Fazeli et al., 2024 - Google Patents

Chemical control of water and its effect on flow-accelerated corrosion (FAC) in combined cycle power plants

Fazeli et al., 2024

View PDF
Document ID
7168009856513503876
Author
Fazeli S
Zamani Jashnabad A
Sajjadnejad M
Haghshenas S
Publication year
Publication venue
Materials Chemistry and Mechanics

External Links

Snippet

The current water chemistry regime in combined cycle power plants (CCPPs) with drum boilers and heat recovery steam generators (HRSGs) involves injecting NH3 and Na3PO4 or NaOH into the feed water and boiler water, respectively. This article discusses the …
Continue reading at www.matchemmech.com (PDF) (other versions)

Classifications

    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23F—NON-MECHANICAL REMOVAL OF METALLIC MATERIAL FROM SURFACE; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL; MULTI-STEP PROCESSES FOR SURFACE TREATMENT OF METALLIC MATERIAL INVOLVING AT LEAST ONE PROCESS PROVIDED FOR IN CLASS C23 AND AT LEAST ONE PROCESS COVERED BY SUBCLASS C21D OR C22F OR CLASS C25
    • C23F11/00—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent
    • C23F11/08—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent in other liquids
    • C23F11/10—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent in other liquids using organic inhibitors
    • C23F11/14—Nitrogen-containing compounds
    • C23F11/144—Aminocarboxylic acids
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23F—NON-MECHANICAL REMOVAL OF METALLIC MATERIAL FROM SURFACE; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL; MULTI-STEP PROCESSES FOR SURFACE TREATMENT OF METALLIC MATERIAL INVOLVING AT LEAST ONE PROCESS PROVIDED FOR IN CLASS C23 AND AT LEAST ONE PROCESS COVERED BY SUBCLASS C21D OR C22F OR CLASS C25
    • C23F11/00—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent
    • C23F11/08—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent in other liquids
    • C23F11/10—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent in other liquids using organic inhibitors
    • C23F11/12—Oxygen-containing compounds
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23F—NON-MECHANICAL REMOVAL OF METALLIC MATERIAL FROM SURFACE; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL; MULTI-STEP PROCESSES FOR SURFACE TREATMENT OF METALLIC MATERIAL INVOLVING AT LEAST ONE PROCESS PROVIDED FOR IN CLASS C23 AND AT LEAST ONE PROCESS COVERED BY SUBCLASS C21D OR C22F OR CLASS C25
    • C23F11/00—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent
    • C23F11/08—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent in other liquids
    • C23F11/10—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent in other liquids using organic inhibitors
    • C23F11/173—Macromolecular compounds
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23F—NON-MECHANICAL REMOVAL OF METALLIC MATERIAL FROM SURFACE; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL; MULTI-STEP PROCESSES FOR SURFACE TREATMENT OF METALLIC MATERIAL INVOLVING AT LEAST ONE PROCESS PROVIDED FOR IN CLASS C23 AND AT LEAST ONE PROCESS COVERED BY SUBCLASS C21D OR C22F OR CLASS C25
    • C23F11/00—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent
    • C23F11/08—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent in other liquids
    • C23F11/18—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent in other liquids using inorganic inhibitors
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING ENGINES OR PUMPS
    • F22—STEAM GENERATION
    • F22B—METHODS OF STEAM GENERATION; STEAM BOILERS
    • F22B37/00—Component parts or details of steam boilers
    • F22B37/02—Component parts or details of steam boilers applicable to more than one kind or type of steam boiler
    • F22B37/42—Applications, arrangements, or dispositions of alarm or automatic safety devices
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23F—NON-MECHANICAL REMOVAL OF METALLIC MATERIAL FROM SURFACE; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL; MULTI-STEP PROCESSES FOR SURFACE TREATMENT OF METALLIC MATERIAL INVOLVING AT LEAST ONE PROCESS PROVIDED FOR IN CLASS C23 AND AT LEAST ONE PROCESS COVERED BY SUBCLASS C21D OR C22F OR CLASS C25
    • C23F14/00—Inhibiting incrustation in apparatus for heating liquids for physical or chemical purposes
    • C23F14/02—Inhibiting incrustation in apparatus for heating liquids for physical or chemical purposes by chemical means

Similar Documents

Publication Publication Date Title
Dooley et al. Flow-accelerated corrosion of pressure vessels in fossil plants
Khalifeh Stress corrosion cracking damages
Soltanloo et al. Root cause failure investigation of a boiler waterwall tube employed in a 325 MW thermal power plant: caustic corrosion phenomenon and its effects
Gong et al. Failure analysis on premature fracture of anchor bolts in seawater booster pump of nuclear power plant
French Failures of boilers and related equipment
Liu et al. Corrosion failure analysis of the heat exchanger in a hot water heating boiler
Fazeli et al. Chemical control of water and its effect on flow-accelerated corrosion (FAC) in combined cycle power plants
Saha Boiler tube failures: Some case studies
Utomo et al. A recent review on the failure analysis of boiler tube
Zhou et al. Steam turbine operating conditions, chemistry of condensates and environment assisted cracking-a critical review.
Ranjbar et al. Primming assisted failure of superheater tubes in a sugarcane industry
Petrova et al. International water and steam quality standards on thermal power plants at all-volatile treatment
Haweel et al. Boiler corrosion in thermal power plant: kinetics and mathematical studies
Pourali et al. Chemical conditioning and monitoring to control and minimize chemistry-related damages in Heller dry cooled combined cycle power plants
JP4305440B2 (en) Anticorrosive for reducing erosion and corrosion and method for reducing the same
Sinha Aspects of failure of condenser tubes and their remedial measures at power plants
JP5034483B2 (en) Anticorrosive for reducing erosion and corrosion
Petrova Implementation of water chemistry in fossil power plants with drum boilers and in combined cycle/HRSG plants
Zamrudy et al. Effect of Na2SiO3 (sodium silicate) as a corrosion inhibitor on decreasing the corrosion rate in service water piping in electric steam power plant
Awwaluddin et al. Failure analysis of boiler leakage due to caustic corrosion on Cr-Mo steel
Zakaria et al. Corrosion-erosion on waste heat recovery boiler system via blowdown optimization
Keeth Some corrosion problems encountered in steam plant operations
Rao A Review of Chloride Stress Corrosion Cracking Factors for Austenitic Stainless Steel
Syrett et al. Corrosion in the condensate-feedwater system
Suliman et al. Water quality in HVAC hydronic systems: an international review