AU2001293022A1

AU2001293022A1 - Processes to control the residual monomer level of copolymers of tertiary amino monomer with a vinyl-functional monomer

Info

Publication number: AU2001293022A1
Application number: AU2001293022A
Authority: AU
Inventors: Leo Zhaoqing Liu; Richard E. Rice; Dominic Wai-Kwing Yeung
Original assignee: Rhodia Inc
Current assignee: Solvay USA Inc
Priority date: 2000-09-27
Filing date: 2001-09-21
Publication date: 2002-06-20
Anticipated expiration: 2021-09-21

Description

PROCESSES TO CONTROL THE RESIDUAL MONOMER LEVEL OF COPOLYMERS OF TERTIARY AMINO MONOMER WITH A VINYL-

FUNCTIONAL MONOMER

FIELD OF THE INVENTION

The present invention relates to processes for controlling residual monomers while making copolymers of tertiary amino-monomer and vinyl- functional monomer able to undergo Michael addition. BACKGROUND OF THE INVENTION

Copolymers of tertiary amino-containing monomers and vinyl-functional monomers are useful in liquid detergent compositions for machine or hand dishwashing. For example, the copolymers are useful to maintain suds in hand dishwashing compositions. Such copolymers are also useful for products in the laundry field for a product having improved grease and soil removal properties, and in products in the personal care field, particularly hand soaps, body washes, shampoos, shaving creams, shaving gels and dephiliatories, which have improved foam retention. There is also a need for such polymers for improved oil field chemicals, agricultural chemicals, fire-fighting foam, detergents, mining chemicals, flocculants and coagulants.

SUMMARY OF THE INVENTION The present inventors discovered a problem. Namely, they discovered that copolymers of tertiary amino-containing monomers and vinyl-functional monomers formed monomers when heated. The present inventors also discovered the monomers resulted from unstable Michael addition adducts of the copolymers and vinyl-functional monomers which formed during production of the copolymer. The vinyl-functional monomers can be liberated from the adduct under certain conditions to be potentially toxic.

For purposes of this specification and claims, the term copolymer encompasses polymers of two or more different monomers, e.g., bipolymers (two different monomers) or terpolymers (three different monomers).

The present invention solves the aforementioned problem in that it has been surprisingly discovered that these polymeric materials can be made with a negligible amount of undesirable adducts or monomers. In the present invention, adduct formation is prevented/minimized by performing at least one of the following steps in a process for making copolymers from tertiary amino monomers and vinyl-functional monomers:

1. Avoid formation of adduct by separating the tertiary amino monomer (e.g. dimethylaminoethyl(meth)acrylate) from the vinyl-functional monomer prior to polymerization.

2. Avoid formation of adduct by avoiding contact of water with a mixture of the tertiary amino monomer and the vinyl-functional monomer prior to polymerization. 3. Conduct polymerization at a high temperature (typically about 70 to about 90°C, preferably about 80 to about 90°C) and at a suitable pH (typically about 3 to about 10, preferably about 4 to about 8, most preferably about 4 to about 6) to cause the adduct formed to be unstable and revert to monomers. Thus, monomers bound by the adduct will be liberated to copolymerize. Preferably, acid, e.g., mineral acid or citric acid, which is one of the reactants is fed to the reactor before the monomers.

Thus, the present invention provides methods for making compositions for hand dishwashing, personal care, particularly hand soaps, body washes, shampoos, shaving creams, shaving gels and dephiliatories, which have improved foam retention, improved oil field chemicals, agricultural chemicals, fire-fighting foam, detergents, mining chemicals, flocculants and coagulants.

The present process has many advantages. Conventional processes attempt to reduce monomers by employing high initiator concentration and long reaction times. In contrast, the present invention reduces monomer with less initiator and less reaction time than conventional processes for producing low residual monomer polymers. This saves processing time conventionally needed to react residual monomers and saves energy. Also, the present process has a synergistic benefit because the lower concentration of ingredients causes adducts to dissociate faster in the present process. These and other objects, features and advantages will become apparent to those of ordinary skill in the art from a reading of the following detailed description and the appended claims. All percentages, ratios and proportions herein are by weight, unless otherwise specified. All temperatures are in degrees Celsius (°C) unless otherwise specified. All documents cited are, in relevant part, incorporated herein by reference in their entirety. Additional background on compositions and methods of use is provided by PCT International Application Nos. PCT/US98//24853, PCT/US98/24707, PCT/US98/24699 and PCT/US98/24852, all incorporated herein by reference in their entirety.

BRIEF DESCRIPTION OF THE DRAWINGS

Fig. 1 shows a process flow diagram of a first embodiment of the present invention.

Fig. 2 shows a process flow diagram of a second embodiment of the present invention. Fig. 3 shows a process flow diagram of a third embodiment of the present invention.

DETAILED DESCRIPTION OF THE INVENTION The present invention relates to processes for producing high purity polymeric materials. High purity polymeric material means copolymers with low levels of residual monomers or adducts. These high purity materials are useful to provide enhanced suds/foam duration and enhanced suds/foam volume when formulated into liquid compositions suitable in the field of hand dishwashing, personal care (particularly for hand washing and/or body washing soaps, shampoo, shaving foam, shaving gel or dephiliatories), agricultural chemicals, e.g., agrochemical foams, oil well chemicals, e.g., oil well foams, fire fighting foams, and home care products, e.g., laundry detergents, shower rinses for bathroom use, and hard surface cleaner foams, mining chemicals, flocculants and coagulants, e.g. coagulants for treatment of titanium dioxide in paper plants. Among their other advantages, they also provide enhanced soil release for laundry detergents for use in washing machines. I. PROCESS STEPS

The desired reaction is to copolymerize at least one tertiary amino- containing monomer and at least one vinyl-functional monomer to form copolymers rather than Michael addition adducts. In the present process, the vinyl-functional monomers are not substituted by an alkyl group on the 2-position of the vinyl moiety (for example, not methacrylic acid, hydroxyethylmethacrylate or hydroxypropylmethacrylate) because Michael addition adducts do not form if the hydrogen atom was substituted by an alkyl group on the 2-position of the vinyl moiety.

