MX336836B - Metodo para la fabricacion de una lamina de acero galvanizado de alta resistencia que tiene una excelente estabilidad de propiedades mecanicas, formabilidad, y aspecto del recubrimiento. - Google Patents

Metodo para la fabricacion de una lamina de acero galvanizado de alta resistencia que tiene una excelente estabilidad de propiedades mecanicas, formabilidad, y aspecto del recubrimiento.

Info

Publication number
MX336836B
MX336836B MX2013014134A MX2013014134A MX336836B MX 336836 B MX336836 B MX 336836B MX 2013014134 A MX2013014134 A MX 2013014134A MX 2013014134 A MX2013014134 A MX 2013014134A MX 336836 B MX336836 B MX 336836B
Authority
MX
Mexico
Prior art keywords
steel sheet
vol
concentration
processability
dip galvanized
Prior art date
Application number
MX2013014134A
Other languages
English (en)
Other versions
MX2013014134A (es
Inventor
Yasunobu Nagataki
Tatsuya Nakagaito
Yoshiyasu Kawasaki
Shinjiro Kaneko
Yoshitsugu Suzuki
Mai Miyata
Original Assignee
Jfe Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jfe Steel Corp filed Critical Jfe Steel Corp
Publication of MX2013014134A publication Critical patent/MX2013014134A/es
Publication of MX336836B publication Critical patent/MX336836B/es

Abstract

Se proporciona un método para la fabricación de una lámina de acero galvanizado de alta resistencia que tiene una tensión de rotura TS de 540 MPa o más y que tiene una excelente estabilidad de propiedades mecánicas, formabilidad, y aspecto del recubrimiento. Una primera etapa de calentamiento, en la cual el calentamiento a de 400 ºC a 750 °C se lleva a cabo en una atmósfera que contiene O2: 0.1 a 20 por ciento en volumen y H2O: 1 a 50 por ciento en volumen y calentamiento a de 600 °C a 850 ºC se lleva a cabo en una atmósfera que contiene O2: 0.01 a menos de 0.1 por ciento en volumen y H2O: 1 a 20 por ciento en volumen, se aplica a una lámina de acero que contiene C: 0.04% o más y 0.13% o menos, Si: 0.7% o más y 2.3% o menos, Mn: 0.8% o más y 2.0% o menos, P: 0.1% o menos, S: 0.01% o menos, Al: 0.1% o menos, y N: 0.008% o menos, con base en por ciento en masa, una segunda etapa de calentamiento, en la cual la retención de la lámina de acero se lleva a cabo en una atmósfera que contiene H2: 1 a 50 por ciento en volumen y que tiene un punto de rocío de 0 °C o inferior a de 750 ºC a 900 °C durante 15 a 600s, el enfriamiento a un intervalo de temperatura de 450 °C a 550 °C se lleva a cabo, y la retención se lleva a cabo a esa temperatura durante 10 a 200 s, se aplica, y un tratamiento de galvanizado se aplica.
MX2013014134A 2011-06-01 2012-06-01 Metodo para la fabricacion de una lamina de acero galvanizado de alta resistencia que tiene una excelente estabilidad de propiedades mecanicas, formabilidad, y aspecto del recubrimiento. MX336836B (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2011123786A JP5793971B2 (ja) 2011-06-01 2011-06-01 材質安定性、加工性およびめっき外観に優れた高強度溶融亜鉛めっき鋼板の製造方法
PCT/JP2012/064730 WO2012165661A1 (ja) 2011-06-01 2012-06-01 材質安定性、加工性およびめっき外観に優れた高強度溶融亜鉛めっき鋼板の製造方法

Publications (2)

Publication Number Publication Date
MX2013014134A MX2013014134A (es) 2014-01-23
MX336836B true MX336836B (es) 2016-02-03

Family

ID=47259501

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2013014134A MX336836B (es) 2011-06-01 2012-06-01 Metodo para la fabricacion de una lamina de acero galvanizado de alta resistencia que tiene una excelente estabilidad de propiedades mecanicas, formabilidad, y aspecto del recubrimiento.

Country Status (9)

Country Link
US (1) US9340859B2 (es)
EP (1) EP2716773B1 (es)
JP (1) JP5793971B2 (es)
KR (1) KR101585311B1 (es)
CN (1) CN103597102B (es)
CA (1) CA2835809C (es)
MX (1) MX336836B (es)
TW (1) TWI493054B (es)
WO (1) WO2012165661A1 (es)

