TWI498645B - 液晶顯示器及補償膜 - Google Patents
液晶顯示器及補償膜 Download PDFInfo
- Publication number
- TWI498645B TWI498645B TW101142288A TW101142288A TWI498645B TW I498645 B TWI498645 B TW I498645B TW 101142288 A TW101142288 A TW 101142288A TW 101142288 A TW101142288 A TW 101142288A TW I498645 B TWI498645 B TW I498645B
- Authority
- TW
- Taiwan
- Prior art keywords
- liquid crystal
- crystal display
- compensation layer
- compensation
- film
- Prior art date
Description
本發明是有關於一種液晶顯示器，且特別是有關於一種垂直配向型(vertical alignment)液晶顯示器，其包括能夠改良視角的補償層。
液晶顯示器(liquid crystal display,LCD)是目前應用最廣泛的平板顯示器之一。通常，液晶顯示器具有封裝(encapsulated)在薄膜電晶體(thin film transistor,TFT)陣列基板與彩色濾光片基板(color filter substrate)之間的液晶層。當電場被施加在陣列基板與彩色濾光片基板的電極上時，封裝在這兩個基板之間的液晶層的液晶分子被重新排列，從而顯示出影像。液晶顯示器包括偏光膜(polarizing film)(偏光板)，其位於陣列基板與彩色濾光片基板外。此偏光膜能夠使背光單元(backlight unit)所發出的光當中的沿著特定方向傳播且已穿過液晶層的光發生選擇性透射，以此方式來控制偏光(polarization of light)。偏光板通常包括能夠使光朝著特定方向偏振的偏光片(polarizer)、保護層以及補償膜。
因液晶折射率存在異向性(anisotropy)而導致的視角問題是液晶顯示器的一個基本問題。為了改良現有的扭轉向列(twisted nematic,TN)模式的視角，已採用多種廣視角技術，如垂直配向(vertical alignment,VA)模式、水平
配向模式(IPS,FFS)等等。
水平配向模式液晶的缺點在於反應速度慢，但它提供良好的對比度，且在傾斜角度下提供良好的視角。相反，垂直配向模式液晶的反應速度快，且提供卓越的前對比度(front contrast ratio)。然而，在傾斜角度下由於偏振狀態波動劇烈，所以垂直配向模式液晶會呈現較低的視角特性。因此，對於使用垂直配向模式液晶的液晶顯示器而言，改良視角特性極為重要，而用以改良視角的補償膜是使用垂直配向模式液晶的液晶顯示器所不可或缺的。
對於使用垂直配向模式液晶的液晶顯示器所用的習知的補償膜，慢軸(slow axis)受到雙軸拉伸(biaxial elongation)的操控。然而，當慢軸受到雙軸拉伸的操控時，必須對慢軸進行寬度方向的設定，這導致必須單獨進行橫向拉伸，因而控制此軸變得困難，且增加製造成本。
本發明的目的是提供一種包括單軸定向(uniaxially oriented)補償層的液晶顯示器，它能夠顯著改良視角(對比度)，協助進行軸操控，且降低成本。本發明特別是要提供一種使側面視角(對比度)得以顯著改良的垂直配向液晶顯示器。
本發明之一觀點提供一種液晶顯示器。此液晶顯示器包括：液晶面板，其包括封裝在第一基板與第二基板之間的垂直配向液晶；第一補償層，其堆疊(stacked)在第一
基板的一側；第一偏光層，其堆疊在第一補償層的一側；第二補償層，其堆疊在第二基板的一側；以及第二偏光層，其堆疊在第二補償層的一側，其中第一補償層包括聚醯亞胺共聚物(polyimide copolymer)。此處，聚醯亞胺共聚物是指含有馬來醯亞胺(maleimide)化合物和芳香族乙烯基(aromatic vinyl)化合物的單體混合物的共聚物