An example of the desired reaction is the following polymerization reaction I of dimethylaminomethylmethacrylate (a tertiary amino-containing monomer known as DMAEMA) with hydroxyethylacrylate (a vinyl-functional monomer knows as HEA):

DMAEMA HEA

However, the present inventors discovered that an undesirable reaction, namely a formation of adducts, can also occur when these monomers are combined. The adduct formation occurs by a Michael addition reaction II as follows:

II.

A small amount of Michael addition adduct may also form by combining one monomer of tertiary amino-containing monomer and one monomer of vinyl- functional monomer as follows in reaction IIA.

The adducts are undesirable because they can liberate monomers under certain conditions. The amount of residual monomers in a commercial polymer product must meet a required, acceptable low level due to potential toxicity. Due to the relative stability of the resulting polymer-adduct at room temperature, the value of residual monomer as measured at room temperature is low. However, the value does not reflect the true amount since the adduct will dissociate upon heating liberating out the bound monomer. Thus, the actual value will be higher. Therefore, the inventors sought processing conditions to essentially eliminate the adduct.

The inventors found use of one or more of the following steps controlled the amount of residual monomers and adduct:

1. Avoid formation of adduct by separating the tertiary amino- containing monomer from the vinyl-functional monomer prior to polymerization. 2. Avoid contacting any mixture of tertiary amino-containing monomer and vinyl-functional monomer with water prior to polymerization. It was found that adduct formation is fast in the presence of water. However, in the absence of water, the formation of adduct is not observed at room temperature.

3. Conduct polymerization at a high temperature (about 70 to about 90°C, preferably about 80 to about 90°C) and suitable pH (about 3 to about 10, preferably about 4 to about 8, most preferably about 4 to about 6). This destabilizes the adduct formed to liberate the bound monomers from the adduct.

The liberated monomers can then copolymerize.

Preferably, acid (a reactant) is supplied to the reactor before the monomers.

Conventionally, copolymers of tertiary amino monomer with a vinyl functional monomer have a Michael addition adduct and monomer level of more than 1000 ppm. With the conditions as defined above, the present invention will be able to control the residual monomer level as desired. For example, the present invention may achieve a residual monomer level below 1000 ppm, preferably below 100 ppm, by weight of copolymer. In other words, the weight ratio of copolymer to the total of residual monomer and adduct can be 1000 : less than 1, preferably, 1000:less than 0.1.

A. Feed Tertiary Amino-containing Monomer Separately From Vinyl- functional Monomer

Fig. 1 shows a diagram of a first embodiment of a process of the present invention. Typically this process and other processes described by this specification are performed as semi-batch processes. However, batch or continuous processes are not precluded.

As shown in Fig. 1, a tertiary amino-containing monomer, water, and an acid are mixed in a reactor to form a neutralized tertiary amino-containing monomer mixture (step 10) having a pH of about 3 to about 10. The neutralized tertiary amino-containing monomer mixture, a vinyl-functional monomer, water, and an initiator are fed to the reactor (step 20). The initiator may be a single ingredient (typically sodium persulfate) or a redox system combining an oxidizing component (typically sodium persulfate) and a reducing component (typically sodium metabisulfite). Water is typically fed directly to the reactor with the vinyl-functional monomer and neutralized tertiary amino-containing monomer, and/or with other ingredients.

Generally, the neutralized tertiary amino-containing monomer mixture, a vinyl-functional monomer/water mixture, and initiator are separately fed to the reactor. Preferably, the neutralized tertiary amino-containing monomer mixture, the vinyl-functional monomer/water mixture, at least a portion of the initiator are separately, yet simultaneously, fed to the reactor to form tl e polymerization mixture. The initiator can be a single organic or inorganic compound or a redox (reduction/oxidation) system of two or more compounds. For example, United States patent no. 5,863,526, incorporated herein by reference in its entirety, discloses typical initiator systems. The polymerization mixture is maintained in the reactor at polymerization conditions including a pH of about 3 to about 10, preferably about 4 to about 8, most preferably about 4 to about 6, and a temperature of about 70 to about 90°C, preferably about 80 to about 90°C, for a time of about 1 to about 3 hours, to form a copolymer (step 22) and the copolymer product is recovered (step 24).

B. Feed Tertiary Amino-containing Monomer and Vinyl-functional

Monomer As Separate Water-free Ingredients Fig. 2 shows a second embodiment of tl e present invention. In the second embodiment, water and acid are fed first to the reactor (step 40). Then, water-free tertiary amino-containing monomer, water-free vinyl-functional monomer and initiator are separately fed to the reactor to admix with the acid and water in the reactor (step 50). In the reactor, the monomers polymerize in the presence of the initiator described above (step 52).

Generally, the water is provided with acid and initiator. The polymerization mixture is maintained at the above-described polymerization conditions to form the copolymer product (step 52). Then the copolymer product is recovered (step 54). If desired, the tertiary amino-containing monomer, the vinyl-functional monomer, and the initiator are separately, yet simultaneously fed to the reactor (step 40).

C. Feed Water-free Tertiary Amino-containing Monomer Combined With Water-free Vinyl-functional Monomer

Fig. 3 shows a third embodiment of the present invention. This is the same as the second embodiment except that the water-free monomers are mixed to form a water-free mixture prior to being fed to the reactor. It is sometimes desirable to combine streams to simplify processing. Thus, in the process, water and acid are fed first to the reactor (step 40). The tertiary amino-containing monomer and the vinyl-functional monomer stream are mixed to form a water- free monomer mixture (step 60). Then the water-free monomer mixture and initiator are separately fed to the reactor to admix with the acid and water in the reactor (step 70). In the reactor, the monomers polymerize in the presence of the initiator described above at the above-described polymerization conditions (step 72). Then the resulting polymer is recovered (step 74).

