Experimental characterization of microscopic damage progress in quasi-isotropic CFRP laminates: effect of interlaminar-toughened layers

Takeda et al., 1998

Document ID
5097649463196276735
Author
Takeda N
Kobayashi S
Ogihara S
Kobayashi A
Publication year
Publication venue
Advanced composite materials

External Links

Snippet

Microscopic damage progress under static tensile loading in quasi-isotropic CFRP laminates was observed by an optical microscope and a scanning acoustic microscope (SAM). Material systems used were toughened-type CFRP, T800H/3631 and newly …
Continue reading at www.tandfonline.com (other versions)

Classifications

    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10S—TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10S428/00—Stock material or miscellaneous articles
    • Y10S428/902—High modulus filament or fiber

Similar Documents

Publication Publication Date Title
Ye Role of matrix resin in delamination onset and growth in composite laminates
Sela et al. Interlaminar fracture toughness and toughening of laminated composite materials: a review
Hull et al. Damage mechanism characterization in composite damage tolerance investigations
Sohn et al. Impact damage characterisation of carbon fibre/epoxy composites with multi-layer reinforcement
Xu et al. Improving compression-after-impact performance of carbon–fiber composites by CNTs/thermoplastic hybrid film interlayer
Khan et al. Fatigue behaviour of stitched GRP laminates
Lagace et al. Impact damage resistance of several laminated material systems
Gao et al. Mode II delamination and damage resistance of carbon/epoxy composite laminates interleaved with thermoplastic particles
Fotouhi et al. Notch insensitive orientation-dispersed pseudo-ductile thin-ply carbon/glass hybrid laminates
Takeda et al. Experimental characterization of microscopic damage progress in quasi-isotropic CFRP laminates: effect of interlaminar-toughened layers
Imielińska et al. Effects of manufacturing and face/core bonding on impact damage in glass/polyester–PVC foam core sandwich panels
Lavoie et al. Stitch cracks in constraint plies adjacent to a cracked ply
Kinsey et al. Post-impact compressive behaviour of low temperature curing woven CFRP laminates
Ogihara et al. Experimental characterization of microscopic failure process under quasi-static tension in interleaved and toughness-improved CFRP cross-ply laminates
Reifsnider et al. Delamination in quasi-isotropic graphite-epoxy laminates
Venkatesan et al. The influence of thickness and recycled milled glass fiber fillers on the delamination resistance of polymer composite angle brackets
Greenhalgh et al. Fractographic study into the effect of drilling damage on bearing mechanisms and performance in Carbon-Fibre epoxy composites
Curson et al. Impact failure mechanisms in carbon fiber/PEEK composites
Chen et al. Fatigue-induced damage mechanisms in carbon fibre-reinforced plastic composites
Kim et al. Impact performance of a woven fabric CFRP laminate
Kobayashi et al. Experimental characterization of the effects of stacking sequence on the transverse crack behavior in quasi-isotropic interleaved CFRP laminates
Xian et al. The interlaminar fracture behaviour and toughening mechanisms of new carbon fibre-reinforced bismaleimide composites
Ogihara et al. Damage mechanics characterization of transverse cracking behavior in high-temperature CFRP laminates
Davies et al. Interlaminar tests for marine applications. Evaluation of the influence of peel plies and fabrication delays
Kuboki et al. Interlaminar fracture toughness and the associated fracture behavior for glass fiber reinforced polymers (GFRP)