在一實施例中，單體混合物可更包括順丁烯二酐(maleic anhydride)。
在一實施例中，單體混合物可更包括順丁烯二酐與丙烯腈(vinyl cyanide)化合物。
在一實施例中，聚醯亞胺共聚物可包括用化學式1-1表示的單元、用化學式1-2表示的單元、用化學式1-3表示的單元以及用化學式1-4表示的單元：
其中R為氫原子、經取代或未經取代的C1
~C6
烷基(alkyl group)或者經取代或未經取代的C6
~C12
芳基(aryl group)；[化學式1-2]
其中Ar各自獨立為經取代或未經取代的C6
~C12
芳基；
在一實施例中，聚醯亞胺共聚物可用化學式1來表示：
其中R為氫原子、經取代或未經取代的C1
~C6
烷基或者經取代或未經取代的C6
~C12
芳基；Ar各自獨立為經取代或未經取代的C6
~C12
芳基；以及M與N各自獨立為2到8的整數。
在一實施例中，第一補償層可具有反波長色散
(reversed wavelength dispersion)特性。
在一實施例中，第一補償層可具有：Cs
為-0.7至-0.2；波長為550 nm時Re
為40 nm至100 nm；以及波長為550 nm時Rth
為100 nm至150 nm。
在一實施例中，第二補償層可以是雙軸膜或C板。
在一實施例中，雙軸膜可具有：同一平面的x方向及y方向的折射率(nx
,ny
)與厚度方向的折射率(nz
)滿足以下關係nx
>ny
>nz
；Re
大於0(Re
>0)；以及Rth
小於0(Rth
<0)。雙軸膜可以是環烯聚合物(cycloolefin polymer,COP)、三乙酸纖維素(triacetate cellulose,TAC)或聚醚碸(polyether sulfone,PES)補償膜。
在一實施例中，C板可以是環烯聚合物或丙烯酸補償膜，其同一平面的x方向及y方向的折射率(nx
,ny
)與厚度方向的折射率(nz
)滿足以下關係nx
=ny
<nz
，且Rth
大於0(Rth
>0)。
在一實施例中，第一補償層的慢軸可垂直於第二補償層的慢軸。此處，第一補償層的慢軸可垂直於第一偏光層的吸收軸，且第二補償層的慢軸可垂直於第二偏光層的吸收軸。
本發明之另一觀點提供一種補償膜，其包括由馬來醯亞胺化合物衍生的重複單元、由芳香族乙烯基化合物衍生的重複單元、由順丁烯二酐衍生的重複單元以及由丙烯腈化合物衍生的重複單元。
在一實施例中，第一補償層具有：Cs
為-0.7至-0.2；
波長為550 nm時Re
為40 nm至100 nm；以及波長為550 nm時Rth
為100 nm至150 nm。
下面將參照所附圖式來詳細敍述本發明的各實施例。
圖1是依照本發明之一實施例的一種液晶顯示器的剖面圖。在圖1中，依照本發明之一實施例的液晶顯示器100包括液晶面板，所述液晶面板包括封裝在第一基板104與第二基板106之間的液晶層102，其中第一光學膜110堆疊在第一基板104的一側(上側)，且第二光學膜120堆疊在第二基板106的一側(下側)。
如本文所用的術語“上側”與“下側”是為了便於參考圖式的上側與下側而提出，未必是指上面部分與下面部分。
在一實施例中，第一基板104可以是彩色濾光片(CF)基板(上基板)，且第二基板106可以是薄膜電晶體(TFT)基板(下基板)。
第一基板104與第二基板106可以是玻璃基板或塑膠基板。塑膠基板適用於可撓性顯示器，且可包括聚對苯二甲酸乙二酯(polyethylene terephthalate,PET)、聚碳酸酯(polycarbonate,PC)、聚醯亞胺(polyimide,PI)、聚萘二甲酸乙二酯(polyethylene naphthalate,PEN)、聚醚碸(polyether sulfone,PES)、聚芳酯(polyarylate,PAR)以及環烯共聚物(cycloolefin copolymers,COC)(但不限於這些)中的至少一者。
