fibers of a given diame-ter can be thermoset in less time than is possible at lower temperatures. Fibers prepared from a pitch having a lower ;
mesophase content and/or a lower average molecular weight, on the other hand~ require relatively longer heat treatment at somewhat lower temperatures to render them infusible. `
A minimum temperature of at least 250~C. is gen-erally necessary to effectively thermoset the carbonaceous '`":
104~1S67 fibers produced in sccordance with the invention. Tempera-tures in excess of 400C. may cause melting andtor excessive burn-off of the fibers and should be avoided. Preferably, temperatures of from about 275C. to about 350C. are em ployed. At such temperatures, thermosetting can generally be effected within from about 5 minutes to about 60 min- -utes. Since it is undesirable to oxidize the fibers more than necessary to render them totally infusible, the fibers are generally not heated for longer than about 60 minutes, 10 or at temperatures in excess of 400C.
After the fibers have been thermoset, the infusible fibers are carbonized by heating in an inert atmosphere, such as that described above, to a temperature sufficiently elevated to remove hydrogen and other volatiles and produce a substantially all-carbon fiber. Fibers having a carbon content greater than about 98 per cent by weight can gen-erally be produced by heating to a temperature in excess of about 1000C., and at temperatures in excess of about 1500C., the fibers are completely carbonized.
Usually, carbonization is effected at a tempera-ture of from about lOOO~C. to about 2000C., preferably from about 1500C. to about 1900C. Generally, residence times of from about 0.5 minute to about 25 minutes, prefer- -ably from about l minute to about 5 minutes, are employed.
- While more extended heating times can be employed with good results, such residence times are uneconomical and, as a practical matter, there is no advantage in employing . . , . . . . ., . .. ., . ~ . .. .. . . . .. ,, ~ .

_ . . .. .
~ 4~ S~
such long periods.
In order to ensure that the rate of weight loss of the fibers does not become so excessive as to disrupt the fiber structure it is preferred to heat the fibers for a brief period at a temperature of from about 700~C. to about 900~C. before they are heated to their final carboni-zation temperature. Residence times at these temperatures of from about 30 seconds to about 5 minutes are usually sufficient. Preferably, the fibers are heated at a tem- ; `
perature of about 700C. for about one-half minute and then at a temperature of about 900Q C. for like time. In any event, the heating rate must be controlled so that the volatilization does not proceed at an excessive ra~e.
In a preferred method of heat treatment, con-tinuous filaments of the fibers are passed through a series . ~ ;
of heating zones which are held at successively higher tem- ;
peratures. If desired,the first of such zones may contain an oxidizing atmosphere where thermosetting of the fibers ~ ~
is effected. Several arrangements of apparatus can be ` ;
utilized in providing the series of heating zones. Thus, one furnace can be used with the fibers being passed through the furnace several times and with the temperature being increased each time. Alternatively, the fibers may be given a single pass through several furnaces, with each successive furnace being maintained at a higher temperature than that of the previous furnace. Also, a single furnace with several heating zones maintained at successively .
`: ' )567 higher temperature in the direction of travel of the fi-bers, can be used.
The carbon fibers produced in this manner have a highly oriented structure characterized by the presence of carbon crystallites preferentially aligned parallel to the fiber axis, and are graphltizable materials which when heated to graphitizing temperatures develop the threP-di-mensional order characteristic of polycrystalline graphite and graphitic-like properties associated therewith, such as high density and low electrical resistivity.
If desired, the carbonized fibers may be further heated in an inert atmosphere, as described hereinbefore, to a still higher temperature in a range of from about 2500C. to about 3300C., preferably from about 2800C. to about 3000~C., to produce fibers having not only a high degree of preferred orlentation of their carbon crystal-lites parallel to the fiber axis, but also a structure characteristic of polycrystalline graphite. A residence time of about 1 minute is satisfactory, although both shorter and longer times may be employed, e.g., from about 10 seconds to about 5 minutes, or longer~ Residence times longer than 5 minutes are uneconomical and unnecessary, but may be employed if desired.
The fibers produced by heating at a temperature above about 2500C., prefera~ly above about 2800~C., are characterized as having the three-dimensional order of polycrystalline graphite. This three-dimensional order , ':' ..

