Palmatier, 2005 - Google Patents
Ultrasonic impact treatment of traffic signal mast arm weldsPalmatier, 2005
View PDF- Document ID
- 381392566484777981
- Author
- Palmatier A
- Publication year
- Publication venue
- Masters of Science in Engineering Thesis, The University of Texas at Austin
External Links
Snippet
UIT should be applied so that it creates a groove with a width that indents approximately half upon the weld metal and half upon the base metal heat affected zone (HAZ). When the groove width is not applied evenly, the width should cover more of the base metal HAZ than …
- 210000003371 Toes 0 abstract description 222
Classifications
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/0058—Kind of property studied
- G01N2203/006—Crack, flaws, fracture or rupture
- G01N2203/0062—Crack or flaws
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K9/00—Arc welding or cutting
- B23K9/04—Welding for other purposes than joining, e.g. built-up welding
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Tsutsumi et al. | Effects of weld geometry and HAZ property on low-cycle fatigue behavior of welded joint | |
| US6338765B1 (en) | Ultrasonic impact methods for treatment of welded structures | |
| Pandey et al. | On the prediction of effect of direction of welding on bead geometry and residual deformation of double-sided fillet welds | |
| Kirkhope et al. | Weld detail fatigue life improvement techniques. Part 2: application to ship structures | |
| Aung et al. | Fatigue-performance improvement of patch-plate welding via PWHT with induction heating | |
| Chen et al. | Experimental investigation and predictive model on tensile behavior of corroded high-strength steel and butt-welded connections | |
| US20050230010A1 (en) | Treatment method for improving fatigue life and long-life metal material treated by using same treatment | |
| Roy et al. | Enhancing fatigue strength by ultrasonic impact treatment | |
| Feng et al. | Fatigue performance of rib-to-deck joints in orthotropic steel deck with PWHT | |
| Gu et al. | Effect of multi-dimensional ultrasonic-assisted pulsed-laser surface irradiation on residual stress in AISI 1045 steel | |
| Kanishka et al. | High-cycle fatigue and wear performance of low-carbon steel plates remanufactured with wire arc additive manufacturing | |
| Rusk et al. | Fatigue life prediction of corrosion-damaged high-strength steel using an equivalent stress riser (ESR) model: Part I: Test development and results | |
| Madi et al. | Low cycle fatigue of welded joints: new experimental approach | |
| Palmatier | Ultrasonic impact treatment of traffic signal mast arm welds | |
| Boroński | Testing low-cycle material properties with micro-specimens | |
| Gerster et al. | Pneumatic impact treatment (pit)–application and quality assurance | |
| Knysh et al. | Influence of the atmosphere corrosion on the fatigue life of welded T-joints treated by high frequency mechanical impact | |
| Lihavainen | A novel approachfor assessing the fatigue strength of ultrasonic impact treated welded structures. | |
| Li et al. | Fatigue Life Prediction of Prefatigued Welded Q235 Steel Butt-Joints Treated by High Frequency Mechanical Impact | |
| Devaney | Process-structure-property characterisation of plasticity and fatigue damage in X100 welded joints for steel catenary risers | |
| Ryabtsev et al. | Fatigue life of steel 40Kh specimens after wear-resistant surfacing with a sublayer of low-carbon steel | |
| Zeng et al. | Low-cycle fatigue of laser-arc hybrid welded S960 high-strength steel joints | |
| Akhlaghi | Welding simulation and fatigue assessment of tubular K-joints in high-strength steel | |
| Tang et al. | Numerical simulation of residual stresses in welding and ultrasonic impact treatment process | |
| Hui | Fatigue life improvement of welded girders with ultrasonic impact treatment |