Dillon et al., 1990 - Google Patents
Stress-assisted Corrosion in BoilersDillon et al., 1990
- Document ID
- 1474445942847517468
- Author
- Dillon J
- Port R
- Publication year
- Publication venue
- CORROSION 1990
External Links
Snippet
The mechanism of stress-assisted corrosion in boiler waterside environments is discussed. Case histories are presented to illustrate this mechanism. These case histories describe corrosion associated with stresses imparted by original tube forming or bending operations …
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Ali et al. | Corrosion-related failures in heat exchangers | |
| Gong et al. | Failure analysis on premature fracture of anchor bolts in seawater booster pump of nuclear power plant | |
| Hales et al. | Boiler feedwater pipe failure by flow-assisted chelant corrosion | |
| Dai et al. | Effect of postweld heat treatment on the sulfide stress cracking of dissimilar welds of nickel-based alloy 625 on steels | |
| Port | Identification of corrosion damage in boilers | |
| Dillon et al. | Stress-assisted Corrosion in Boilers | |
| Wang et al. | Failure analysis of cracking in the thin-walled pressure vessel of electric water heater | |
| Khalifeh | Stress Corrosion Cracking | |
| Esmacher | Stress-enhanced corrosion of boiler tubing | |
| Franco | Failures of heat exchangers | |
| King | Failures of pressure vessels | |
| Bakic et al. | Oxidation behavior during prolonged service of boiler tubes made of 2.25 Cr1Mo and 12Cr1Mo0. 3V heat resistance steels | |
| Otegui | Mechanisms of Damage and Failure | |
| Lee et al. | A Recent Failure Case Studies on Duplex Stainless Steels in Refinery (A Study on Damage Mechanism Analysis and Inspection Method) | |
| Zilberstein et al. | Evaluation of materials performance in a supercritical wet oxidation system | |
| Toppo et al. | Studies on the Influence of Sodium Hydroxide Concentration on the Stress Corrosion Cracking Behavior of Modified 9Cr-1Mo (P91) Steel Weldment | |
| Nelson | Prevention of Localized Corrosion in Sulfuric Acid Handling Equipment | |
| Djukic et al. | Contribution to the methodology of hydrogen damages analysis of boiler water wall tube and condition of their appearance | |
| A Celovsky et al. | S08: investigation and repair of a cracked feeder at Point Lepreau GS | |
| Elayaperumal | Analysis of failures of metallic materials due to environmental factors | |
| Sarrat et al. | DetaClad™ Characterization for High-Temperature and High-Pressure Hydrogen Service | |
| Bulloch | Deaerator feedwater vessel weld cracking monitored over a service time of around 80,000 hours | |
| Parkins | Prevention and control of stress corrosion cracking-An overview | |
| Pantazopoulos et al. | Progressive failures of components in chemical process industry: Case history investigation and root-cause analysis | |
| Gonzalez-Velazquez | Deterioration and Damage Mechanisms in Mechanical Components |