Generally, the monomer mixture, the acid, the water, and the initiator are separately fed to a polymerization reactor to form the polymerization mixture. Preferably, the water stream and acid stream are fed first to the reactor, and then, the monomer mixture, and the initiator are separately fed to the polymerization reactor to polymerize (step 72). Typically, at least a portion of the iniator is added at the same time as the monomer mixture. Additional water may be provided with the initiators or separately. II. COPOLYMER The above-described processes may be employed to make copolymers from one or more tertiary amino monomers, e.g., dimethylaminomethylmethacrylate (known as DMAEMA), together with one or more vinyl-functionalmonomers, e.g., hydroxyethylacrylate (HEA), hydroxypropylacrylate (HP A), or acrylic acid (AA). For example, one tertiary amino-containing monomer may be mixed with two vinyl-functional monomers, or two tertiary amino-containing monomers may be mixed with one vinyl- functional monomer.

The following describes non-limiting examples of polymeric material for use in the present invention.

The polymers of the present invention may be random or block polymers. For example, the polymeric suds stabilizers of the present invention may have random and or repeating units, and/or block polymers such as di-, tri- and multi- block polymers.

For example a copolymer can be made from two monomers, G and H, such that G and H are randomly distributed in the copolymer, such as

GHGGHGGGGGHHG etc. or G and H can be in repeating distributions in the copolymer, for example

GHGHGHGHGHGHGH etc. or

GGGGGHHGGGGGHH etc.

The same is true of the terpolymer, the distribution of the three monomers can be either random or repeating.

Furthermore, the resulting copolymer has a weight average molecular weight of from about 1,000 to about 2,000,000 typically from about 5,000 to about 1,000,000, more typically from about 10,000 to about 750,000, more typically from about 20,000 to about 500,000, or 35,000 to about 300,000 daltons. The molecular weight of the polymer, can be determined via conventional gel permeation chromatography or any other suitable procedure known to those of ordinary skill in the art.

Additionally, the polymers can be present as the free base or as a salt.

Typical counter ions include, acetate, citrate, maleate, sulfate, chloride, etc. The present description describes the copolymers in terms of their monomeric units. The monomeric units are the repeating units in the polymer.

The monomer reactants correspond to the monomer units in that the monomer reactants have a double bond while, in the corresponding monomeric unit, the double bond is opened to form two single bonds for linking the monomeric unit to at least one other monomeric unit.

For example, a typical vinyl-functional monomer is HEA having the structure shown in Formula III:

The monomeric unit corresponding to HEA has the structure shown in

Formula IV:

as part of a backbone of a copolymer or the structure shown in formula IVA:

when it is a monomeric unit involved in a Michael addition. A. Tertiary Amino-Containing Monomers

As stated above, polymers made by processes of the present invention include tertiary amino-containing monomeric units. Thus, the present invention provides a process which employs, as a reactant, one or more tertiary amino- containing monomers of Formula Va:

These tertiary amino-containing monomer of Formula Va correspond to tertiary amino-containing units having the Formula V:

wherein each of R , R and R are independently selected from the group consisting of hydrogen, Ci to C₆ alkyl, and mixtures thereof, preferably hydrogen, Ci to C₃ alkyl, more preferably, hydrogen or methyl. T is selected from the group consisting of substituted or unsubstituted, saturated or unsaturated, linear or branched radicals selected from the group consisting of alkyl, cycloalkyl, aryl, alkaryl, aralkyl, heterocyclic ring, silyl, nitro, halo, cyano, sulfonato, alkoxy, keto, ester, ether, carbonyl, amido, amino, glycidyl, carbanato, carbamate, carboxylic, and carboalkoxy radicals and mixtures thereof. Z is selected from the group consisting of: -(CH₂ , (CH -CH=CH)-, -(CH₂-CHOH)-, (CH₂-CHΝR⁴)-, -(CH₂-CHR⁵-O)- and mixtures thereof, preferably -(CH₂)-. R⁴ and R⁵ are selected from the group consisting of hydrogen, to C₆ alkyl and mixtures thereof, preferably hydrogen, methyl, ethyl and mixtures thereof; z is an integer selected from about 0 to about 12, preferably about 2 to about 10, more preferably about 2 to about 6. A is NR⁶R⁷ or NR⁶R⁷R⁸, wherein each of R⁶, R⁷ and R⁸, when present, are independently selected from the group consisting of H, Cι-C₈ linear or branched alkyl, alkyleneoxy having the formula:

-(R⁹O)yR¹⁰ , wherein R⁹ is C -C₄ linear or branched alkylene, and mixtures thereof; R ° is hydrogen, Cι-C₄ alkyl, and mixtures thereof; y is from 1 to about 10. Preferably, R⁶, R⁷ and R⁸, when present, are independently, hydrogen, or C to C₄ alkyl. Alternatively, NR⁶R⁷ or NR⁶R⁷R⁸ can form a heterocyclic ring containing from 4 to 7 carbon atoms, optionally containing additional hetero atoms, optionally fused to a benzene ring, and optionally substituted by Ci to C₈ hydrocarbyl, and or acetates. Examples of suitable heterocycles, both substituted and unsubstituted, are indolyl, isoindolinyl imidazolyl, imidazolinyl, piperidinyl pyrazolyl, pyrazolinyl, pyridinyl, piperazinyl, pyrrolidinyl, pyrrolidinyl, guanidino, amidino, quinidinyl, thiazolinyl, morpholine and mixtures thereof, with morpholino and piperazinyl being preferred. The units of Formula V have the proviso that at least one of A and T contains a tertiary amino moiety. A structure wherein NR⁶R⁷ or NR R R forms a nitrogen-containing ring is one example of a tertiary amino moiety.

