AU605115B2 - Films of polypropylene blends and polyethylene blends and articles made therewith - Google Patents

Description

AUSTRALIA

Patents Act 005115 COMPLETE SPECIFICATION

(ORIGINAL)

Class Int. Class Application Number: 9:57,6 e,16.

Lodged: Complete Specification Lodged: Accepted: Published: Priority Related Art: This douet cont-ans th e amendments made under Section 49 and is currect for prioting.

CAPIflJTNS REF.: DOCKET NO. 14,360 Name(s) of Applicant(s): AM1E--I-CAN, CA-N-- PA-K-AGNG .NC. and BAXTER -TRAVENODL-LABOR-T-ORI--ES- INC.

fWTGnWR-n tON4L Address(es) of Applicant(s): Ameican-Lanel~ Greenwich,-Cohecticut, United States of America and One Baxter Parkway, Deerfield, Illinois. 60015. United States of America.

Actual Inventor(s): Roger Peter Genske, Yong Joo Kim, Russell Paul Gehrke, Richard Eugerie Johnson, Jr., R. Daniel Webster and Leonard F. Czuba Address for S, rvice is: PHILLIPS, CRMONDE AND FITZPATRICK Patent and Tradc Mark Attorneys 367 Collins Street Melbourne, Australia, 3000 Complete Specification for the invention entitled: FILMS OF POLYPROPYLENE BLENDS AND POLYETHYLENE BLENDS AND ARTICLES MADE THEREWITH The following statement is a full description of this invention, incltuding the best method of performing it knowvn to applicant(s): 1119/9/84

L

No legaliation or ASSistant General Counsel witne required Intelro rt Patents I, o: het uommlssfoner of Patents

I

o/ If D AS DW PHILLIPS ORMONDE FITZPATRICK Patent and Trade Mark Attorneys 367 Collins Street Melbourne, Australia 4 I I qr~ i 14,360 BACKGROUND OF THE INVENTION 0 0 0 0 o o o o 0,0 O o r 10 0 oa 0 0 o0 4B 0 00 0 0 0 o 04 0o o* 0 00 0 10 o oo 0 0 0 0 0 0 00 0 0 o 00 Polypropylene provides excellent resistance to high temperature processing, such as at retort conditions of about 2500F for about 30 minutes. Polypropylene has thus found widespread use, particularly as a sealant layer in pouches which are subjected to heat treatment after the pouch is filled with product and sealed.

While polypropylene has been accepted as the material of choice for use in sealant layers of retortable pouches, it has been selected more or less by necessity, as few other materials in the same general price range can provide similar high temperature processability.

Likewise, for some uses such as in contact with food or medical solutions, polypropylene is among the few materials which is approved for product contact. Thus, polypropylene provides a combination of desirable properties which is not found in other known materials.

Polypropylene does have associated undesirable properties. Most prominent in packages is the tendency of the polypropylene to be brittle, and to be even more brittle after is has been retort processed. The degree of brittleness of a package film is most easily detected by measuring the capability of a package to tolerate physically stressful treatment. Brittleness of the

I

1: 14,360 overall package is a property which is a composite of the brittleness of the individual layers, interfacial bond strengths, the elasticity of adjacent layers and their capability to absorb and dissipate physical shock, and any overwhelming brittleness of any one layer.

The composite brittleness of retort processed packages using polypropylene may generally be observed as the fraction of the packages which fail after being subjected to physical stress or shock.

161. Polyethylenes in the density range of about 0.91 to S about 0.965, and linear low density polyethylenes o (LLDPE) have many fine and desirable properties which ooO make them particulary suitable for many uses.

o. Polyethylene as used herein is defined as those ~polyethylenes, homopolymer and copolymer, which have a density in the range of about 0.91 to about 0.965, and LLDPE. Many PE's are stiff and rigid, able to hold 00o shape in thick sections. PE is readily processed and formed in both the solid form and the more fluid o plasticated form. It is relatively economical for many 000 uses. In packaging applications it has been found to provide a good barrier to transmission of water vapor.