9332 -1 ~
.

~ 4~3l567 is established by the X-ray diffraction pattern of the fi-bers, specifically by the presence of the (112) cross-lat-tice line and the resolution of the (10) band into two distinct lines~ (100) and (101). The short arcs which constitute th~ (OOQ) bands of the pattern show the carbon crystallites of the fibers to be preferentially aligned . .
parallel to the fiber axis. Microdensitometer scanning - of the (002) band of the exposed X-ray film indicate this preferred orientation to be no more than about 10, usually from about 5 to about 10 (expressed as the full width at ;
half maximum of the azimuthal intensity distribution). Ap-parent layer size (La) and apparent stack height (Lc) of the crystallites are in excess of 1000 A and are thus too .
large to be measured by X-ray techniques. The interlayer : spacing (d) of the crystallites, calculated from the dis-tance between the corresponding (00~ diffraction arcs, is no more than 3.37 A, usually from 3.36 A to 3.37 A.
.,., ,: .
EXAMPLES
.` .
; The following examples are set forth for pur-poses of illustration so that those skilled în the art may better understand the invention. It should be under-stood that they are exemp~ary only, and should not be con-strued as limiting the invention in any manner.

. ' .
., ' ' ' -, . . , .. , . . .. . . . .. . . . ~

9332-l ~ 56 EXAMPLE 1 _ PRODUCTION OF MESOPHASE PITCH WITH AGITATION

A commercial petroleum pitch was employed to pro-duce a pitch having a mesophase content of about 52 per - cent by weight. The precursor p~tch had a number average molecular weight of 400, a denslty of 1.23 grams/cc., a softening temperature of 120C., and contained 0.83 per cent by weight quinoline insolubles (Q. I. was detenminecl by quinoline extraction at 75C.). Chemical analysis showed a carbon conten~ of 93.0%, a hydrogen content of 5.6%, a sulfur content of 1.1% and 0.044% ash.
The mesophase pitch was produced by heating 240 grams of the precursor pitch in a 350 milliliter reactor to a temperature of about 300C. over a one hour period, then increasing the temperature of the pitch from about ~`
300C.,to about 400C. at a rate of about 60C. per hour9 and maintalning the pitch at about 400C. for an additional 17 hours. The pitch was continuously stirred after it had been heated to 300ac. by means of a stirrer rotating at a speed of 300 rpm. so as to produce a homogeneous emulsion of the mesophase and non-mesophase portions of the pitch.
Argon gas was continuously bubbled through the pitch throughout the entire run at a rate of 1.2 scfh.~ w~ile an additional flow of about 2.6 scfh. of ar~on was passed through the dome of the reactor. Ater heating the pitch , for 17 hours at 400ac., the pitch was cooled while s~ir-.. . . . , .. , . . . _ .. . . . . .. .. .. . . . . . ... .... .. . . .. .. .. ...... .. . . .... ... .
... . . .

`,~ ;, .

~O~)S67 `; ::
ring was continued.
Twelve (12.0) grams of the pitch produced in r~
this manner was then separated into its mesophase and non~
mesophase components by extracting the non-mesophase por- ~ ~
tion with boiling pyridine (115~C.~ in a Soxhlet extractor. ~ -The pyridine soluble non-mesophase material (P. S.) was recovered from the pyridine by distilling the extract solu-tion under reduced pressure to volatilize the pyridine.
The recovered pyridine solubles were then dried in a vacuum oven at 11~C. to remove traces of pyridine, as were the pyridine insolubles (P. I.). Both materials were then weighed, from which it was determined that the pitch con-tained 52 per cent by weight pyridine insolubles (indicating a mesophase content of close to 52 per cent).
Exactly 1.07 grams of the pyridine insolubles .. . .
were then solubilized by reducing the aromatic bonds of this material with hydrogen generated by the reaction of lithium with ethylenediamine. The solid insolubles were added to 65 milliliters of anhydrous ethylenediamine, and the resulting suspension was stirred and maintained at a temperature of 80~C.-90C. while about 1.5 grams of lithium were added over a period of 2 hours. After the addition of lithium was complete, the entire mixture was r~fluxed for one hour. At the end of this time, the mixture was cooled, poured over ice and acidified with concentrated hydrochloric acid. The acidified mixture was then cen-trifuged and a solid brown product was collected. This ,, ,, ,, " ,. , , ~ . . . ....... ..... ~;.. ,, . ~ , .