Typical copolymers, made by processes of the present invention, are made from at least one tertiary amino-containing monomer having a Formula Via:

Each of these monomers corresponds to a tertiary amino-containing monomeric unit having a Formula VI:

wherein in both Formulas Via and NI,

R¹ is H or an alkyl having 1 to 10 carbon atoms, R² is a moiety selected from the group consisting of

wherein R is selected from the group consisting of

O O

— O — , — C — , and — c— O — a is an integer from 0 to 16, preferably 0 to 10; b is an integer from 2 to 10; c is an integer from 2 to 10; d is an integer from 1 to 100;

R⁴ and R⁵ are independently selected from the group consisting of -H and

wherein R⁸ is independently selected from the group consisting of a bond and an alkylene having 1 to 18, preferably 1 to 10, carbon atoms, and

R⁹ and R¹⁰ are independently selected from the group consisting of -H, alkyl having 1 to 10, preferably 1 to 8 carbon atoms, wherein at least one of R⁴ and R⁵ contains a tertiary amino;

R¹² and R¹³ are independently selected from the group consisting of alkyl having from 1 to 10, preferably 1 to 8 carbon atoms,

CH₂ CH₂

I I

CH₂ .CH₂ , and

NH

wherein x is an integer from 2 to 10.

Examples of the tertiary amino-containing unit of Formula NI include, but are not limited to, the following structures:

B. Vinyl-functional Monomers The present copolymers also contain at least one vinyl-functional monomeric unit. Thus, the present invention provides a process which employs, as a reactant, one or more vinyl-functional monomers. As defined in this specification, a vinyl-functional monomer is a substituted vinyl monomer which has two H atoms at its 1 position and one H atom at its 2 position. Typical vinyl- functional monomers are as shown in Formula Vila:

Vila.

This corresponds to vinyl-functional monomeric units as illustrated by Formula Nil :

(the one and two positions may be reversed).

In Formula Vila and VIII, R¹⁶ is a group that permits the monomer to undergo Michael addition. Typically R is selected from the group consisting of H, OH, ΝH₂, NR¹⁷R¹⁸, NHR¹⁹, NH-(CH₂)_m-NH₂-HCl, wherein m is an integer from 1 to 25, preferably 2 to 12, OR²⁰, alkyl, -O-C(O)-alkyl, and wherein k is an integer from 1 to 25, preferably 1 to 12.

In the substituents of Formula VII and Formula Vila, each of R¹⁷, R 18 R¹⁹, and R²⁰ are independently selected from the group consisting of alkyl, poly(oxyalkylene)-hydroxyalkyl, and hydroxyalkyl. Moreover, in the substituents of Formula VII and Formula Vila , the alkyls typically have from about one to about thirty-six carbon atoms, more typically about one to about twenty-two carbon atoms, even more typically about 1 to about 4 carbon atoms, and the oxy alkylene groups are typically independently oxyethylene, oxypropylene or oxybutylene groups.

For example, in Formula VII and Formula Vila R²⁰ is typically selected from the group consisting of:

-(CH₂)_e-OH,

wherein e is an integer from 2 to 25, preferably 2 to 5; or

-(CH₂)rCH₃

wherein f is an integer from 0 to 25, preferably 0 to 12; or

R24 - CH₂CH0-^H wherein g is an integer from 1 to 100, preferably 1 to 50, h is an integer from 1 to 100, preferably 1 to 50,

R ,23^J is -H, -CH₃ or -C₂H₅, and

R ,24 is -CH₃ or -C₂H₅; or a polyhydroxy monomeric unit of Formula VIII:

wherein n is an integer from 0 to 49, preferably 0 to 24.

In formulas VII and Vila R 1^ι9^y . is typically -(CH₂)_rOH wherein j is an integer from 1 to 25, preferably 2 to 12;

Typically, at least one vinyl-functional monomeric unit is selected from the group consisting of:

wherein n is an integer from 2 to 50, preferably 2 to 30, more preferably 2 to 27,

wherein R²⁵ is -H.

In typical copolymers made according to the present invention, the mol ratio of one or more tertiary amino monomeric unit : one or more one vinyl- functional monomeric unit range is 1 to 9:9 to 1.

The present invention is further illustrated by the following examples, provided that no observations or other statements made therein should be construed to limit the invention, unless otherwise expressly indicated in the claims appended hereto. All amounts, parts, percentages, and ratios are expressed in this specification and the claims by weight unless otherwise apparent in context. EXAMPLES

Procedure

DMAEMA copolymers were prepared from DMAEMA, acid, water, and HEA alone or with AA. The acid was either citric or sulphuric acid.

Unless otherwise indicated, the monomers, acid, water, a sodium persulfate solution and a sodium metabisulfite were added over 2.5 hours at 85°C to a reaction vessel. The molecular weight of the samples was controlled by the metabisulfite level which varied from 0% to 4.0% based on the active monomer weight. The samples were made using sulphuric or citric acid for neutralization and the active content was 25 to 50%. Typically, monomers and the two components of a redox initiator system were metered over 2.5 hours, held for 1 hour, and then extra initiator was added to further reduce residual monomer, and the resulting mixture was then held for another hour. The reaction temperature was generally about 85°C.

The residual monomer values were measured at room temperature and after heating at 80°C in a phosphate buffer (pH = 4.2) for several hours. The sample after being heated would reveal the amount of monomer that was not polymerized but bound to the polymer. The residual monomer values were measured with HPLC (high pressure liquid chromatography). The polymer concentration of the analyzed samples was 1-5 mg/ml active polymer.