And it is particularly the packaging application which oO is of interest to the inventors herein, while it will be seen that other applications may abound.

S0 High density polyethylene (HDPE, having a density greater than about 0.94) in particular is known to provide excellent properties of stiffness and resistance to transmission of moisture vapor. It also has acceptable high temperature processing capabilities.

-2-

I

14,360 0 o o o o o* o «a o 00 0 0 0 *0 00 0 0 0 0 0rt 0 O O t 20 ag 0 0 0 0 0 0 0 0 00 5 y*< It would be desirable to combine layers of polypropylene and PE into one packaging film to obtain the combined properties of high temperature processability, a strong heat seal, and resistance to water vapor transmission. The package should also have excellent tolerance of physical shock abuse.

Polypropylene and PE layers may be combined into a multiple layer film as by adhesive lamination. Such a construction, though, has undesirable cost disadvantage of the plurality of steps necessary in its fabrication.

Further, such films do tend to exhibit the brittleness which is a normal property of polyproyplene. The brittleness may be somewhat improved upon by using a polypropylene copolymer rather than the homopolymer.

While there is some improvement in performance with the use of the copolymer, the general level of brittleness is still so high as to be effective to prevent widespread use of such structures.

If, however, an economical structure could be made which would combine the desirable properties of polypropylene and PE while improving on the ability of the package to tolerate physical abuse, such a package may find substantial utility and acceptance. Such a structure may use novel compositions of matter in one or more layers, and might use particular combinations of layers and positional relationships to achieve the balance of properties desired.

It is an object of this invention to provide multiple layer films made from compositions of polymers.

rVOUC Ic-m~ i i 14,360 It is a specific object to provide multiple layer films suitable for use in retortable packages which have excellent tolerance to shock abuse both before and after retort processing.

A direct object is to provide closed and sealed packages having increased tolerance to shock abuse.

It is finally an object of the invention to provide novel process for making a multiple layer film w'ich is useful in packaging.

SUMMARY OF THE DISCLOSURE SOne embodiment of the invention is seen in multiple layer films containing a novel composition of matter which is a blend of polypropylene and an ethylenebased copolymer selected from the group consisting of o ethylene butene-1 copolymers and ethylene propylene c oo copolymers (hereinafter referred to as EBC) or (ii) an 0 0 elastomer, such as polybutylene, polyisobutylene, @@00o0 0 20 ethylene propylene diene monomer terpolymer, styrene o 8butadiene s'tyrene copolymer, styrene ethylene butylene "oo styrene copolymer, styrene isoprene styrene copolymer, o 044 o°o 0 polybutene-l, and isobutylene isoprene copolymer, [hereinafter, the aforesaid groups and (ii) of materials is referred to in the description/as the The terms elastomer" and "elastomeric" describe 27 polymers, copolymers, rubbers, and the like, which at -4- 1, f 14,360 room temperature can be stretched substantially under low stress, and upon immediate release of.the stress, have the tendency to return generally to approximately the original shape.

In preferred compositions of this embodiment, the blend is about 30% by weight to about 80% by weight polypropylene and about 70% by weight to about 20% by weight of a Modifier.

The EBC is essentially a copolymer of two moieties, both moieties being present in the main chain of the polymer. The overall mole ratio is about 10 to about mole percent ethylene, and conversely about 90 to about mole percent of the second moiety. The ethylene is preferably copolymerized with either propylene or butene-l. In the case of propylene, the mole ratio preferred range is about 60% to about 80% ethylene and about 40% to about 20% propylene. One such material is S0 sold by Mitsui Petrochemical Industries, Ltd. as TAFMER 4 P. In the case of butene-1, the mole ratio preferred range is about 5% to about 15% butene-1 and about 95% to about 85% ethylene. One such material containing butene-1 is sold by Mitsui Petrochemical Industries, 0.