本發明之第一光學膜110可包括第一補償層112與第一偏光層114。第一光學膜110可更包括第一保護層116等等。也就是說，第一光學膜110可以是包括偏光層(偏光片)的偏光板。
第一補償層112可包括聚醯亞胺(PI)共聚物。此聚醯亞胺共聚物可以是含有馬來醯亞胺化合物(maleimide compound)和芳香族乙烯基化合物(aromatic vinyl compound)的單體混合物的共聚物。舉例而言，此單體混合物可更包括順丁烯二酐。較佳的是，此單體混合物更包括順丁烯二酐與丙烯腈化合物。
換言之，第一補償層112之共聚物可包括由馬來醯亞胺化合物衍生的化學式1-1的重複單元(N上經取代之馬來醯亞胺(N-substituted maleimide))：
其中R為氫原子、經取代或未經取代的C1
~C6
烷基或者經取代或未經取代的C6
~C12
芳基(aryl group)，以及由芳香族乙烯基化合物衍生的化學式1-2的重複單元：[化學式1-2]
其中Ar為經取代或未經取代的C6
~C12
芳基，以及選擇性地包括由順丁烯二酐衍生的化學式1-3的重複單元：
以及由丙烯腈化合物衍生的化學式1-4的重複單元：
當此共聚物包括由順丁烯二酐衍生的重複單元時，其與構成第一偏光層114的水溶性聚乙烯醇(polyvinyl alcohol,PVA)薄膜之間的黏著可得以改良。
在一實施例中，聚醯亞胺共聚物可以是含有馬來醯亞胺化合物和芳香族乙烯基化合物以及選擇性地含有順丁烯二酐和丙烯腈化合物的單體混合物的共聚物。此共聚物可透過自由基聚合作用(radical polymerization)使單體混合物發生共聚合作用(copolymerizing)來製備而成，且此共聚物可在市場上購買。舉例而言，此共聚物可藉由以下步
驟來製備：將用來製備共聚物的所有單體同時放入聚合反應器，然後使所形成的混合物發生共聚合作用。
在另一實施例中，聚醯亞胺共聚物可藉由以下步驟來製備：使含有馬來醯亞胺化合物、芳香族乙烯基化合物以及選擇性地含有順丁烯二酐的單體混合物發生共聚合作用，然後將已製備的共聚物與芳香族乙烯基化合物和丙烯腈化合物的共聚物混合在一起。
在另一實施例中，聚醯亞胺共聚物可藉由以下步驟來製備：使含有馬來醯亞胺化合物、芳香族乙烯基化合物以及選擇性地含有順丁烯二酐的單體混合物發生共聚合作用，然後將已製備的共聚物與芳香族乙烯基聚合物和丙烯腈聚合物混合在一起。
聚醯亞胺共聚物的具體實例可包括用化學式1表示的共聚物，但並不限於此。
在化學式1中，R為氫原子、經取代或未經取代的C1
~C6
烷基或者經取代或未經取代的C6
~C12
芳基，Ar各自獨立為經取代或未經取代的C6
~C12
芳基，且M與N各自獨立為2至8整數。
其中，用化學式1表示的共聚物是指藉由以下步驟來
製備的聚醯亞胺共聚物：使含有馬來醯亞胺化合物、芳香族乙烯基化合物以及順丁烯二酐的單體混合物發生共聚合作用，然後將已製備的共聚物與芳香族乙烯基化合物和丙烯腈化合物的共聚物或者與芳香族乙烯基聚合物和丙烯腈聚合物混合在一起，其中此共聚物的每個重複單元的內容和重量平均分子量與習知的共聚物幾乎相同，但並不限於此，且其中芳香族乙烯基化合物相對於丙烯腈化合物的含量比(content ratio)介於2：8至8：2範圍內。
可對包括聚醯亞胺共聚物的補償層(補償膜)進行單軸拉伸，以便提供橫光軸。也就是說，當進行拉伸時，共軛雙鍵(conjugated double bonds)的方位會對慢軸進行橫向(transverse direction,TD)控制，這樣便排除了單獨進行橫向拉伸的必要性，從而使補償層的製造變得容易，同時顯著降低製造成本。
根據光軸的數量，補償層(補償膜)可分為單軸補償層與雙軸補償層。也就是說，當補償層具有單一個光軸時，稱其為單軸補償層，而當補償層具有兩個光軸時，稱其為雙軸補償層。此外，根據光軸方向的折射率與另一方向的折射率之間的差，補償層(補償膜)可稱為正補償層與負補償層。也就是說，若光軸方向的折射率大於另一方向的折射率，則稱其為正補償層。若光軸方向的折射率小於另一方向的折射率，則稱其為負補償層。