Families Citing this family (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5978826B2 (ja) * 2012-07-23 2016-08-24 Ｊｆｅスチール株式会社 表面安定性に優れた高強度溶融亜鉛めっき鋼板の製造方法
JP5626324B2 (ja) 2012-12-11 2014-11-19 Ｊｆｅスチール株式会社 溶融亜鉛めっき鋼板の製造方法
JP6356808B2 (ja) 2013-12-10 2018-07-11 アルセロールミタル 鋼板の焼鈍方法
CN105814229B (zh) * 2013-12-13 2018-05-18 杰富意钢铁株式会社 高强度合金化热镀锌钢板的制造方法
JP6052270B2 (ja) * 2013-12-13 2016-12-27 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板およびその製造方法
KR101545856B1 (ko) 2014-01-21 2015-08-20 주식회사 성우하이텍 진동 스폿 용접장치 및 진동 스폿 용접방법
EA035895B1 (ru) * 2015-04-22 2020-08-27 Кокрий Ментенанс Эт Энженьери С.А. Способ и устройство для управления реакцией
JP6237937B2 (ja) 2016-03-11 2017-11-29 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板の製造方法
WO2017154494A1 (ja) * 2016-03-11 2017-09-14 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板の製造方法
EP3502300B1 (en) * 2016-10-25 2021-01-13 JFE Steel Corporation Method for producing high strength hot-dip galvanized steel sheet
RU2741917C1 (ru) * 2017-12-12 2021-01-29 ДжФЕ СТИЛ КОРПОРЕЙШН Многослойный лист электротехнической стали
US11560614B2 (en) 2018-03-30 2023-01-24 Jfe Steel Corporation High-strength galvanized steel sheet, high strength member, and method for manufacturing the same
US12276006B2 (en) 2020-02-21 2025-04-15 Jfe Steel Corporation Method of producing high-strength hot-dip galvanized steel sheet
CN113969336B (zh) * 2020-07-23 2023-03-28 宝山钢铁股份有限公司 一种热镀锌钢板的制造方法、钢板及车用构件
KR102451005B1 (ko) * 2020-10-23 2022-10-07 주식회사 포스코 열적 안정성이 우수한 고강도 강판 및 이의 제조방법
US20240229211A9 (en) * 2021-03-08 2024-07-11 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) Method for manufacturing hot-dip galvanized steel sheet and method for manufacturing alloyed hot-dip galvanized steel sheet
JP2022136976A (ja) * 2021-03-08 2022-09-21 株式会社神戸製鋼所 溶融亜鉛めっき鋼板の製造方法および合金化溶融亜鉛めっき鋼板の製造方法
CN114672717A (zh) * 2022-02-28 2022-06-28 日照钢铁控股集团有限公司 一种高扩孔热镀锌板的生产方法

Family Cites Families (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2787366B2 (ja) 1990-05-22 1998-08-13 新日本製鐵株式会社 溶融亜鉛めっき高張力冷延鋼板の製造方法
JP2587724B2 (ja) * 1990-11-30 1997-03-05 新日本製鐵株式会社 めっき密着性の良好な高Ｓｉ含有高張力溶融亜鉛めっき鋼板の製造方法
JP3583306B2 (ja) 1999-01-20 2004-11-04 株式会社神戸製鋼所 板幅方向における伸びのバラツキが改善された高強度高延性冷延鋼板の製造方法
JP2001140022A (ja) 1999-08-27 2001-05-22 Nippon Steel Corp プレス成形性に優れた高強度合金化溶融亜鉛めっき鋼板の製造方法
JP4956998B2 (ja) * 2005-05-30 2012-06-20 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP4221023B2 (ja) 2005-12-06 2009-02-12 株式会社神戸製鋼所 耐パウダリング性に優れた高強度合金化溶融亜鉛めっき鋼板およびその製造方法
JP4972775B2 (ja) * 2006-02-28 2012-07-11 Ｊｆｅスチール株式会社 外観性とめっき密着性に優れる高強度溶融亜鉛めっき鋼板の製造方法
JP5194811B2 (ja) * 2007-03-30 2013-05-08 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板
JP5151246B2 (ja) * 2007-05-24 2013-02-27 Ｊｆｅスチール株式会社 深絞り性と強度−延性バランスに優れた高強度冷延鋼板および高強度溶融亜鉛めっき鋼板ならびにその製造方法
JP5272547B2 (ja) * 2007-07-11 2013-08-28 Ｊｆｅスチール株式会社 降伏強度が低く、材質変動の小さい高強度溶融亜鉛めっき鋼板およびその製造方法
JP5119903B2 (ja) * 2007-12-20 2013-01-16 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板および高強度合金化溶融亜鉛めっき鋼板の製造方法
JP4894863B2 (ja) 2008-02-08 2012-03-14 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5444752B2 (ja) 2009-02-23 2014-03-19 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板の製造方法および高強度合金化溶融亜鉛めっき鋼板の製造方法
JP4998756B2 (ja) * 2009-02-25 2012-08-15 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5786316B2 (ja) 2010-01-22 2015-09-30 Ｊｆｅスチール株式会社 加工性および耐衝撃特性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5786317B2 (ja) * 2010-01-22 2015-09-30 Ｊｆｅスチール株式会社 材質安定性と加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5083354B2 (ja) * 2010-03-29 2012-11-28 Ｊｆｅスチール株式会社 化成処理性に優れた高Ｓｉ冷延鋼板の製造方法
KR101657862B1 (ko) 2012-04-17 2016-09-19 제이에프이 스틸 가부시키가이샤 도금 밀착성 및 슬라이딩 특성이 우수한 합금화 용융 아연 도금 강판의 제조 방법