Ia Ltd. as TAFMER A.

o 0 The multiple layer films of this invention include a basic two layer structure comprising first and second layers, wherein said first layer comprises a blend of a polypropylene polymer (preferably in the range of about to about 95%) chosen from the group consisting of polypropylene homopolymer and polypropylene copolymer, and a Modifier (preferably in the range of about 80% to irsH~- i' 14,360 about The second layer contains PE or PE blended with a Modifier. A second basic structure comprises said first and second layers and further includes a third layer adhered to the second layer wherein the third layer is a blend of polypropylene and a Modifier, preferably, an EBC.

Further, it is within the scope of this invention to provide films of more than three layers, wherein additional layers may be adhered to either of the outside surfaces of the first and third layers of the said basic three-layer structure. Preferably, such additonal layers are of the same composition of the first, second or third layers of the said basic Sthree-layer structurc.

The preferred composition of the second layer of I °the two- or three-layer basic structures is about 65% to about 95% of the PE (preferably HDPE) and about 35% to b a about 5% of the a Modifier, preferably EBC.

°o The invention is further embodied in packages, such as pouches, made from multiple layer films. While the particular form of the package is not critical, typical packages are fabricated from flexible film by the use of o Preferably, the multilayer films of this invention are coextruded but they may be made of other methods such as by lamination.

14,360 BRIEF DESCRIPTION OF THE DRAWINGS 4 44 44r 4 44.44 4 44 44 4 4444( 44 Ir I 40 4a 4: c 4.4 4 4r 4 4 4 C 041

OC

:20

IICI

I

00~e 00 0 44 40 28 FIGURE 1 is a cross-section of a two layer film of this invention.

FIGURE 2 is a cross-section of a three layer film of this invention.

FIGURE 3 is a pictorial view of a typical pouch-type package made from films of the invention.

FIGURE 4 is an enlarged cross-section of a portion of the pouch of FIGURE 3, and taken at 4-4 of FIGURE 3.

FIGURE 5 is a pictorial view of a preferred pouchtype package made from films of the invention.

FIGURE 6 is a cross-section of a five layer film of this invention.

DETAILED DESCRIPTION OF SPECIFIC EMBODIMENTS THE INVENTION Preferred embodiments of the invention are seen as multiple layer film structures.

One preferred embodiment of the invention is a two layer coextruded film having a first layer of polypropylene blend and second layer of PE blend. In this embodiment, the polypropylene layer and the PE layer are affixed to each other in face-to-face contact with each other, with gbod adhesion and preferably without the use of intervening adhesives.

Another preferred embodiment is a three layer film having first and third layers of polypropylene blends and a second layer of a PE blend. In this embodiment, L I f I 0 00 0 0 0 0 00 00 0 000 0o o0 o0 0 o o 0 000 0 00 o oo 0 000 0 o oo 0 002 00 0 0 00 20 0 0 0 0o o0 a oo 0 0 0 0 00 0 0 0 o 0 00 o 2 27 14,360 the first and third polypropylene layers are affixed in surface-to-surface contact with the second PE layer, on opposing surfaces thereof, preferably without the use of intervening adhesives.

Turning now to the drawings, FIGURE 1 represents a cross-sectional view of the basic two layer film structure of the invention. Layer 12 is a blend of a polypropylene and Modifier, preferably EBC. Layer 14 is a blend of a PE and a Modifier, preferably EBC.

Films of the embodiments of FIGURE 1 may be used for making packages wherein either layer 12 or layer 14 is on the outside, or conversely on the inside of a package made therefrom. The selection of specific polymers, blend compositions, and layer thicknesses and ratios depends on the end use contemplated.

FIGURE 2 represents a cross-sectional view of the basic three layer film structure of this invention. As in the two layer embodiment of FIGURE 1, layer 12 is a blend of polypropylene and Modifier, preferably EBC and layer 14 is a blend of a PE and Modifier, preferably EBC. Layer 16, is a blend of a polypropylene and Modifier, preferably EBC.

FIGURE 6 illustrates a five layer film of this invention comprising layers 12, 14, 16, 14 and 16. The composition of each layer is desirably the same as the composition of the like-numbered layer previously described, although the Modifiers may be different in some cases.