~ ~ 9332-1 ,.
4~)5i67 material was washed repeatedly with distilled water until ~he wash water evidenced no conductivity (as determined by means of a conductivity meter) 9 and then filtered and dried. A total of 1.01 grams of reduceld pyridine insolubles were recovered, representing a 97 per clent y~eld.
The reduced pyridine insolubles were then ex-tracted with boiling toluene. Sixty-one per cent (61%) of this materi~l was found to be soluble ln toluene while the remaining thirty-nine per cent (39%) was insoluble.(5) Gel permeation chromatography determinations were made on a toluene soluble non-mesophase sample of the pitch and a toluene soluble reduced mesophase sample of the pitch (toluene soluble reduced pyridine insoluble portion of the pitch) employing dilute toluene solutions of these materials. Measurements were made at 80C. with the use of a chromatograph having a differential refractom : eter detector. The fractionating column had an equivalent distillation plate count of 800 plates per foot. About S0 chromatographic fractions were collected for each sample.
The refractive index of each fraction was automatically compared to that of the pure solvent by means of two - ;
photoelectric cells sensitive to the intensity of light passing through such fractions and solvent, and the dif-

(5) The insoluble material represents reduced pyridine insolubles having a molecular weight in excess of 4000, ~he upper molecular weight limit of the toluene solllble material.

!..

.' ~ .
~'' `.

: 1~4~5~7 fPrences in signal intensities between the two cells were automatically plotted against the cumulative elution volume of the samples to depict the relative concentration by weight of solute in each such fraction.
The number average molecular weight of 30 of the fractions was determined by vapor phase osmometry. From these determinations, a molecular weight distribu~ion curve de-picting the relationship of the molecular weight to the `-elution volume of the samples was prepared by plotting the molecular weight detenmined for the fractions against the cumulative elution volume of the samples. These curves were used as a standard to detenmine the molecular we~gh~s of the fractions of su~sequent samples.
The molecular weight data from the curves and t4e GPC data were processed by a computer and transcribed into a complete molecular weight distribution analysis.
The computer printout gave the number average molecular weight (Mn), weight average molecular weight ~Mw), molecu-lar weight distributlon parameter (MW/Mn), and a compila-tion of molecular weight and percentage by weight of solute present in each chromatographic fraction of both the toluene soluble non-mesophase and toluene soluble re-duced mesophase (toluene soluble reduced pyridine însoluble) samples. The number average molecular weight of ~he tolu-ene soluble reduced mesophase sample (toluene soluble re-duc~d pyridine insoluble portion of the pitch) was found to be 2525, while the weight average molecular weight of .

. , 4~1S67 this material was found to be 2830. The number average molecular weight of the 50 chromatographic fractions col-lected ranged from 750 to 4000.
The number average molecular weight of the toluene soluble non-mesophase sample was determined to be 640, and the weight average molecular weight was determined to be 677. Less than 13 per cent of the non-mesophase portion of the pitch (including toluene soluble and toluene insoluble material) had a number average molecular wei~ht : lo of less than 600.

The pitch could be easily spun ~nto fibers, and a considerable quan~ity of fibers 8-20 microns in diameter was produced by spinning the pitch through a spinnerette `
(0.013 inch diameter hole) at a temperature between 364~C.-370C. Since no plugging of the spinnerette and very ~;
little volatile evolution was observed during spinning, long spinning runs were possible without fiber breakage.
; A portion of the as-drawn fibers produced in this manner was placed in a furnace which had been preheated to 210C. The temperature of the furnace was then raised to 300C. at a rate of 4.3CC. per minute while oxy~en was passed through the furnace at a flow rate of 0.2 liters/
minute. The resulting oxidized fibers were totally in-fusible and could be heated at elevated temperatures with- ".~! ' out sagging. Ater heating the infusibl2 fibers to l900~C. --over a period of about 10 minutes in a nitrogen atmosphere, the fibers were found to have a tensile strength of 44 ;

, . , . . , " ... . .. ., . ., . ., . . . , ., , .. ,, , . . ~, . , .. " . .. . . .. ..... .. .

