Kuzyukov et al., 1999 - Google Patents
Corrosion cracking of chemical and petrochemical equipmentKuzyukov et al., 1999
- Document ID
- 4189433888566732438
- Author
- Kuzyukov A
- Borisenko V
- Levchenko V
- Nikhaenko Y
- Publication year
- Publication venue
- Materials Science
External Links
Snippet
For technological facilities used in chemical and petrochemical industries, we present certain examples of the process of corrosion cracking of copper-lined apparatus and the equipment, manufactured from carbon and stainless steels of the 08Kh18N10T and …
- 238000005260 corrosion 0 title abstract description 87
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Warke | Stress-corrosion cracking | |
| US6010669A (en) | Method for restoring the functionality of equipment subjected to heavy corrosion in a plant for the production of urea | |
| Shankar et al. | Failure analysis of titanium heater tubes and stainless steel heat exchanger weld joints in nitric acid loop | |
| Liu et al. | Corrosion failure analysis of the heat exchanger in a hot water heating boiler | |
| KR101603455B1 (en) | Process and apparatus for treating hydrocarbon streams | |
| Kuzyukov et al. | Corrosion cracking of chemical and petrochemical equipment | |
| Hänninen et al. | Environment sensitive cracking in pressure boundary materials of light water reactors | |
| Hickling | “Strain Induced Corrosion Cracking: Relationship to Stress Corrosion Cracking/Corrosion Fatigue and Importance for Nuclear Plant Service Life | |
| Yu et al. | Crack failure analysis of stainless steel seamless pipe | |
| Jiajun et al. | Research Progress on Hydrogen-assisted Fatigue Crack Growth of Pipeline Steels in Hydrogen-blended Natural Gas Environment | |
| Polyakov et al. | The main mechanisms of stress corrosion cracking in natural gas trunk lines | |
| Moller | Designing with stainless steels for service in stress corrosion environments | |
| Chen et al. | Several failure analysis cases of pressure equipment under the conditions of complex medium environment | |
| Eastep et al. | Stress-Corrosion Cracking | |
| Avery et al. | Stainless steel for potable water treatment plants (PWTP)—Guidelines | |
| Hargrave et al. | Stress-Assisted Corrosion in Recovery Boilers | |
| Pircher | Behavior of pressure-vessel steels exposed to hydrogen from corrosion and environment | |
| Shi et al. | Failure Analysis of a Cracked Stainless-Steel Steam-Water Separator | |
| Wang et al. | Failure Analysis and Treatment of Under-Scale Corrosion Burst in CFB Boilers’ Water Wall Tube | |
| Vainman et al. | Effects of hydrogen on stress cracking in unheated thermal powder station pipes | |
| Timofeev et al. | Intercrystalline corrosion cracking of welded joints of the austenitic pipelines of nuclear power plants | |
| Elliott | Materials selection for corrosion control | |
| Wang et al. | Failure Analysis of a Waste Heat Boiler of a Sulfur-Burning Sulfuric Acid Plant | |
| Harrison | Corrosion of Feed Line Surfaces | |
| Singh | Applied chemistry |