14,360 I The multilayer film of FIGURES 1,2 and 6 are especially useful for making pouches such.as the one h i seen in FIGURE 3. In a preferred method of formation of j| that pouch, portions of the film are brought in face-to-face contact with each other such that the layers 12 on both of the facing portions are facing each other. Heat seals 18 are formed about the common periphery of the facing portion to make an enclosed package capable of holding a product. After product is inserted into the package, a final heat seal is made across the open end to close and seal the package.

Referring specifically to the overall thickness of the films of FIGURES 1, 2 and 6, they are preferably between about 2 mils and about 8 mils thick. The lesser thickness of about 2 mils represents about the thinnest 0, film which has good tolerance of shock abuse in typical commercial handling of packages filled with a liquidous I 0product. The greater thickness of about 8 mils provides a film having essentially as much strength as can be o ,20 achieved economically in a flexible package. While greater film thicknesses are possible, functional, and are included in the invention herein, they are generally more costly, and so are not preferred, In the overall film structure of FIGURES 1, 2, and 00 0o0 6, layer 12 is the layer which is used as the inside 0 0 0o 00 surface layer, and to form the heat seals where the film is used in a heat sealed package. For these applications, the heat seal layer 12 should be at least about 1 mil thick, to facilitate formation of strong heat seals. Preferably, layer 12 has a thickness of

I

-II I 14,360 approximately 3 mils to about 4-1/2 mils thick. In a preferred embodiment of films having multiple layers, layer 12 comprises approximately 60% of the total thickness of the multilayer film. This provides a film that has good durability and forms excellent heat seals.

Moreover, this maximizes the sealant layer relevant to the maximum thickness of the film, while still achieving balanced film properties.

Layer 14 functions primarily as an effective barrier to infusion of moisture vapor. For this function, it should be at least about 0.5 mil thick.

While the minimum thickness of about 0.5 mil is usually effective for barrier purposes, a thickness of approximately 1 mil to about 1-1/2 mils is preferred.

This thickness provides a multilayer film that has good O0 clarity and flexibility while still providing a water vapor barrier. In a preferred embodiment, layer 14 oo 4 0o comprises approximately 20% of the total thickness of the multilayer film.

o 20 Layer 16 is typically used as the outside layer of oo0 o0oo the package, as seen in Figure 4. As such, it serves a primary function of providing resistance to penetration o 0 0 of the package as by puncture, cutting, or abrasion. To 0o serve this function, it requires a degree of physical 0 o substance in terms of thickness, and about 0.5 mil is 0 0 °0 0usually the minimum thickness which will provide this functional performance, so this is a preferred minimum thickness. For most typical applications, though, layer 16 is somewhat thicker, and a thickness of approximately 1 mil to about 1-1/2 mils is generally preferred. In a ~~1111 14,360 0 44 a 1 oo t o I 04 oo no o otI o it 006 0 4 04 O 44 o t *o a O 4 00 0 0 o 0 0 44 preferred embodiment, layer 16 comprises approximately of the total thickness of the multilayer film.

A secondary function of layer 16 is in its surface properties as they relate to other surfaces which it contacts in various machining operations, and as it is brought into contact with surfaces of other films or packages. As regards machining operations, sufficient surface friction is needed to enable drawing the film through packaging machines. However, high levels of friction are often associated with blocking, or sticking, of films together. Conventional slip and anti-block additives may be used as needed in any of the film layers, but are particularly applicable to layers 12 and 16, most particularly to layer 16. Where conventional additives are used, they are not considered herein in defining the percent of each component in the composition.

In the multilayer structures, the composition of each of the layers 12, 14 and 16 is a blend of polymer and a Modifier. The affect of the blending a Modifier into the layers is seen in a plurality of beneficial evidences. First, the interfacial adhesion between the PE layer and the adjacent polypropylene layers is enhanced by the inclusion of a Modifier in each of the layers. Second, the ability of packages fabricated from the multiple layer films of the invention to withstand shock abuse, bott before and after retort processing, is higher than for similar films which do not include EBC in the blend compositions. Finally, the films having a Modifier incorporated therein have improved capability ii I .i rl rn"- 14,360 to be flexed and folded repeatedly without developing cracks as a result of the flexing and folding.