9332-1 ~

104~567 220 x 10 psi. and a Young's modulus of elastlcity of 42 x 10 psi. (Tensile strength and Young's modulus are the average values of 10 samples.) PRODUCTIO~ OF MESOPHASE PITCH WITHOUT AGITATION
, For comparative purposes, a mesophase pitch was prepared from the same precursor p~tch in a manner -~ s~milar to that described above but without stirring.
Two hundred and fifty-three grams (253 g.) of the pitch were placed in a 350 milliliter reactor, covered with a watch glass, packed in a sagger, and heated in a furnace ;~
in an inert atmosphere to a temperature of about 400~C.
at a rate of about 60C. per hour and maintained at this ;~
temperature for eight hours.
- A thirteen gram (13.0 g.) sample of the pitch ;
having a pyridine insoluble content of 50 per cent (indicating a mesophase content of close to 50 per cent) was separated into its mesophase and non-mesophase components and subjected to molecular weight determinations as described above. After reducing the pyridine insoluble portion of the sample with hydrogen generated by the reaction of lithium with ethylenediamine, the reduced pyridine insolubles were extracted with boiling toluene and found to contain ninety-one per cent (91%) toluene ;~
insoluble material and only nine per cent (9%) toluene soluble material.(5) (5) The insoluble material represen~s reduced pyridine in- -solubles having a molecular weight in excess of 4000, the upper molecular weight limit of toluene soluble material.

~ S6 7 ; Gel permeation chromatograph~ determinations showed the number average molecular weight of ~he toluene soluble reduced pyridine insoluble portion of the pitch (toluene soluble reduced mesophase sample of the pitch) to be 2150, and the weight average molecular weight of this material to be 2440.
The number average molecular weight of the toluene soluble non-mesophase portion of the pitch was determined by gel permeation chromatography to be 593, and the ~eight average molecular weight was detenmined to be ~27. More than 30 per cent of the non-mesophase portion of the pitch ``
(including toluene soluble and toluene lnsoluble material) had a number average molecular weight of less than 600.
The pitch could not be spun into fibers of less than 40 microns in diameter, although some f~bers in excess `
;' of 40 microns in diameter were obtained with difficulty at temperatures of about 380C. Long spinning runs were `
impossible due to frequent fiber breakage caused by plug- -~
glng of the spinnerette by the pltch and excess evolution of volatiles during spinning.

380~ C . ~EAT TREATED PITCH

A commercial petroleum pitch was employed to produce a pitch having a mesophase content of about 56 per cent by weight. The pre~ursor pitch had a number average molecular weight of 400, a density of 1.23 grams/cc., a . . ',: ' .. .

, ' ' ` .
~ 4V567 softening temperature of 120C. and contained 0083 per cent ; by weight quinoline insolubles ~Q.I. was determined by quinoline extraction at 75C.). Chemical analysis showed a carbon content of 93.~/~, a hydrogen content of 5.6%, a sulfur content of 1. 1~tD and 0.044% ash.
The mesophase pitch was produced by heating 65 pounds of the precursor petroleum pitch in a seve~ gallon reactor to a temperature of 380~C. at a rate of about 100C. ;~
per hour, and maintaining the pitch at this temperature for an additional fifty-one hours. The pitch was continuously stirred during this time by means of a stirrer rotating at a speed of 700-1200 rpm. 60 as to produce a homogeneous emulsion o the mesophase and non-mesophase portions of the pitch. Nitrogen gas was continuously bubbled through the ; pitch throug~.out the entire run at a rate of 50 scfh. `
Five (5.0) grams of the pitch produced in this - manner was then separated into its mesophase and non-meso-phase components by extracting the non-mesophase portion with boiling pyridine (115C.) in a Soxhlet extractor.
The pyridine soluble non-mesophase material (P.S.) was re-covered from the pyridine by distilling the extract solu-!,i tion under reduced pressure to volatilize the pyridine.
- The recovered pyridine solubles were then drled in a vacuum oven at 110C. to remove traces of pyridine, as were the pyridine insolubles tP.I.). Both materials were then weighed, frDm which it was determined that the pitch con-- tained 56 per cent by weight pyridine insolubles (indica-... . . ... .. . . . . . . . .. . .