In the following examples % initiator is based on weight percent of the monomers. All residual monomer values are parts per million based on active content (polymer solids). Comparative Example 1 - Adduct Formation of DMAEMA and HEA

The ^• stability of monomer feed of a sulphuric acid neutralized HEA:DMAEMA (6:1) copolymer was studied with time by HPLC. The monomer mixture was 64% active and had a pH of 5.7. after mixing at room temperature for 2 hours a chromatograph confirmed formation of an adduct of HEA and DMAEMA. This adduct was shown to dissociate into the monomers if it was heated at 80°C in a diluted solution at pH 4.2, indicating the reaction was reversible.

Example 1

Comparative Example 1 was repeated. However, when the two monomers were mixed in neat, little adduct was found over 1 day at room temperature. Comparative Example 2 and

Examples 2-4 - Results From HEA:DMAEMA Copolymers Prepared with 4

Feeds

In Comparative Example 2 DMAEMA was neutralized by adding it to acid and water and then HEA was added. Then the monomer mixture and redox initiator components, namely sodium persulfate solution and a sodium metabisulfite solution were separately but simultaneously added to the reactor over 2 D hours. The resulting mixture was held in the reactor for another 1 hour and then extra initiator was added to the reactor. The reaction temperature was

85°C. In Example 2 an attempt to reduce the complexation of HEA and

DMAEMA during polymerization HEA:DMAEMA copolymers was made with two separate monomer feeds. The DMAEMA was neutralized with acid by adding it to citric acid and water. The HEA was diluted with water. The two monomer solutions, and the two components of the initiator system, namely sodium persulfate and sodium metabisulfite solution, were added simultaneously but separately to the reactor over 2.5 hours. Then the mixture was held for 1 hour and extra initiator was added and the resulting mixture was held another hour. The reaction temperature was 85°C.

The separate feeds of Example 2 greatly reduced the total amount of non polymerized AA and HEA. The presence of AA listed in Table 1 was most likely due to the acrylic acid present in the HEA (<1%) raw material as supplied or to a small extent may be due to some hydrolysis of HEA.

A) HEA:DMAEMA (3:1)

The sample of Example 2 prepared with the four feed steams produced a similar product with respect to viscosity, appearance and pH as the sample from Comparative Example 2. The residual monomer values were as shown in TABLE 1. In the following tables, the term ND means less than 0.5 ppm. All residual monomer values are parts per million based on active content (polymer solids).

Further treatment with extra amount of initiator in the four feed method of

Example 2 was able to reduce the residual monomer to <500 ppm (when heated at 80°C for 4 hours).

In the comparative Example 2, the results showed that both AA and HEA values dramatically increased when the sample was heated. This indicates that both monomers were bound to the polymer/adduct and that the actual residual monomer values were much higher than indicated by the value as measured with the pre-heated sample.

Examples 3 and 4 repeat Example 2 but were made with different sodium metabisulfite levels in an attempt to obtain higher and lower molecular weight products. Example 3 prepared with 0.3% metabisulfite formed a gel. Example 4 prepared with twice the sodium metabisulfite (1.2%) produced a lower molecular weight sample. The results are shown in Tables 2 A and 2B.

In the Tables of the Examples in this specification under the headings "Residual monomer before further treatment : room temp (80°C/4 hrs)" and "Residual monomer after further treatment : room temp (80°C/4 hrs)", the values outside of parentheses are those in ppm based on active polymer measured at room temperature before heating and the values in parentheses are those in ppm based on active polymer of the analyzed samples after heating to 80°C for four hours.

The results of these samples were in TABLES 2 A and 2B.

¹ Synthesis Method: DMAEMA was neutralized by adding it to citric acid and water. HEA was mixed with water. The two monomer mixtures, i.e., DMAEMA (citric) and HEA, and the redox initiator components, namely sodium persulfate solution and sodium metabisulfite solution were metered separately but simultaneously over 2.5 hours. Then the combined ingredients were held for 1 hour and extra initiator was added. Then the combined ingredients were held for another hour. The Reaction Temperature was 85°C and there was 27.0% active polymer.

Comparative Example 3 and Example 5 - HEA:DMAEMA (6:1)

HEA:DMAEMA (6:1) copolymers were made with the "four-feed" procedure using sulphuric acid for neutralization. When the DMAEMA and HEA were separated the DMAEMA monomer pH increased to pH 7.0 due to the acidic nature of the HEA (pH = 3.3 in water). The pH of the finished product was maintained at about 2.2.

By separating the monomer feeds we were able to substantially reduce the free AA and HEA values. Typical results were as shown in TABLE 3.

Extra treatment with initiator was unable to significantly reduce the residual monomer to as in the HEA:DMAEMA (3:1) case as shown in TABLE 4.

Extending the addition time from 2.5 hours to 5 hours revealed no improvement in further reduction in the amount of residual monomer.

When the sample pH was adjusted with sodium hydroxide and treated with extra initiator the residual monomer was reduced to acceptable levels. This is due to a faster dissociation of the monomers from the adduct at a higher pH as shown in TABLE 5.

Examples 6-7 and Comparative Example 4 - HEA:DMAEMA (6:1) Several samples were prepared using the "four-feed" method except citric acid was used instead of sulfuric acid to neutralize the DMAEMA. The citric acid should act as a buffer and help to maintain a steady pH during the reaction. The finished product of higher pH was obtained when citric acid was used instead of sulphuric acid. Samples prepared with a DMAEMA monomer pH of 7 all formed gels and were discarded. When the DMAEMA pH was about 5 (similar to the 3:1 case) no gelling was observed. Two samples were prepared at 40% and 27% active solid and both possessed similar characteristics to that of the 6:1 copolymer made with the combined feeds. The residual monomer was lower initially after the reaction than the sulphuric acid sample. Both samples were of acceptable residual monomer after being treated with an extra amount of initiator. The results of these samples are in TABLES 6 A and 6B.