The overall composition of layer 12 is preferably about 20% by weight to about 95% by weight, most preferably about 30% to about 80%, of a polypropylene polymer either homopolymer or copolymer or a blend of homopolymer and copolymer, and preferably about 80% by weight to about 5% by weight, most preferably about to about 20%, of a Modifier.

The overall range of compositions of layer 16 is the same as the range of compositions defined for layer 12. Layers 16 and 12 need not, however, have the same compositions. Their compositions may vary, independent of each other so long as they stay within the defind ranges of compositions for those layers.

Any of the known polypropylene polymers may be used for the polypropylene component of layers 12 and 16.

Included are both homopolymers and copolymers. Thus, wherever in the writing "polypropylene" is mentioned, t.

0 is intended to include both homopolymer and copolymer, except where otherwise specifically stated.

The overall composition of layer 14 is preferably about 2% by weight to about 50% by weight, most preferably about 5% to about 35% Modifier and, preferably, about 98% by weight to about 50% by weight, most preferably about 95% to about 65%, HDPE. In mostpreferred embodiments, the composition is at least 27 70% HDPE and no more than about 30% Modifier.

i_ 14,360 0 o 0 0 0 a 0 0 0 0 4 0 o 4 0o 00 0000 o a 20 00 00 o o4 0 00 0 00 0 0 0 0 00 0 0 0 0 In some cases, it may be advantageous that the Modifiers be different in adjacent layers, provided adequate adhesion is observed. However, enhanced adhesion may be obtained at the layer interface between a polypropylene polymer layer and an HDPE layer wherein both layers have the same Modifier as a component of the composition of each of the layers. A most preferred structure is one where the same EBC composition is used as a component of both layers. It is, however, typical that different fractions of the EBC composition be used in the different layers.

A coextrusion of polypropylene and HDPE without EBC had an interlayer adhesion of about 100 grams per inch width. A similar extrusion, but including 30% TAFMER A in the HDPE layer 14, and 40% TAFMER A in the polypropylene layer 12, had such good interlayer adhesion that it could not be separated, using the same conventional peel test.

In a further preferred method for forming packages from the films of the present invention a form, fill and seal packaging machine (not shown) can be utilized. In a typical form, fill and seal packaging machine the film is fed into the machine to a former for folding the web of film. The former is typically situated so that the sheet is folded around a dispensing tube. To create a sealed pouch, as shown in FIGURE 5, the packaging machine includes two sealing stations. At one sealing station an end seal 20 is created in the film and at the second sealing station a first side seal 21 is created in the film. After the first side seal 21 is created, ~Swrlr~-- 14,360 the product to be housed is dispensed into the film and a second side seal 22 is created to enclose the product.

After the second side seal 22 is created the film is severed and a filled flexible container 36 is thereby created as shown in FIGURE Also, illustrated in FIGURE 5 fitments 32 and 33 (which preferably are a single unit 34) may be sealed to the inside or outside layer of the container 36.

Preferably, the fitment 34 is heat sealed to the inside layer 12. Due to the construction of the inside layer 12, a strong heat seal is created.

Thus, the present invention creates films that can run through form, fill and seal packaging machines to create flexible pouches and containers 36 including a ~fitment 34 that can house a medical product to be maintained and extracted under sterile conditions.

o 1 0E 06 EXAMPLE 1 0 0.

00 0 o 0£1 20 0 1 D t a o 0 o aC U a 0 00 00 0 0 0 0 0 Pellets of a polypropylene'copolymer, having about 4.5 mole percent ethylene, are dry blended with pellets of a styrene ethylene butylene styrene elastomer Modifier in a weight ratio of about 75% polypropylene to about 25% elastomer Modifier. This blend of pellets is coextruded with a layer of the same polypropylene in unblended composition. The thickness of the thus formed two layer film is about 6.5 mils, with about 84% of the thickness bieng the blend layer and about 16% of the thickness being the unblended polypropylene copolymer layer.