液晶顯示器用的補償膜具有相位延遲(phase retardation)值，故能夠抵消或增加由液晶胞(cells)所引
起的相位延遲。相位延遲值的種類包括兩種，即，平面內(in-plane)的相位延遲值(Re
)與厚度方向的相位延遲值(Rth
)，其由方程式1來定義。
[方程式1]Re
=(nx
-ny
)×d Rth
=(nz
-(nx
+ny
)/2)×d Cs
=(nx
-ny
)/(nz
-ny
)
其中，nx
、ny
及nz
分別表示x軸、y軸以及z軸(厚度)方向的折射率，d表示膜的厚度，且Cs
表示平面內折射率軸與垂直方向軸之間的折射率之比。此處，x軸是指平面內折射率變為最大值的方向，y軸是指垂直於x軸的方向，且z軸是指厚度方向。
第一補償層112可以是含有聚醯亞胺共聚物的雙軸膜，舉例而言，此聚醯亞胺共聚物是聚醯亞胺與聚苯乙烯(polystyrene)的共聚物，具體而言，此聚醯亞胺共聚物是用化學式1表示的共聚物。更具體而言，第一補償層可以是負雙軸膜，其同一平面的x方向和y方向的折射率nx
、ny
與厚度方向的折射率nz
滿足以下關係nz
>nx
>ny
。
第一補償層112可具有反波長色散(reversed wavelength dispersion)特性。反波長色散的意思是：當可見光範圍內的波長增大時，平面內的相位延遲值(Re
)增大。若補償層具有反波長色散特性，則它能夠補償垂直配向液晶的正波長色散，從而改良側表面的側面對比與色移(color shift)。
第一補償層112在波長為550 nm時的Re
可介於40 nm至100 nm範圍內，較佳的是介於45 mm至95 nm範圍內。第一補償層112在波長為550 nm時的Rth
可介於100 nm至150 nm範圍內，較佳的是介於105 mm至145 nm範圍內。在此範圍內，側面視角可大大改良，特別是垂直配向模式液晶的側面對比度(lateral contrast ratio)能夠得到顯著改良。
由兩個習知的雙軸膜所形成的補償膜具有介於-0.5至-0.3範圍內的Cs
。不同的是，包括聚醯亞胺共聚物的第一補償層112具有介於-0.7至-0.2範圍內的Cs
(係數)，因而能夠製造Cs
值範圍較廣的補償層(膜)。
第一補償層112可形成薄膜形狀，且與第一偏光層114堆疊在一起。第一補償層可具有5 μm至100 μm範圍內的厚度。根據液晶的種類(物理性質)、液晶層的厚度等等，可對補償層的厚度進行適當調整。
第一偏光層114可包括藉由以下步驟來製備的偏光片：用雙色材料(如碘)將聚乙烯醇(polyvinyl alcohol,PVA)薄膜染色，然後拉伸此薄膜。聚乙烯醇薄膜可在市場上購買，或者透過溶劑澆鑄法(solvent casting)、熔體擠出法(melt extrusion)等等來製備。在溶劑澆鑄法中，薄膜可藉由以下步驟來製備：使樹脂在溶劑中溶解以形成溶液；將所形成的溶液塗佈(coating)在鑄造滾筒(casting roll)或鑄造帶(casting belt)上；以及烘乾此塗層。在熔體擠出法中，薄膜可藉由以下步驟來製備：將樹脂加熱至
熔融溫度，以便使樹脂熔化；將熔體擠到冷卻滾筒(cold roll)中；以及使熔體冷卻下來。
用來製備薄膜的溶液可更包括：塑化劑，其用以提高聚乙烯醇薄膜的可撓性；以及界面活性劑，其用以從鑄造帶或鑄造桶(drum)上移除乾燥後的聚乙烯醇薄膜。如此製備的聚乙烯醇薄膜或習知的聚乙烯醇薄膜可經拉伸以便製備偏光片(偏光層)。詳細而言，可對聚乙烯醇進行沖洗/膨潤(swelling)、染色、交聯(crosslinking)、拉伸以及補色處理。
偏光片包括長的烴類鏈環(chain ring of hydrocarbons)，其在聚乙烯醇薄膜拉伸方向上排成一列。此鏈環因染有碘分子而具有導電性。當光的電場向量平行於此鏈環時，此光可被吸收，所以拉伸方向變為光吸收軸(absorption axis)，而垂直於吸收軸的軸則稱為傳送軸(transmission axis)。