² Synthesis Method: In Examples 6 and 7 DMAEMA was neutralized by adding it to acid and water. HEA was mixed with water. Then the two monomer mixtures and the two redox initiator components were metered over 2.5 hours into a reactor and the resulting mixture was held for 1 hour. Then extra initiator was added and then the mixture was held for another hour. The reaction temperature was 85EC. The first initiator component was 2.1% Na₂S₂O₈ and the second initiator component was 1.5% Na₂S₂O₅. Comparative Example 4, used the same procedure as Example 6 except the HEA was added to neutralized DMAEMA to form a monomer mixture prior to being fed to a reactor. Examples 8-10 - Polymerization Without Sodium Metabisulfite

Copolymers were made with separate DMAEMA and HEA monomer feeds but sodium persulfate as the sole initiator. This was an attempt to reduce the number of feeds from 3 to 4, and this could be more practical for industrialization. A higher amount of sodium persulfate (6.3%) based on monomer solid was used to account for no metabisulfite use. Copolymers made were with the following compositions:

HEA:DMAEMA (3:1)

HEA:DMAEMA (6:1) HEA:DMAEMA:AA (6:1:0.33)

All runs were with citric acid neutralized DMAEMA. The 3:1 sample had a lower viscosity than the four-feed method but the other samples have a slightly higher viscosity. The residual monomer values were all comparable to that of the four-feed route and were easily chased down with extra amount of initiator. However, the finish product contains a slight yellow color than that of the previous samples with metabisulfite, and this is as expected.

The results of these samples are in TABLES 7A and 7B.

³ Synthesis Method: DMAEMA was neutralized by adding it to citric acid and water. HEA (and AA in Example 10) was mixed with water. Two monomer mixtures and persulfate initiator (6.3% Na₂S O₈) were metered separately into the reactor over 2.5 hours, and then held for 1 hour. Then extra initiator was added to reduce the residual monomer and the resulting mixture held for another hour. The reaction temperature was 85°C. In Example 10, HEA and AA were mixed to form one of the two monomer mixtures. Examples 11-14 - Samples Prepared with Citric Acid Added Upfront

Several samples were prepared with three feeds by simultaneously but separately adding the sodium persulfate, sodium metabisulfite and a monomer neat mixture (i.e., the monomers were mixed without neutralizing acid or water). Based on the study of the adduct formation, there is essentially no complexation in the absence of water. Citric acid was added upfront to the reactor to maintain the monomer pH and to prevent hydrolysis of the monomers.

The following copolymers were made: HEA:DMAEMA (3:1)

HEA:DMAEMA (6:1)

HEA:DMAEMA:AA (6:1:0.33)

This process gave the residual monomer control comparable to that of the four-feed route, and an acceptable level with extra amount of initiator was attained. The samples were of a light yellow color. The degree of color is lighter than that of those samples made without metabisulfite. The 3:1 copolymer had a lower viscosity than that obtained with the four-feed method.

The results of these samples are shown in TABLES 8 A and 8B.

⁴ Synthesis Method: Citric acid and water were added to the reactor. Neat HEA and neat DMAEMA were mixed to form a water-free monomer mixture. The monomer mixture and two initiator components were metered into the reactor over 2.5 hours, then held for 1 hour, and then extra initiator components were added to reduce residual monomer. The resulting mixture was then held for another hour. The initiator components were 1) 2.1% Na₂S₂O₈ and 2) 0.6% Na₂S₂O5. The reaction temperature was 85°C and there was 27.0%) active polymer.

⁵ Synthesis Method: Citric acid and water were added to the reactor. Neat HEA and neat DMAEMA (and neat AA in Example 14) were mixed to form a water-free monomer mixture. The monomer mixture and two initiator components were metered into the reactor over 2.5 hours, then held for 1 hour, and then extra initiator components were added. The resulting mixture was then held for another hour. The initiator components were 1) 2.1% Na₂S O₈ and 2) 1.5% Na₂S₂O₅. The reaction temperature was 85°C and there was 27.0%) active polymer.

The present invention successfully produces HEA:DMAEMA copolymers and terpolymers via three different methods and with parameters defined to control the levels of residual monomers. The process with the citric acid added upfront would be preferred simply because it has only 3 feeds and no neutralization step. Comparative Examples 5-6 - HEA:DMAEMA:MAA Samples

Samples of terpolymer were prepared with methacrylic acid, instead of acrylic acid, but showed no improvement with regards to the residual monomer levels as AA and HEA were bonding to the polymer. The results of these samples are shown in TABLES 9 A and 9B.

It should be understood that embodiments other than those specifically disclosed may come within the spirit and scope of the present invention. Thus, it is submitted that the present invention is not limited by the foregoing description. Rather the present invention is defined by the claims appended hereto.

⁶ Synthesis Method: Neutralized DMAEMA by adding it to citric acid, MAA, water, then added HEA. Metered monomer mixture and the two initiator components over 2.5 hours. Held for 1 hour and added extra initator components. Held another hour; Reaction Temperature 85EC; DMAEMA:HEA:MAA (1:3:0.33)

⁷ Synthesis Method: Neutralized DMAEMA by adding it to sulphuric acid, MAA, water, then added HEA. Metered monomer mixture and the two initiator components over 2.5 hours. Held for 1 hour and added extra initiator components. Held another hour; Reaction Temperature 85EC; DMAEMA:HEA:MAA(1 :6:0.33)

Claims

WE CLAIM:

1. A process for copolymerizing at least one tertiary amino- containing monomer and at least one vinyl-functional monomer comprising the steps of: mixing the at least one tertiary amino-containing monomer, the at least one vinyl-functional monomer, an acid, and a polymerization initiator in a polymerization reactor to form a polymerization mixture in the reactor, wherein the at least one vinyl-functional monomer has is selected from at least one member of the group consisting of a monomer of Formula Vila:

wherein R¹⁶ is a group which permits the vinyl-functional monomer to undergo Michael addition, copolymerizing the at least one tertiary amino-containing monomer and the at least one vinyl-functional monomer in tlie polymerization mixture, to form a copolymer comprising at least one corresponding tertiary amino-containing monomer and at least one corresponding vinyl-functional unit, and optionally a Michael addition adduct of the copolymer and the at least one vinyl-functional monomer, and optionally a Michael addition adduct of the at least one tertiary amino-containing monomer and the at least one vinyl-functional monomer; wherein the process comprises at least one step selected from the group consisting of: a. maintaining the at least one tertiary amino-containing monomer separate from the at least one vinyl-functional monomer prior to the copolymerizing, b. maintaining the at least one tertiary amino-containing monomer and the at least one vinyl-functional monomer water-free prior to the copolymerizing, and c. conducting the copolymerizing at about 70 to about 90°C and a pH of about 3 to about 10.