~I

ii 14,360 EXAMPLE 2 Pellets of a polypropylene copolymer, having about mole percent ethylene, are dry blended with pellets of styrene ethylene butylene styrene Modifier in a weight ratio of about 75% polypropylene and about elastomer Modifier. This blend of pellets is coextruded with a layer of the same polypropylene in unblended composition. The thickness of the thus formed two layer film is about 6.5 mils, with about 75% of the thickness being the blend layer and about 25% of the thickness being the unblended polypropylene copolymer layer. EXAMPLE 3 A three layer film is made by coextruding high 44 9 density polyethylene blended with an elastomer Modifier o t.

0 4 between two layers of polypropylene blended with an elastomer Modifier. The polypropylene blend is about 75% by weight polypropylene and about 25% by weight styrene ethylene butylene styrene copolymer. Pellets of an ethylene propylene diene monomer terpolymer elastomer Modifier are dry blended with pellets of a high density 0o "a polyethylene in a weight ratio of about 2% elastomer oJ Modifier and about 75% high density polyethylene to form uu6 a the composition for the middle layer. A three layer film about 6.5 mils thick is thus formed by the coextrusion; the basic layer structure being PPE/HDPE/PPE, with elastomer modifications to the layers as indicated. The two layers of polypropylene copolymer 14,360 are about 33% and about 46% respectively of the overall film thickness. Correspondingly the high.density polyethylene layer is about 21% of the overall film thickness.

EXAMPLE 4 A three layer film about 6.5 mils thick is made by coextrusion as in EXAMPLE 3 using the same polypropylene blended with an elastomer Modifier as the two outer layers. The high density plyethylene layer is a blend of high density polyethylene and polyisobutylene, in a weight ratio of about 20% polyisobutylene and about Shigh density polyethylene. The two layers of polypropylene copolymer are about 39% and about Srespecitvely of the overall film thickness.

Correspondingly, the layer of high density polyethylene is about 21% of the overall film thickness.

00 CUo 0 a EXAMPLE A three layer film about 6.5 mils thick is made by o 0 coextrusion as in EXAMPLE 3 using the same polypropylene 0 oo blended with an elastomer Modifier as the two outer ao1 layers. The high density polyethylene layer is a blend of high density polyethylene and styrene butadiene styrene elastomer Modifier, in a weight ratio of about styrene ethylene butylene styrene copolymer and 29 about 80% high density polyethylene. The two layers of

V

14,360 polypropylene copolymer blend are about 27% to about 49% respectively of th.e overall film thickness.

V Correspondingly, the layer of high density polyethylene I blend is about 24% of the overall film thickness.

EXAMPLES 6-21 Additional 2-layer and 3-layer films were formed by coextrusion processes. The so-formed films were f fabricated into pouches by forming heat seals as i described hereinabove with reference to FIGURE 3. The pouches were filled to their capacity with about 1 liter I of liquid and were sealed closed. Some of the pouches r were then retort processed for about 30 minutes at about 250 0 F. The pouches, both those which were retort processed and those which were not, were then subjected Sto drop testing.

SIn the drop testing, the pouches were dropped in a free fall onto a hard surface. The height of the drop was increased, up to about 9 feet, until the pouches failed on impact. A failure was defined as rupture of the package, or a significant weakening of the package, particularly at the heat seals. If a package survived a maximum of the 9 foot drop, it was reported as 9 feet.

The results of the testing on EXAMPLES 6-21 are shown in the following Table i, wherein EXAMPLES 6-19 are pouches made of films of the present invention, and EXAMPLES 20 and 21 are pouches made of other films. The Table shows pouch film construction, film thickness, and the maximum successful drop heights for the pouches, -17- 39 i 14,360 where some of the pouches tested had been retort processed, and some had not been retort processed. The pouch film construction shows the weight percent of each component in each layer, ignoring conventional additives of slip and anti-block. Under each layer composition is the percent that the layer represents of the overall thickness of the entire film.

