Wright, 2016 - Google Patents
Layered Double Hydroxides as PVC thermal stabilisers: The effect of particle size and concentrationWright, 2016
View PDF- Document ID
- 240163257941034432
- Author
- Wright H
- Publication year
- Publication venue
- PQDT-Global
External Links
Snippet
Layered double hydroxides have shown promise as PVC thermal stabilisers, however how the properties of these clays effect their stabilising abilities is not fully understood. The purpose of this research was to help understand the relationship between the LDH clays …
- 229920000915 polyvinyl chloride 0 title abstract description 380
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—USE OF INORGANIC OR NON-MACROMOLECULAR ORGANIC SUBSTANCES AS COMPOUNDING INGREDIENTS
- C08K3/00—Use of inorganic ingredients
- C08K3/18—Oxygen-containing compounds, e.g. metal carbonyls
- C08K3/20—Oxides; Hydroxides
- C08K3/22—Oxides; Hydroxides of metals
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—USE OF INORGANIC OR NON-MACROMOLECULAR ORGANIC SUBSTANCES AS COMPOUNDING INGREDIENTS
- C08K3/00—Use of inorganic ingredients
- C08K3/18—Oxygen-containing compounds, e.g. metal carbonyls
- C08K3/24—Acids; Salts thereof
- C08K3/26—Carbonates; Bicarbonates
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2002/00—Crystal-structural characteristics
- C01P2002/20—Two-dimensional structures
- C01P2002/22—Two-dimensional structures layered hydroxide-type, e.g. of the hydrotalcite-type
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—USE OF INORGANIC OR NON-MACROMOLECULAR ORGANIC SUBSTANCES AS COMPOUNDING INGREDIENTS
- C08K3/00—Use of inorganic ingredients
- C08K3/0008—Inorganic ingredients according to more than one of the "one dot" groups of C08K3/02 - C08K3/40
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01F—COMPOUNDS OF THE METALS BERYLLIUM, MAGNESIUM, ALUMINIUM, CALCIUM, STRONTIUM, BARIUM, RADIUM, THORIUM, OR OF THE RARE-EARTH METALS
- C01F7/00—Compounds of aluminium
- C01F7/002—Compounds containing, besides aluminium, two or more other elements, with the exception of oxygen and hydrogen
- C01F7/004—Compounds containing, besides aluminium, two or more other elements, with the exception of oxygen and hydrogen containing carbonate ions, e.g. dawsonite
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/60—Particles characterised by their size
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—USE OF INORGANIC OR NON-MACROMOLECULAR ORGANIC SUBSTANCES AS COMPOUNDING INGREDIENTS
- C08K3/00—Use of inorganic ingredients
- C08K3/32—Phosphorus-containing compounds
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—USE OF INORGANIC OR NON-MACROMOLECULAR ORGANIC SUBSTANCES AS COMPOUNDING INGREDIENTS
- C08K5/00—Use of organic ingredients
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2002/00—Crystal-structural characteristics
- C01P2002/80—Crystal-structural characteristics defined by measured data other than those specified in group C01P2002/70
- C01P2002/88—Crystal-structural characteristics defined by measured data other than those specified in group C01P2002/70 by thermal analysis data, e.g. TGA, DTA, DSC
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2006/00—Physical properties of inorganic compounds
- C01P2006/12—Surface area
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—USE OF INORGANIC OR NON-MACROMOLECULAR ORGANIC SUBSTANCES AS COMPOUNDING INGREDIENTS
- C08K9/00—Use of pretreated ingredients
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; MISCELLANEOUS COMPOSITIONS; MISCELLANEOUS APPLICATIONS OF MATERIALS
- C09C—TREATMENT OF INORGANIC MATERIALS, OTHER THAN FIBROUS FILLERS, TO ENHANCE THEIR PIGMENTING OR FILLING PROPERTIES; PREPARATION OF CARBON BLACK; PREPARATION OF INORGANIC MATERIALS WHICH ARE NO SINGLE CHEMICAL COMPOUNDS AND WHICH ARE MAINLY USED AS PIGMENTS OR FILLERS
- C09C1/00—Treatment of specific inorganic materials other than fibrous fillers; Preparation of carbon black
- C09C1/40—Compounds of aluminium
- C09C1/42—Clays
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—USE OF INORGANIC OR NON-MACROMOLECULAR ORGANIC SUBSTANCES AS COMPOUNDING INGREDIENTS
- C08K2201/00—Specific properties of additives
- C08K2201/002—Physical properties
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01F—COMPOUNDS OF THE METALS BERYLLIUM, MAGNESIUM, ALUMINIUM, CALCIUM, STRONTIUM, BARIUM, RADIUM, THORIUM, OR OF THE RARE-EARTH METALS
- C01F5/00—Compounds of magnesium
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
- C01G9/00—Compounds of zinc
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| US5356567A (en) | Lithium aluminum complex hydroxide salt stabilizer for resins | |
| JP2004225052A (en) | Thermal-degradation inhibitor | |
| KR101040942B1 (en) | Hydrotalcite for synthetic resin stabilizer and synthetic resin composition comprising same | |
| JP5370682B2 (en) | Zn-Mg-Al hydrotalcite-type particle powder and resin composition containing the Zn-Mg-Al hydrotalcite-type particle powder | |
| KR100202750B1 (en) | Method for producing composite metal hydroxide and composite metal hydroxide obtained thereby and flame retardant polymer composition using same | |
| EP1690832B1 (en) | Resin composition containing calcium hydroxide and article formed therefrom | |
| US20080145296A1 (en) | Mg-Al-based hydrotalcite-type particles, chlorine-containing resin composition and process for producing the particles | |
| EP1088853B1 (en) | Mg-Al-based hydrotalcite-type particles, chlorine-containing resin stabilizer and process for producing the particles | |
| US5419883A (en) | Lithium aluminum complex hydroxide salt and process for preparation thereof | |
| JPWO2016031803A1 (en) | Novel magnesium hydroxide-based solid solution, resin composition containing the same, and precursor of highly active magnesium oxide | |
| AU669867B2 (en) | Stabilized vinyl halide compositions containing hydrotalcites | |
| Wright | Layered Double Hydroxides as PVC thermal stabilisers: The effect of particle size and concentration | |
| US7041265B2 (en) | Alkaline earth metal-basic silicate particle | |
| CN116848065A (en) | Zinc hydrotalcite | |
| US6803401B2 (en) | Halogen scavenger for olefin formulations | |
| JP4106508B2 (en) | Chlorine-containing resin composition | |
| JP4427084B2 (en) | Stabilized halogen-containing resin composition | |
| JP2002053722A (en) | Chlorine-containing resin composition | |
| AU707027B2 (en) | Halogen scavenger for polymers and copolymers | |
| Royeppen | Modified layered double hydroxides as PVC heat stabilisers | |
| KR100486669B1 (en) | Method of synthesizing hydrotalcites | |
| JP2001525312A (en) | Cationic layered compound and its production method and use | |
| NL1009934C2 (en) | Anionic clays, anionic clays containing stabilizers, method of stabilizing polymer compositions. | |
| CN100448776C (en) | Calcium hydroxide, resin composition and shaped article containing it | |
| NL1025641C1 (en) | Hydrotalcite particles for stabilizing polymers have a defined particle size, soluble salt content and surface area |