2. The process of Claim 1, wherein the copolymerizing occurs at a temperature and pH sufficient to form a composition wherein the ratio of the weight of the copolymer to total of the monomers, vinyl-functional monomeric unit bound to the copolymer by Michael addition, and Michael addition adduct of the vinyl-functional monomer and the tertiary amino-containing monomer is 1,000 parts by weight : less than about 1 part by weight.

3. The process of Claim 1, wherein the at least one tertiary amino- containing monomer, the at least one vinyl-functional monomer and the initiator are fed separately to the polymerization reactor.

4. The process of Claim 3, wherein the at least one tertiary amino- containing monomer and the at least one vinyl-functional monomer are fed separately, yet simultaneously, to the polymerization reactor.

5. The process of Claim 3, wherein the acid is fed to the reactor before the at least one tertiary amino-containing monomer and the at least one vinyl-functional monomer.

6. The process of Claim 3, wherein the acid is fed to the reactor separately, yet simultaneously with the at least one tertiary amino-containing monomer and the at least one vinyl-functional monomer.

7. The process of Claim 3, wherein the at least one tertiary amino- containing monomer is neutralized with the acid prior to feeding the at least one tertiary amino-containing monomer to the polymerization reactor.

8. The process of Claim 3, wherein the acid is combined with the at least one vinyl-functional monomer before feeding the at least one vinyl- functional monomer to the reactor.

9. The process of Claim 1, wherein the acid is fed to the reactor separately, yet simultaneously with, the at least one tertiary amino-containing monomer and the at least one vinyl-functional monomer.

10. The process of Claim 1, wherein the at least one tertiary amino- containing monomer and the at least one vinyl-functional monomer are water-free when fed to the reactor.

11. The process of Claim 10, wherein the at least one tertiary amino-containing monomer, and the at least one vinyl-functional monomer, are combined to form a water-free monomer mixture; and the monomer mixture and the initiator are fed separately, yet simultaneously, to the reactor.

12. The process of Claim 10, wherein the at least one tertiary amino-containing monomer, and the at least one vinyl-functional monomer, are combined to form a water-free monomer mixture; the monomer mixture and the polymerization initiator are separately fed to the polymerization reactor to form the polymerization mixture; and the copolymerizing occurs at a temperature and pH sufficient to form a composition wherein the weight ratio of the copolymer to the total of the monomers, vinyl functional monomeric unit bound to the copolymer by Michael addition, and the Michael addition adduct of the tertiary amine-containing monomer and the vinyl-functional monomer is 1,000 : less than about 1.

13. The process of Claim 1, wherein acid and water are fed to the reactor prior to feeding the at least one tertiary amino-containing monomer and the at least one vinyl-functional monomer to the reactor.

14. The process of Claim 1, wherein the acid comprises citric acid or a mineral acid.

15. The process of Claim 1 , wherein the at least one tertiary amino-containing monomer and the at least one vinyl-functional containing monomer are copolymerized in the reactor at about 70 to about 90°C and pH of about 3 to about 10 to form the copolymer and, optionally, the Michael addition adduct.

16. The process of Claim 15, wherein the polymerization occurs at a pH of about 4 to about 8.

17. The process of Claim 15, wherein the polymerization occurs at a pH of about 4 to about 6.

18. The process of Claim 15, wherein the polymerization occurs at a temperature of about 80 to about 90°C.

19. The process of Claim 15, further comprising neutralizing the at least one tertiary amino-containing monomer with the acid prior to feeding the at least one tertiary amino-containing monomer to the polymerization reactor.

20. The process of Claim 15, wherein the at least one tertiary amino- containing monomer, the at least one vinyl-functional monomer and the initiator are separately, yet simultaneously fed to the polymerization reactor.

21. The process of Claim 15, wherein an acid stream is fed to the polymerization reactor separately from the at least one tertiary amino-containing monomer and the at least one vinyl-functional monomer, either prior to or simultaneous with the at least one tertiary amino-containing monomer and the at least one vinyl-functional monomer.

22. The process of Claim 15, wherein the at least one tertiary amino-containing monomer and the at least one vinyl-functional monomer are combined to form a monomer mixture, the monomer mixture and the polymerization initiator are separately fed to the polymerization reactor to form the polymerization mixture.

23. The process of Claim 15, wherein the at least one tertiary amino-containing monomer, the at least one vinyl-functional monomer, and the polymerization initiator are separately fed to the polymerization reactor to form the polymerization mixture.