. ,.. ,. ... ,,.. ,,.. ,, , " . ~ .

~ 933~1 ., ting a mesophase content of close to 56 per cent).
One (1.00) gram of the pyrid:Lne insolubles was then solubilized by reducing the aromatLc bonds of this material with hydrogen generated by the reaction of lithium with ethylenediamine. The solid lnsolubles were added to 65 millil~ters of anhydrous ethylenediamine, and the re-~ sultlng suspension was st~rred and maintained at a tem- , i perature of 80C.-90C. while about 1.5 grams of lithium -were added over a period of 2 hours. After the addition of -~ 10 lithium was complete, the entire mixture was refluxed for . ~:
. .
one hour. At the end of this time, the mixture was cooled, poured over ice and acidified wlth concentrated hydrochloric acid. The acidified mixture was then centrifuged and a solid brown product was collected. This material was ... . . .
washed repeatedly with distilled water until the wash water ,: :
evidenced no conductivity (as determined by means of a conductivity meter), and then filtered and dried. A total of 0 96 grams of reduced pyridine insolubles was recovered, representing a 96 per cent yield.
The reduced pyridine insolubles were then `~
extracted with boiling toluene. Sixty-eight per cent ~68%) of this material was found to be soluble in toluene while the remaining thirty-two per cent (3~/~) was ~nsoluble.( ~5) The insoluble ma~erial represents reduced pyridine ~ -insolubles having a molecular weight in excess of 4000, ~he upper molecular weight l~mit of toluene soluble material.

`

,~ .....

~ 9332-1 , ,. ~ .
~04iD567 ~
Gel permeation chromatography determinations were made on a toluene soluble non-mesophase sample of the pitch and a toluene soluble reduced mesophase sample of the pitch (toluene soluble reduced pyridine insoluble portion of the pitch) employing dilute toluene soluti.ons of these materials, as described above. The GPC data and the molecular weight data from the molecular weight distribution curve described in Example l were processed by a computer and transcribed into a complete molecular weight distribution analysis. The computer printout gave the number average molecular weight ~Mn)~ welght average molecular weight (MW?, molecular welght distribution parameter (~ lMn), a-nd a compilation of molecu-lar weight and percentage by weight of solute present in ' each chromatographic fraction of both the toluene soluble non-mesophase and toluene soluble reduced mesophase (toluene soluble reduced pyridine insoluble) samples. The number average molecular weight of the toluene soluble reduced mesophase sample (toluene soluble reduced pyridine in-soluble portion of the pitch) was found to be 2620, while the weight average molecular weight of this material was ~ r .
: .
found to be 2980. -~
.. ~ .
The number average molecular weight of the ` toluene soluble non-mesophase sample was determined to be ~`
616, and the weight average molecular weight was determined to be 652. Less than 16 per eent of the non-mesophase portion of the pitch (including toluene soluble and toluene insoluble materi~l) had a number average molecular _49_ ... ... .. , . _ .... ~ . . . . . . . . ... . .. . ... . . .. . .

y,~

: ` :
` 1~4~S67 weight of less than 600. The number average molecular weight of the entire non-mesophase portion of the pitch, determined by vapor phase osmometry on a pyridine soluble sample of the pitch, was found to be 1040.
The pitch couldbe easily spum into fibers, and a .. ~. .
considerable ~uantity of fibers 8-20 microns in diameter was produced by spinning the pitch through a 41-hole spin~
nerette (0.006 inch diameter holes) at a r~te of about 740 feet per minute between 350C.-380C. The filaments passed through a nitrogen atmosphere as they left the spinnerette : and before they were taken up by a reel. Since no plug-ging of the spinnerette and very little volatile evolution was observed during spinning, long spinning runs were pos-sible without fiber breakage.
A portion of the as-drawn fibers produced in this man-ner were heated to 298C. in air at a rate of 6C. per minute. The resulting oxidized fibers were totally infusi-ble and could be heated at elevated temperatures without sagging. After heating the infusible fibers to 1800C. over a period of about 60 minutes in a nitrogen atmosphere, the fibers were found to have a tensile strength of 241 x 10 psi. and a Young's modulus of e~asticity of 22 x 106 psi.
(Tensile strength ~nd Young's modulus are the average values of 10 samples.) -, .:.: . .
450C. HEAT TREATED PITCH