Also Published As

Publication number Publication date
TW201303040A (zh) 2013-01-16
KR101585311B1 (ko) 2016-01-13
KR20140007476A (ko) 2014-01-17
CN103597102B (zh) 2016-05-04
CA2835809C (en) 2016-10-11
CN103597102A (zh) 2014-02-19
TWI493054B (zh) 2015-07-21
US20140174608A1 (en) 2014-06-26
WO2012165661A1 (ja) 2012-12-06
CA2835809A1 (en) 2012-12-06
US9340859B2 (en) 2016-05-17
EP2716773A1 (en) 2014-04-09
JP5793971B2 (ja) 2015-10-14
EP2716773A4 (en) 2015-06-03
MX2013014134A (es) 2014-01-23
EP2716773B1 (en) 2019-05-22
JP2012251192A (ja) 2012-12-20

Similar Documents

Publication Publication Date Title
MX2014000642A (es) Lamina de acero de alta resistecia para conformacion por prensado en tibio y metodo para la fabricacion de la misma.
MX336836B (es) Metodo para la fabricacion de una lamina de acero galvanizado de alta resistencia que tiene una excelente estabilidad de propiedades mecanicas, formabilidad, y aspecto del recubrimiento.
MX2013012422A (es) Lamina de acero para miembro de estampado en caliente y metodo para producir la misma.
IN2014DN11262A (es)
ZA201402969B (en) HIGH-STRENGTH HOT DIP GALVANIZED STEEL SHEET AND HIGH-STRENGTH ALLOYED HOT-DIP GALVANIZED STEEL SHEET HAVING EXCELLENT FORMABILITY AND SMALL MATERIAL ANISOTROPY WITH ULTIMATE TENSILE STRENGTH OF 980 MPa OR MORE AND MANUFACTURING METHOD THEREFOR
MX2019004000A (es) Lamina de acero recubierta de metal, metodo de fabricacion de lamina de acero galvanizada por inmersion en caliente, y metodo de fabricacion de lamina de acero galvanizada-recocida aleada.
WO2016006159A8 (ja) 合金化溶融亜鉛めっき鋼板の製造方法
MX2014007786A (es) Lamina de acero de alta resistencia enchapada por inmersion en caliente para estampacion, excelente en tenacidad a baja temperatura y resistencia a la corrosion y metodo de fabricacion de la misma.
MX2016011356A (es) Chapa de acero galvanofusionado por inmersion en caliente de alta resistencia que tiene una excelente propiedad de endurecimiento por horneado y capacidad de flexion.
MX378125B (es) Método de fabricación de hoja de acero galvanizado para estampación en caliente, hoja de acero galvanizado y recocido por inmersión en caliente para estampación en caliente y método de fabricación de las mismas, y componente estampado en caliente.
MX2018006419A (es) Metodo para la fabricacion de lamina de acero galvanizada de alta resistencia, metodo para la fabricacion de lamina de acero laminada en caliente para laminas de acero galvanizadas de alta resistencia, metodo para la fabricacion de lamina de acero laminada en frio para laminas de acero galvanizadas de alta resistencia, y lamina de acero galvanizada de alta resistencia.
PT2240622E (pt) Processo para a preparação de uma peça feita de um produto de aço revestido com al-si e o produto intermediário deste processo
CA2709509A1 (en) Methods for manufacturing high strength hot-dip galvanized steel sheet and high strength hot-dip galvannealed steel sheet
CA2648429A1 (en) Method of production of hot dip galvannealed steel sheet with excellent workability, powderability, and slidability
MX2014002021A (es) Lamina de acero laminada en caliente para lamina de acero laminada en frio, lamina de acero laminada en caliente para lamina de acero galvanizada, y metodo para la fabricacion de las mismas.
GB201214327D0 (en) High strength steel sheet excellent in seam weldability
MX2015013368A (es) Hoja de acero revestida con aleacion de zinc por inmersion en caliente excelente en adherencia de revestimiento, y metodo para producir la misma.
WO2016110910A8 (ja) 合金化溶融亜鉛めっき鋼板の製造方法
MX2016017399A (es) Metodo para producir una hoja de acero recubierta de alta resistencia con una resistencia, ductilidad y capacidad de formacion mejoradas.
WO2014186689A3 (en) High strength steel exhibiting good ductility and method of production via in-line heat treatment downstream of molten zinc bath
UA118699C2 (uk) Спосіб отримання високоміцного сталевого листа з покриттям, що має покращену міцність і пластичність, та отриманий лист
MX350227B (es) Lamina de acero galvanizada por inmersion en caliente de alta resistencia con excelente estirabilidad profunda y susceptibilidad a rebordeado por extendido, y proceso para producir la msima.
MX2015001690A (es) Lamina de acero electrico de alta resistencia y metodo para la produccion de la misma.
MX2019004791A (es) Metodo para la fabricacion de lamina de acero galvanizada de alta resistencia.
GB201218559D0 (en) Hot dipped galvanized steel sheet and alloyed hot-dip galvanised steel sheet, each having excellent processability, high yield ratio and high strength

Legal Events

Date Code Title Description
FG Grant or registration