t 0 4 04 o *o 0 00 0 0 o 0o 0 0 0o 00000 1; 0 0 0 o -s 14,360 TABLE 1 Exanple Pouch Construction Film Maximun Successful No. Inner Layer Middle Layer Outer Layer Thickness Dropeight Mils Not Retort Retort Processed Processed op 0 0042 o to 0( f 0I( 00 0 00 00 4 0000 o *q *004

(I

0 00 o t.O* o 0 00o

PPE

Tafrer A

PPE

Tabrer A

PPE

Tafmer A 40% PPE 60% Tafmer A 70% PPE 30% Taftier P 80%

PPE

Tafmer P 60%

PPE

30% Tafmer P 83%

PPE

Tafmer 67% 70% HDPE 30% Tafmer A 20% 60% PPE 40% Tafmer A 98% HDPE 2% PB 98% HDPE 2% PB 20% 70% HDPE 30% Tafrer A 40% PPE 60% Tafer A 50% HDPE 50% Tafrier A 50% HDPE 50% Tafmer A 20% 70% PPS 30% Tafmer P 80% HDPE 20% SIS 17% 80% HDPE 20% SIS 16% 70% PPE 30% Tafmer P 17% I I i I IC ~1 1 I 14,360 TABLE 1, cont'd.

Exanpie Pouch Construction Film Maxinun Successful NO. Inner Layer middle Layer Outer Layer Thickness Dropeight Mils Not Retort Ptort. Processed Processed 0 00 00 0 Lo 00 00 8 0400 00o 0 0o 00 O s0 0 0 p~ 0 vooa 0 o 0 14 16 17 18 19 20 Ccuparative Exanple 21 Canparative Exanple 62% PPE 38% PIB 62% PPE 38% PIB 50% PP Tafmer A 50% PP 50% Tafmer A 60% 80% PP

SEBS

80% PPE

SEES

100% PP 80% 100% PP 60% 95% hDPE 5% PB 95% HDPE 5% PB 20% 90% HDPE 10% SEES 90% HDPE 10% SEES 20% 50% PP 50% Tafmer A 62% PPE 38% PIB 80% HDPE 20% SIS 80% HDPE 20% Tafmer P 100% HDPE 4 4.

4 100% HDPE 20% 100% PP .J .0 i _I 14,360 TABLE 1, cont'd.

PPE i Polypropylene copolymer PP Polypropylene homopolymer HDPE High Density Polyethylene SIS Styrene Isoprene Styrene Copolymer PIB Polyisobutylene SEBS Styrene Ethylene Butylene Styrene Copolymer PB Polybutylene As seen from the tabulated results, the pouches made from the films of this invention have superior drop test properties compared to pouches made of films other "than films of this invention.

The films described and illustrated herein may be used for a multiplicity of applications.

Advantageously, the films are used to form sealed pouches, preferably heat sealed pouches, and mostly advantageously such pouches which are filled with product and subjected to retort processing at 0 f temperatures of about 250 F. for times typically about 30 minutes. The term "films" typically refers to flexible sheet structures of up to about 8 mils thickness. As used herein, it is intended to also o include thicker sheet structures having semi-rigid or rigid properties. Such sheet structures having semi-rigid or rigid properties. Such sheet structures may be used to form semi-rigid or rigid trays, 28 decorative panels, and other moldings; and same are i _I 14,360 contemplated herein. Indeed, a container may be fabricated from a formed tray made from a-thicker structure of the invention and may have a thinner film lid also made from film of the invention.

The multilayer films of the invention are especially preferred for use in making packages which will be subjected to retort processing. Typical retort processing is at about 250 0 F. for about 30 minutes.

Temperatures may be as high as about 2750F.; time as long as about 45 minutes. Temperature and/or time of processing is adjusted according to particular needs or desires. For use with somewhat higher temperatures or somewhat longer processing times, films having higher fractions of polypropylene, within the iterated ranges, are used. Lower fractions of polypropylene are sometimes preferred when the package will not be subjected to more severe processing associated with the 'highest temperatures and longest times of retort processing.

