Smart behaviour of CNT modified adhesive films for carbon fiber composite repairUreña et al., 2017
View PDF- Document ID
- 16427699892337108567
- Author
- Ureña A
- García-Nieto C
- Sánchez-Romate X
- Rams J
- Sánchez M
- Publication year
- Publication venue
- Conf Smart Struct Mater, SMART Int Conf Smart Mater Nanotechnol in Eng, SMN
External Links
Snippet
Epoxy adhesives films were doped by spraying an aqueous dispersion of carbon nanotubes. Sensing capability of carbon fiber reinforced composite coupons with bonded patch repairs was evaluated; several single lap shear and Mode-I fracture energy tests were …
- 239000002131 composite material 0 title abstract description 23
Classifications
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/02—Details not specific for a particular testing method
- G01N2203/026—Specifications of the specimen
- G01N2203/0262—Shape of the specimen
- G01N2203/0278—Thin specimens
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N29/00—Investigating or analysing materials by the use of ultrasonic, sonic or infrasonic waves; Visualisation of the interior of objects by transmitting ultrasonic or sonic waves through the object
- G01N29/22—Details, e.g. general constructional or apparatus details
- G01N29/24—Probes
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/0014—Type of force applied
- G01N2203/0016—Tensile or compressive
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N3/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N3/08—Investigating strength properties of solid materials by application of mechanical stress by applying steady tensile or compressive forces
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Boztepe et al. | Novel carbon nanotube interlaminar film sensors for carbon fiber composites under uniaxial fatigue loading | |
| Mortell et al. | In-situ SEM study of transverse cracking and delamination in laminated composite materials | |
| Ladani et al. | Enhancing fatigue resistance and damage characterisation in adhesively-bonded composite joints by carbon nanofibres | |
| Caminero et al. | Analysis of adhesively bonded repairs in composites: Damage detection and prognosis | |
| Jiao et al. | A comparative study on fatigue behaviour of steel beams retrofitted with welding, pultruded CFRP plates and wet layup CFRP sheets | |
| Adams et al. | A review of defect types and nondestructive testing techniques for composites and bonded joints | |
| Sam-Daliri et al. | Impedance analysis for condition monitoring of single lap CNT-epoxy adhesive joint | |
| Camanho et al. | Failure mechanisms in bolted CFRP | |
| Feng et al. | Focusing on in-service repair to composite laminates of different thicknesses via scarf-repaired method | |
| Martin | Composite Laminate | |
| de Freitas et al. | Test method to assess interface adhesion in composite bonding | |
| Ahmed et al. | Integration of carbon nanotube sensing skins and carbon fiber composites for monitoring and structural repair of fatigue cracked metal structures | |
| Sánchez-Romate et al. | Structural health monitoring of a CFRP structural bonded repair by using a carbon nanotube modified adhesive film | |
| Sánchez-Romate et al. | Fatigue crack growth identification in bonded joints by using carbon nanotube doped adhesive films | |
| Chester et al. | Adhesively bonded repairs to primary aircraft structure | |
| Khashaba | Static and fatigue analysis of bolted/bonded joints modified with CNTs in CFRP composites under hot, cold and room temperatures | |
| Wan et al. | On-line tensile damage monitoring of WGF/epoxy T-joint by the embedded MWCNT@ WGF sensor | |
| Prabhu et al. | Uniaxial tensile failure of multi-core asymmetric sandwich composite structures with bonded repair | |
| Pierce et al. | Injection repair of composites for automotive and aerospace applications | |
| Pérez et al. | Comparative experimental analysis of the effect caused by artificial and real induced damage in composite laminates | |
| Wang et al. | Strain monitoring using carbon nanotube Buckypaper sensor on composite repaired structure | |
| Sam-Daliri et al. | Condition monitoring of crack extension in the reinforced adhesive joint by carbon nanotubes | |
| Boursier et al. | Failure initiation and effect of defects in structural discontinuous fiber composites | |
| Fikry et al. | Effect of matrix cracking on mechanical properties in FRP angle-ply laminates | |
| Ureña et al. | Smart behaviour of CNT modified adhesive films for carbon fiber composite repair |