Tegehall et al., 2015 - Google Patents

Impact of laminate cracks under solder pads on the fatigue lives of ball grid array solder joints

Tegehall et al., 2015

View PDF
Document ID
14000854691578301603
Author
Tegehall P
Wetter G
Publication year
Publication venue
Microelectronics Reliability

External Links

Snippet

This paper reports how the solder joint fatigue lives of three types of lead free plastic BGA components were affected by cracks formed in the printed PCB laminate during a thermal cycling test. The investigation showed that cracks were formed in the laminate for all three …
Continue reading at www.diva-portal.org (PDF) (other versions)

Classifications

    • H—ELECTRICITY
    • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K1/00—Printed circuits
    • H05K1/02—Details
    • H05K1/03—Use of materials for the substrate
    • H—ELECTRICITY
    • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K1/00—Printed circuits
    • H05K1/02—Details
    • H05K1/0266—Marks, test patterns, inspection means or identification means
    • H—ELECTRICITY
    • H01—BASIC ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES; ELECTRIC SOLID STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H01L2924/00—Indexing scheme for arrangements or methods for connecting or disconnecting semiconductor or solid-state bodies as covered by H01L24/00
    • H01L2924/0001—Technical content checked by a classifier
    • H01L2924/0002—Not covered by any one of groups H01L24/00, H01L24/00 and H01L2224/00
    • H—ELECTRICITY
    • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K2201/00—Indexing scheme relating to printed circuits covered by H05K1/00
    • H05K2201/03—Conductive materials
    • H—ELECTRICITY
    • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K3/00—Apparatus or processes for manufacturing printed circuits
    • H05K3/22—Secondary treatment of printed circuits
    • H—ELECTRICITY
    • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K2203/00—Indexing scheme relating to apparatus or processes for manufacturing printed circuits covered by H05K3/00
    • H05K2203/17—Post-manufacturing processes
    • H05K2203/176—Removing, replacing or disconnecting component; Easily removable component
    • H—ELECTRICITY
    • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K2203/00—Indexing scheme relating to apparatus or processes for manufacturing printed circuits covered by H05K3/00
    • H05K2203/16—Inspection; Monitoring; Aligning
    • H05K2203/162—Testing a finished product, e.g. heat cycle testing of solder joints

Similar Documents

Publication Publication Date Title
Tegehall et al. Impact of laminate cracks under solder pads on the fatigue lives of ball grid array solder joints
US6888360B1 (en) Surface mount technology evaluation board having varied board pad characteristics
Kim et al. Improved drop reliability performance with lead free solders of low Ag content and their failure modes
Juarez Jr et al. Manufacturability and reliability screening of lower melting point, Pb-free alloys containing bismuth
Meilunas et al. Reliability and failure analysis of lead-free solder joints
Raj et al. Comparative study on impact of various low creep doped lead free solder alloys
Ribas et al. Low temperature soldering: Thermal cycling reliability performance
Henshall et al. Comparison of thermal fatigue performance of SAC105 (Sn-1.0 Ag-0.5 Cu), Sn-3.5 Ag, and SAC305 (Sn-3.0 Ag-0.5 Cu) BGA components with SAC305 solder paste
Lövberg et al. On the formation and propagation of laminate cracks and their influence on the fatigue lives of solder joints
Li Failure analysis on bad wetting of ENIG surface finish pads
Romdhane et al. Evaluation of SAC solder joint thermomechanical fatigue in different types of components
Bakhshi et al. Effects of voiding on the degradation of microvias in high density interconnect printed circuit boards under thermomechanical stresses
Tegehall Impact of various combinations of PCB laminate, solder pad finish and solder composition on the fatigue life of solder joints to various types of components
Wickham et al. Effect of voiding on lead-free reliability.
Nousiainen et al. Failure mechanisms of thermomechanically loaded SnAgCu/plastic core solder ball composite joints in low-temperature co-fired ceramic/printed wiring board assemblies
Ghaffarian Reliability of PWB microvias for high density package assembly
Froš et al. Effects of thermal cycling and PCB substrate type on reliability of solder joints
Nousiainen et al. Thermal fatigue endurance of collapsible 95.5 Sn4Ag0. 5Cu spheres in LTCC/PWB assemblies
Tegehall Impact of thermal cycling profile on cracking of PCB laminate and on the fatigue life of solder joints to various types of components
Tegehall Impact of the choice of solder composition, PCB laminate, PCB stack-up and surface finish on PCB on fatigue life of solder joints
Wang et al. High drop performance interconnection: polymer cored solder ball
Akkara Thermal Cycling Reliability of Doped SnAgCu Solder Alloys after Long-Term Aging
Lea et al. Blowholing in PTH Solder Fillets: Part 1 Assessment of the Problem
Li An analysis case on the crack failure of CBGA solder joints
Liu et al. Reliability of high Tg copper clad laminate for lead-free assembly