Thus it is seen that the invention provides multilayer films containing novel compositions of polymers blended with Modifiers. The films are especially excellent for use as medical solution *containers and pouches. They are also excellent for forming in retortable packages and having excellent resistance to shock abuse both before and after retort processing.

Finally, the invention provides novel process for 29 making multiple layer films which are useful in packaging.

I i_

Claims (12)

1. A multiple layer film, comprising: a first layer, the composition of said first layer comprising a polypropylene homopolymer or copolymer and (ii) as a second component, a polymeric composition selected from the group consisting of ethylene butene-1 copolymer and ethylene propylene copolymer, said second component having elastic properties; and a second layer adhered to said first layer, the Second composition of said fir.st layer comprising high density polyethylene.

2. A multiple layer film comprising: a first layer, the composition of said first o° 15 layer comprising a polypropylene and (ii) as a o A oci/er; onc second component, polymeric compositionhaing elastic prop-e-t-fe-i-e-s;-a-]- a second layer adhered to said first layer, the composition of said second layer comprising (i) polyethylene and (ii) as a second component, a polymeric composition chosen from the group consisting of ethylene butene-1 copolymer and ethylene propylene copolymer, said second component having elastic properties. 0 0

3. A multiple layer film as in Claim 1, said second layer comprising a second component, said second component of said second layer being substantially the same as said second component of said first layer. 23 EJD U i

4. A multiple layer film as in Claim 2, said second component of said second layer being substantially the same as said second component of said first layer. A multiple layer film, comprising: first and third layers, each of said first and third layers comprising compositions of 40% by weight to 95% by weight of polypropylene and (ii) as second component, 5% by weight to 60% by weight of a Modifier; a second layer the composition of said second layer comprising polyethylene; said second layer being between said first and third layers. S 6. A multiple layer film as in Claim 5, said Modifier in 15 each of said first and third layers having elasticity properties and being selected from the group consisting of ethylene butene-l copolymer and (ii) ethylene propylene copolymer. 4,. S 7. A multiple layer film as in Claim 2 wherein said polyethylene in said second layer comprises high a density polyethylene.

8. A multiple layer film as in Claim 5 wherein said polyethylene in said second layer comprises high density polyethylene, said second layer further comprising a Modifier, said Modifier in said second layer being substantially the same as said Modifier in at least one of said first and third layers, said second layer being in surface-to-surface bonding contact with said at least one of said first and third layers. 3 24- U EJD T 0A

9. A multiple layer film as in Claim 5, said film comprising a fourth layer, the composition of the said fourth layer comprising a polypropylene, said third layer being between said second and fourth layers; and a fifth layer, the composition of said fifth layer comprising a polyethylene, said fifth layer being between the said third and fourth layers. A multiple layer film as in Claim 9, said fifth layer being in surface-to-surface contact with said third cnd fourth layers, said fourth and fifth layers conprising Modifiers such that good adhesion exists between said third and fifth layers and between said fourth and fifth layers.

11. A film as in any one of Claims 1 4 wher.fin said second layer comprises approximately 40% of the total thickness of said film.

12. A film as in any one of Claim 5 8 wherein said first layer comprises approximately 60% of the total thickness of said film and said third layer comprises approximately 20% of the total thickness of said film.

13. A multiple layer film of Claim 9 or 10 wherein said first layer comprises approximately 60% of the total thieknoess of said multiple layer film. 14, A film of any one of Claims 1 13, said film having o been fabr i'aoted using a coextrusion process in fabrication ot said first and second layeri,, A packacqo mido with a film of any one of Claims 1 14.

16. A package made with a film of any one of Claims 1 14, said package having been retort processed. EJtI _~I11_C

17. A flexible product to conditions, film of any container adapted to house a medical be maintained and extracted under sterile said container having been made with a one of Claims 1 14.

18. A multiple layer film according to claim 1, 2 or substantially as hereinbefore described with reference to any one of the examples. DATED: 10 September 1990 PHILLIPS ORMONDE FITZPATRICK Attorneys for: AMERICAN NATIONAL CAN COMPANY and BAXTER TRAVENOL LABORATORIES, INC. "i 3tp 26 EJD