For comparative purposes, a mesophase ~itch was . , ~50-.. . .. . . . .

.
1¢~4~567 pr~pared from the same precursor pitch and ~n the same man-ner described above except that the pitch was heated to 450C. at a rate of 100C. per hour and held at this tem-perature for 1 1/4 hours. The resulting pitch had a .
pyridine insoluble content of 57 per cent, indicating a mesophase content of close to 57 per cent.
A portion of the pitch was separated into its mesophase and non-mesophase components and subjected to molecular weight determinations as described above. After reducing the pyridine insoluble portion of the pltch with hydrogen generated by the reaction of llthium with ethylene-diamine, the reduced pyridine insolubles were extracted with boiling toluene and found to contain eighty-two per cent (8~L) toluene insoluble material and only eighteen per cent (l~/o) toluene soluble material.( Gel penmeation chromatography determinations showed the number average molecular weight of the toluene soluble reduced pyridine insoluble portion of the pitch (toluene soluble reduced mesophase sample of the p~tch) to be 2190, and the weight average molecular weight of the material to be 2460.
The number average molecular weight of the toluene soluble non-mesophase portion of the pitch was determined by gel permeation chromatography to be 583 9 __ _ _ (5) The insoluble material represents reduced pyricline insolubles having a molecular weight in excess o 4000, the upper molecular weight limit of toluene soluble material.

~51-^ 9332-l , ; ' ','; ' 1¢~4~567 ~;
` and the weight average molecular weight was determined to be 617. More than 25 per cent of the non-mPsophase portion :~ ~
.: - . . , :
of the pitch (including toluene ~oluble and toluene in- :.

` soluble material) had a number average molecular weight of ; less than 600. The number average molecular weight of the : . , ~ entire non-mesophase portion of the pitch, determined by .
, vapor phase osmometry on a pyridine soluble sample of the .
pitch, was found to be 730. : :
The pitch could not be spun into fibers of less than 40 microns in diameter, although some fibers in ex-cess of 40 microns in diameter were obtained with diffi-culty at temperatures of about 370C. Long spinning runs were impossible due to frequent fiber breakage caused by plugging of the spinnerette by the pitch and excess evolu-tion of volatiles during spinning.

, : .
:'.~ ' ':
., :
,~ .,; , . .
.
~: . .
. .

',, `,'.:
`. .
.. : :

,..
.~,.;

-'.' ','' .', .
.' '`''''';''' -52- :

, .. . . . . ... .. . . ..... . . ..

Claims (6)

WHAT IS CLAIMED IS:

1. A process for producing a mesophase pitch having a mesophase content of from 50 per cent by weight to 65 per cent by weight which comprises heating a carbona-ceous pitch in an inert atmosphere at: a temperature of from 380°C. to 440°C. for a time sufficient to produce a mesophase content of from 50 per cent by weight to 65 per cent by weight while agitating the pitch during forma-tion of the mesophase so as to produce a homogeneous emulsion of the immiscible mesophase and non-mesophase portions of the pitch.

2. A process as in claim 1 wherein the meso-phase content of the pitch has been prepared while pass-ing an inert gas through the pitch during formation of the mesophase.

3. A process as in claim 1 wherein the pitch has been subjected to reduced pressure during formation of the mesophase.

4. A process as in claim 1 wherein the pitch is heated at a temperature of from 380°C. to 410°C.

5. A process as in claim 4 wherein the meso-phase content of the pitch has been prepared while passing an inert gas through the pitch during formation of the mesophase.

6. A process as in claim 4 wherein the pitch has been subjected to reduced pressure during formation of the mesophase.