Moloko, 2019 - Google Patents
Investigation of the Mechanisms and Control Measures for Fireside Corrosion in Eskom Fossil Fuel BoilersMoloko, 2019
- Document ID
- 4457408806046846215
- Author
- Moloko K
- Publication year
- Publication venue
- PQDT-Global
External Links
Snippet
Fireside corrosion in fossil-fired boilers is still amongst the damage mechanisms that contribute toward the most boiler tube failures. It was first identified in South African power generation utilities in the early 1990s when a number of coal-fired subcritical boilers (600 …
Classifications
-
- F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING ENGINES OR PUMPS
- F23—COMBUSTION APPARATUS; COMBUSTION PROCESSES
- F23N—REGULATING OR CONTROLLING COMBUSTION
- F23N5/00—Systems for controlling combustion
- F23N5/003—Systems for controlling combustion using detectors sensitive to combustion gas properties
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Harb et al. | Fireside corrosion in PC-fired boilers | |
| Srivastava et al. | Fuel ash corrosion of boiler and superheater tubes | |
| Gruber et al. | Investigation of the corrosion behaviour of 13CrMo4–5 for biomass fired boilers with coupled online corrosion and deposit probe measurements | |
| Pal et al. | Failure analysis of boiler economizer tubes at power house | |
| Yan et al. | Failure mechanism of superheater tubes of waste heat boiler for waste incineration in complex environment | |
| Chaudhuri | Some aspects of metallurgical assessment of boiler tubes—Basic principles and case studies | |
| Xiong et al. | A typical super-heater tube leakage and high temperature corrosion mechanism investigation in a 260 t/h circulated fluidized boiler | |
| French | Failures of boilers and related equipment | |
| Asnavandi et al. | Fire‐Side Corrosion: A Case Study of Failed Tubes of a Fossil Fuel Boiler | |
| Moloko et al. | Investigation of the mechanism for fireside corrosion in coal-fired boilers in South Africa | |
| Daniel et al. | Furnace-wall corrosion in refuse-fired boilers | |
| Moloko | Investigation of the Mechanisms and Control Measures for Fireside Corrosion in Eskom Fossil Fuel Boilers | |
| Gong et al. | Corrosion evaluation of one dry desulfurization equipment–Circulating fluidized bed boiler | |
| Simms | Environmental degradation of boiler components | |
| Husain et al. | Metallurgical failure analysis of economizer tube of thermal power plant | |
| Liu et al. | High‐temperature corrosion behavior of S30432 and TP310HCbN coatings in simulated 620° C ultra‐supercritical boiler coal ash/gas environment | |
| Triasdian et al. | Failure analysis of water wall tube in circulating fluidized bed boiler | |
| Fatah et al. | Failure investigation of fire-side water-wall tube boiler | |
| Nava-Paz et al. | Waterwall corrosion mechanisms in coal combustion environments | |
| Rahman et al. | Failure analysis of high temperature superheater tube (HTS) of a pulverized coal-fired power station | |
| Hadianfard et al. | Root cause analysis and damage mechanisms of radiant tube failure in the atmospheric distillation unit of an oil refinery | |
| Meroufel et al. | Severe under-deposit corrosion inducing hydrogen embrittlement in water wall tubes | |
| Larsen et al. | Materials problems and solutions in biomass fired plants | |
| Dong et al. | Comparative Analysis of Failure Mechanisms in 12CrMoVG Steel Dual Tubes for Boiler Low-Temperature Reheaters | |
| Li et al. | Failure Analysis of Welded Joint in Superheater Tube in a Waste Incineration Boiler |