24. The process of Claim 1, wherein the copolymerizing occurs at a pH of about 4 to about 8.

25. The process of Claim 1, wherein the copolymerizing occurs at a pH of about 4 to about 6.

26. The process of Claim 1, wherein the copolymerizing occurs at a temperature of about 80 to about 90°C.

27. The process of Claim 1, wherein the copolymerizing occurs for about 1 to about 3 hours.

28. The process of Claim 1, wherein the acid comprises citric acid or a mineral acid.

29 The process of Claim 1, wherein the at least one tertiary amino- containing monomer is selected from at least one member of the group consisting of a monomer of Formula Na:

wherein each of R , R and R are independently selected from the group consisting of hydrogen, Ci to C₆ alkyl, and mixtures thereof,

T is selected from the group consisting of substituted or unsubstituted, saturated or unsaturated, linear or branched radicals selected from the group consisting of alkyl, cycloalkyl, aryl, alkaryl, aralkyl, heterocyclic ring, silyl, nitro, halo, cyano, sulfonato, alkoxy, keto, ester, ether, carbonyl, amido, amino, glycidyl, carbanato, carbamate, carboxylic, and carboalkoxy radicals and mixtures thereof, Z is selected from the group consisting of: -(CH₂)-, (CH -CH=CH)-, -

(CH₂-CHOH)-, (CH₂-CHNR⁴)-, -(CH₂-CHR⁵-O)- and mixtures thereof, wherein R⁴ and R⁵ are selected from the group consisting of hydrogen, Ci to C₆ alkyl and mixtures thereof; z is an integer selected from about 0 to about 12, A is NR⁶R⁷ or NR⁶R⁷R⁸, wherein each of R⁶, R⁷ and R⁸, when present, are independently selected from the group consisting of H, Cι-C₈ linear or branched alkyl, alkyleneoxy having the formula:

-(R⁹O)yR¹⁰ , wherein R⁹ is C₂-C₄ linear or branched alkylene, and mixtures thereof; R¹⁰ is hydrogen, C₁-C₄ alkyl, and mixtures thereof; and y is from 1 to about 10, or NR⁶R⁷ or NR⁶R⁷R⁸ form a heterocyclic ring containing from 4 to 7 carbon atoms, optionally containing additional hetero atoms, optionally fused to a benzene ring, and optionally substituted by Ci to C₈ hydrocarbyl, and/or acetates, wherein at least one of A and T contains a tertiary amino moiety.

30. The process of Claim 1, wherein the at least one tertiary amino- containing monomer is selected from at least one member of the group consisting of a monomer of Formula Via:

wherein R¹ is H or an alkyl having 1 to 10 carbon atoms,

9

R is a moiety selected from the group consisting of

wherein R³ is selected from the group consisting of

O O

R⁴ and R⁵ are independently selected from the group consisting of -H and

R9

/

-Rδ — N \

RlO

wherein R is independently selected from the group consisting of a bond and an alkylene having 1 to 18, and

R⁹ and R¹⁰ are independently selected from the group consisting of -H, alkyl having 1 to 10, wherein at least one of R⁴ and R contains a tertiary amino moiety; 19 1^

R and R are independently selected from the group consisting of alkyl having from 1 to 10,

CH₂ CH₂

CH₂ .CH₂ , and

NH

wherein x is an integer from 2 to 10.

31. The process of Claim 1, wherein the at least one vinyl-functional monomer is selected from at least one member of the group consisting of a monomeric unit of Formula Vila:

wherein R¹⁶ is selected from the group consisting of H, OH, NH₂,

NR¹⁷R¹⁸, NHR¹⁹, NH-(CH₂)_m-NH₂-HCl, wherein m is an integer from 1 to 25, OR²⁰, alkyl, -O-C(O)-alkyl, and

wherein k is an integer from 1 to 25, preferably 1 to 12, wherein each of R¹⁷, R¹⁸, R¹⁹, and R²⁰ are independently selected from the group consisting of alkyl, poly(oxyalkylene)-hydroxyalkyl, and hydroxyalkyl, wherein the alkyls have from about one to about thirty-six carbon atoms, and the oxyalkylene groups are independently oxyethylene, oxypropylene or oxybutylene groups.

32. The process of Claim 31, wherein the alkyls have from about one to about twenty-two carbon atoms.

33. The process of Claim 32, wherein the alkyls have from about 1 to about 4 carbon atoms.

34. The process of Claim 31 , wherein the at least one vinyl-functional monomeric unit is selected from at least one member of the group consisting of a monomeric unit of Formula Vila wherein R²⁰ is selected from the group consisting of:

-(CH₂)_e-OH, wherein e is an integer from 2 to 25;

-(CH₂)_f-CH₃ , wherein f is an integer from 0 to 25;

R23

-^CH CH₂θ^g H

R24 — CH₂CHO-^H

wherein g is an integer from 1 to 100, h is an integer from 1 to 100, R²³ is -H, -CH₃ or -C₂H₅, R²⁴ is -CH₃ or -C₂H₅; and a polyhydroxy monomeric unit of Formula VIII:

wherein n is an integer from 0 to 49; and

R¹⁹ is

-(CH₂)_j-OH, wherein j is an integer from 1 to 25.

35. The process of Claim 1, wherein the tertiary amino-containing monomer is at least one member of the group consisting of dimethylaminomethacrylate, and dimethylaminopropyl(meth)acrylamide, and the vinyl-functional monomer is selected from at least one member of the group consisting of hydroxyethylacrylate, hydroxyethylmethacrylate, hydroxypropylacrylate, hydroxypropylmethacrylate, and acrylic acid.

36. The process of Claim 1, wherein the at least one vinyl-functional containing monomer comprises a member of the group consisting of hydroxyethylacrylate, hydroxypropylacrylate, and acrylic acid.

37. The process of Claim 1, wherein the at least one tertiary amino-containing monomer, the at least one vinyl-functional monomer, and the polymerization initiator are separately fed to a polymerization reactor to form a polymerization mixture; the at least one tertiary amino-containing monomer and the at least one vinyl-functional containing monomer are copolymerized in the polymerization mixture to form the copolymer and, optionally, the Michael addition, at a temperature and pH sufficient to form a composition wherein the ratio of the weight of the copolymer to total of the monomers, vinyl-functional monomeric unit bound to the copolymer by Michael addition, and Michael addition adduct of the vinyl-functional monomer and the tertiary amino- containing monomer is 1,000,000 parts by weight : less than about 1,000 parts by weight.