Effect of metallurgical variables on the corrosion fatigue behaviour of 304 stainless steel in sulphuric/chloride mediaGouda et al., 1980
- Document ID
- 716453883583090323
- Author
- Gouda V
- Staehle R
- Publication year
- Publication venue
- British Corrosion Journal
External Links
Snippet
The corrosion fatigue behaviour of 304 stainless steel was studied as a funciion of grain size, sensitisation, cyclic load, H2SO4 concentration (1 M–5 M) and in 5 M H2SO4+ 1 M NaCl. Parallel experiments were carried out in air. Sensitisation accelerated the corrosion …
- 238000005260 corrosion 0 title abstract description 54
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| HUANG et al. | Influence of thermomechanical treatments on localized corrosion susceptibility and propagation mechanism of AA2099 Al–Li alloy | |
| Kruger¹ | Fundamental aspects of the corrosion of metallic implants | |
| Liao et al. | Effects of Ti content on the microstructure, mechanical properties and corrosion behavior of TixZrNb alloys | |
| Lu et al. | Corrosion behavior of a non-equiatomic CoCrFeNiTi high-entropy alloy: A comparison with 304 stainless steel in simulated body fluids | |
| Ramirez et al. | Cold rolling effect on the microstructure and pitting resistance of the nbr iso 5832-1 austenitic stainless steel | |
| Talha et al. | Long term and electrochemical corrosion investigation of cold worked AISI 316L and 316LVM stainless steels in simulated body fluid | |
| Bayoumi | The mechanics and mechanisms of fracture in stress corrosion cracking of aluminium alloys | |
| Lim et al. | Influence of laser surface melting on the susceptibility to intergranular corrosion of sensitized Alloy 600 | |
| Martin et al. | Passivity breakdown and crack propagation mechanisms of lean duplex (UNS S32001) stainless steel reinforcement in high alkaline solution under stress corrosion cracking | |
| Corsetti et al. | The effect of mean stress and environment on corrosion fatigue behavior of 7075-T6 aluminum | |
| Monticelli et al. | Stress corrosion cracking behaviour of some aluminium-based metal matrix composites | |
| Gouda et al. | Effect of metallurgical variables on the corrosion fatigue behaviour of 304 stainless steel in sulphuric/chloride media | |
| Foct et al. | Stress corrosion cracking mechanisms of alloy 600 polycrystals and single crystals in primary water—Influence of hydrogen | |
| HUANG et al. | Correlations among stress corrosion cracking, grain-boundary microchemistry, and Zn content in high Zn-containing Al–Zn–Mg–Cu alloys | |
| Chen et al. | Corrosion fatigue of a precipitation-hardened Al-Li-Zr alloy in a 0.5 M sodium chloride solution | |
| Berkeley et al. | The effect of pH on the mechanism of corrosion and stress corrosion and degradation of mechanical properties of AA6061 and Nextel 440 fiber-reinforced AA6061 composite | |
| El-Bagoury et al. | Effect of various heat treatment conditions on microstructure, mechanical properties and corrosion behavior of Ni base superalloys | |
| Schuster et al. | Characterisation of Zircaloy corrosion fatigue phenomena in an iodine environment: Part 1: crack growth | |
| Qi et al. | Effects of cathodic polarization on SCC behavior of AA7003 under various aging treatments | |
| Gupta et al. | Influence of deformation and annealing on microstructure and corrosion behavior of austenitic stainless steel | |
| JPS62216B2 (en) | ||
| Qi et al. | Correspondence between susceptibility to SCC of 7050 aluminum alloy and passive film-induced stress at various pH values | |
| Tsai et al. | The stress corrosion crack growth rate in sensitized alloy 600 in thiosulfate solution | |
| Park et al. | Optimizing microstructure of medium Ni-bearing steel to ensure high resistance to corrosion and corrosion-assisted mechanical degradation | |
| Roychowdhury et al. | Role of environmental variables on the stress corrosion cracking of sensitized AISI type 304 stainless steel (SS304) in thiosulfate solutions |