Crack propagation in NiCoCrAl/YSZ multilayer film produced by EB-PVD in crack arrester orientationShi et al., 2019
View PDF- Document ID
- 293856281717171202
- Author
- Shi G
- Wang H
- Wu Z
- Wang J
- Publication year
- Publication venue
- IOP Conference Series: Materials Science and Engineering
External Links
Snippet
A multilayer film containing 10 NiCoCrAl layers with thickness of about 35 μm and 9 ZrO2– Y2O3 (YSZ) layers with thickness of about 1 μm was fabricated by electron beam physical vapor deposition (EB-PVD). Considering the difficulty to machine a surface notch in the thin …
- 229910001233 yttria-stabilized zirconia 0 title abstract description 51
Classifications
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C14/00—Coating by vacuum evaporation, by sputtering or by ion implantation of the coating forming material
- C23C14/06—Coating by vacuum evaporation, by sputtering or by ion implantation of the coating forming material characterised by the coating material
- C23C14/08—Oxides
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C14/00—Coating by vacuum evaporation, by sputtering or by ion implantation of the coating forming material
- C23C14/22—Coating by vacuum evaporation, by sputtering or by ion implantation of the coating forming material characterised by the process of coating
- C23C14/24—Vacuum evaporation
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Jiang et al. | Comparative study on the tensile cracking behavior of CrN and Cr coatings for accident-tolerant fuel claddings | |
| Zhang et al. | Ablation behavior of HfC coating with different thickness for carbon/carbon composites at ultra-high temperature | |
| Zhu et al. | Determination of interfacial adhesion energies of thermal barrier coatings by compression test combined with a cohesive zone finite element model | |
| Zhang et al. | Effects of residual stress on the mechanical properties of plasma-sprayed thermal barrier coatings | |
| Chang et al. | Mechanical properties and high temperature oxidation of CrAlSiN/TiVN hard coatings synthesized by cathodic arc evaporation | |
| US6489036B1 (en) | Ceramic/metal laminate for thermal shock involving applications | |
| CN110031330B (en) | Test sample for bonding strength of ceramic coating, preparation method and test method | |
| Lohmiller et al. | Microstructure–property relationship in highly ductile Au–Cu thin films for flexible electronics | |
| Jawad et al. | Effect of layer architecture on the mechanical behavior of accumulative roll bonded interstitial free steel/aluminum composites | |
| Arai et al. | Mixed-mode interfacial fracture toughness for thermal barrier coating | |
| Bobzin et al. | Analysis of CrN/AlN/Al2O3 and two industrially used coatings deposited on die casting cores after application in an aluminum die casting machine | |
| Deambrosis et al. | Ti1− xAlxN coatings by Reactive High Power Impulse Magnetron Sputtering: Film/substrate interface effect on residual stress and high temperature oxidation | |
| Ma et al. | Study on gradient structure and interface mechanical properties of n–8YSZ/AlCoCrFeNi high–entropy coatings | |
| Bermejo et al. | High-temperature mechanical behaviour of flaw tolerant alumina–zirconia multilayered ceramics | |
| Tsipas et al. | Effect of substrate temperature on the microstructure and properties of thick plasma-sprayed YSZ TBCs | |
| Kong et al. | Comparison of ablation performances and sublayer interaction of CVD-(TaC/SiC) 3 alternate coatings with different crystallite morphologies | |
| Bechtolsheim et al. | Interface structure and formation between gold and trimethylcyclohexane polycarbonate | |
| Choules et al. | Thermal fracture of thermal barrier coatings in a high heat flux environment | |
| Shi et al. | Crack propagation in NiCoCrAl/YSZ multilayer film produced by EB-PVD in crack arrester orientation | |
| Baragetti et al. | Fatigue resistance of CrN thin films deposited by arc evaporation process on H11 tool steel and 2205 duplex stainless steel | |
| Konieczny | Relations between microstructure and mechanical properties in laminated Ti-intermetallic composites synthesized using Ti and Al foils | |
| Shaw et al. | Bridging Processes in Metal-Reinforced Ceramics | |
| Czupryński | Selected properties of thermally sprayed oxide ceramic coatings | |
| Vande Put et al. | Characterization of TBC systems with NiPtAl or NiCoCrAlYTa bond coatings after thermal cycling at 1100 C: a comparative study of failure mechanisms | |
| Kuba et al. | Effect of thermal barrier coating layer on HIP treated IN738LC fatigue characteristic |