Wen et al., 2006 - Google Patents

Synthesis of yttria nanopowders for transparent yttria ceramics

Wen et al., 2006

View PDF
Document ID
16837550232916262484
Author
Wen L
Sun X
Lu Q
Xu G
Hu X
Publication year
Publication venue
Optical materials

External Links

Snippet

This paper describes a precipitation process for synthesizing nanocrystalline yttria powder and sintering transparent yttria ceramics. Hydroxide precursor of Y2O3 with an approximate composition of Y2 (OH) 5NO3· H2O was synthesized by using ammonia water as precipitant …
Continue reading at lib.fibopt.ru (PDF) (other versions)

Classifications

    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3231—Refractory metal oxides, their mixed metal oxides, or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
    • C04B2235/54—Particle size related information
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
    • C04B35/628—Coating the powders or the macroscopic reinforcing agents
    • C04B35/62802—Powder coating materials
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2002/00—Crystal-structural characteristics
    • C01P2002/70—Crystal-structural characteristics defined by measured X-ray, neutron or electron diffraction data
    • C01P2002/72—Crystal-structural characteristics defined by measured X-ray, neutron or electron diffraction data by d-values or two theta-values, e.g. as X-ray diagram
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/60—Particles characterised by their size
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/65—Aspects relating to heat treatments of ceramic bodies such as green ceramics or pre-sintered ceramics, e.g. burning, sintering or melting processes
    • C04B2235/656—Aspects relating to heat treatments of ceramic bodies such as green ceramics or pre-sintered ceramics, e.g. burning, sintering or melting processes characterised by specific heating conditions during heat treatment
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2006/00—Physical properties of inorganic compounds
    • C01P2006/12—Surface area
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
    • C01G25/00—Compounds of zirconium
    • C01G25/02—Oxides

Similar Documents

Publication Publication Date Title
Wen et al. Synthesis of yttria nanopowders for transparent yttria ceramics
Wen et al. Synthesis of nanocrystalline yttria powder and fabrication of transparent YAG ceramics
Li et al. Co-precipitation synthesis route to yttrium aluminum garnet (YAG) transparent ceramics
Huang et al. Precipitation synthesis and sintering of yttria nanopowders
Li et al. Characterization and sintering of nanocrystalline CeO2 powders synthesized by a mimic alkoxide method
Li et al. Synthesis of Nd3+ doped nano-crystalline yttrium aluminum garnet (YAG) powders leading to transparent ceramic
Hajizadeh-Oghaz et al. Synthesis and characterization of Y2O3 nanoparticles by sol–gel process for transparent ceramics applications
Tachiwaki et al. Novel synthesis of Y3Al5O12 (YAG) leading to transparent ceramics
US6841497B1 (en) Method of producing aluminum oxides and products obtained on the basis thereof
Wang et al. Low‐temperature synthesis of praseodymium‐doped ceria nanopowders
Li et al. A homogeneous co-precipitation method to synthesize highly sinterability YAG powders for transparent ceramics
Sun et al. Synthesis of Nanocrystalline α‐Al2O3 Powders from Nanometric Ammonium Aluminum Carbonate Hydroxide
Li et al. Synthesis of yttria nano-powders by the precipitation method: the influence of ammonium hydrogen carbonate to metal ions molar ratio and ammonium sulfate addition
Ru et al. Synthesis of yttrium aluminum garnet (YAG) powder by homogeneous precipitation combined with supercritical carbon dioxide or ethanol fluid drying
Liu et al. Fabrication and characterizations of 8.7 mol% Y2O3-ZrO2 transparent ceramics using co-precipitated nanopowders
Huang et al. Fabrication of Y2O3 transparent ceramics by hot isostatic pressing from precipitated nanopowders
Liu et al. Synthesis of Nd: YAG powders leading to transparent ceramics: the effect of MgO dopant
Vasudevan et al. Effect of microwave sintering on the structural and densification behavior of sol–gel derived zirconia toughened alumina (ZTA) nanocomposites
Wang et al. The effect of precipitant concentration on the formation procedure of yttrium aluminum garnet (YAG) phase
Wang et al. Microwave synthesis of homogeneous YAG nanopowder leading to a transparent ceramic
Liu et al. Influence of pH values on (Nd+ Y): Al molar ratio of Nd: YAG nanopowders and preparation of transparent ceramics
Chen et al. Synthesis of highly sinterable YAG nanopowders by a modified co-precipitation method
Lv et al. Synthesis of nano-sized and highly sinterable Nd: YAG powders by the urea homogeneous precipitation method
Cai et al. Homogeneous (Lu1− xInx) 2O3 (x= 0− 1) solid solutions: Controlled synthesis, structure features and optical properties
Ma et al. Fabrication of Lu2O3: Eu transparent ceramics using powder consisting of mono-dispersed spheres