第一保護層116可包括(例如)諸如三乙醯纖維素(triacetyl cellulose,TAC)等醋酸鹽薄膜、聚碳酸酯薄膜、聚醯胺(polyamides)薄膜、聚醯亞胺薄膜、聚烯烴(polyolefins)薄膜、聚酯(polyesters)薄膜、聚醚碸薄膜以及聚丙烯(polypropylene,PP)薄膜。較佳的是使用三乙醯纖維素。
此外，第一補償層112下方，也就是第一基板104與第一補償層112之間，可形成壓敏黏合劑(pressure sensitive adhesive)。第一保護層116的一側(上側)可形成表面
處理層(未繪示)。此表面處理層可以是防眩層(antiglare layer,AG)或防反射塗層(anti-reflection coating,ARC)。
本發明之第二光學膜120包括第二補償層122與第二偏光層124。此外，第二光學膜120可包括第二保護層126。假如在切割製程中第二偏光層124與第一偏光層114可經切割以使得偏光片的光軸(吸收軸)相互垂直(90°)，則第二偏光層124與第一偏光層114相同，且可以是用相同方法製造的偏光片(偏光層)。
第二補償層122可以是雙軸膜或C板(C-plate)。此雙軸膜可以是正雙軸膜，其同一平面的x方向和y方向的折射率(nx
,ny
)與厚度方向的折射率(nz
)滿足以下關係：nx
>ny
>nz
。較佳的是，第二補償層是環烯聚合物(COP)薄膜、三乙醯纖維素(TAC)薄膜或聚醚碸(PES)薄膜。
C板可以是正C板，其同一平面的x方向和y方向的折射率nx
、ny
與厚度方向的折射率nz
滿足以下關係：nx
=ny
<nz
，且Rth
>0。C板可由同向(homeotropic)液晶製造而成，且可以是環烯聚合物或丙烯酸C板。
液晶層102可以是包括垂直配向模式液晶的液晶層。垂直配向模式的實例包括多域(multi-domain)垂直配向模式，在此模式中，與液晶層相鄰的表面上形成有包括第一基板和第二基板上的多個電極對(pairs)的脊狀物(ridge)，以便形成一種多域的圖案化(patterned)垂直配向模式，其透過對圖案化電極施加電壓、垂直配向模式使用對掌型添加劑(chiral additives)等等來形成多域結
構，其中液晶胞的胞間隙可以是2 μm至8 μm。
圖2是依照本發明之一實施例來解釋液晶顯示器之光軸的概念圖。如圖2所示，第一補償層112的慢軸112a可垂直於第一偏光層的吸收軸114a；第一補償層的慢軸112a可垂直於第二補償層122的慢軸122a；以及第二補償層122的慢軸122a可垂直於第二偏光層124的吸收軸124a。當按上述排列時，這兩個相位延遲膜呈現出卓越的波長色散特性(如良好的折射率)，從而大大改良視角特性。特別是，側面視角(對比度)得以顯著改良。
其中，光軸排列的表述中所用的術語“垂直於”意思是其包括光軸實質上垂直於另一個軸的情形。舉例而言，第一偏光層114的吸收軸114a垂直於第二偏光層124的吸收軸124a，其中垂直角度包括90°±2.0°，較佳的是90°±1.0°，更佳的是90°±0.5°。
液晶顯示器具有垂直於光傳播方向的慢軸與快軸，且這兩個軸相互垂直。第一補償層112與第二補償層122的作用是改變入射光的相速度(phase velocity)，使得沿著慢軸而傳播的偏光的速度變慢。
接下來將參照一些實例來更詳細地解釋本發明。提供這些實例只是為了舉例說明，而不應理解為是對本發明任何形式的限定。
實例
實例1~7
彩色濾光片基板用作上基板，也就是第一基板。聚醯亞胺(PI)補償膜作為第一補償層而附著在第一基板上。第一偏光層與第一保護層按此順序堆疊在第一補償層的一側。薄膜電晶體基板用作下基板，也就是第二基板。雙軸或C板補償膜作為第二補償層而附著在第二基板的一側。此外，第二偏光層與第二保護層按此順序堆疊在第二補償層的一側，從而製造成垂直配向模式液晶顯示器。第一補償層與第二補償層如表1所列舉。
比較例1~4
除了第一補償層與第二補償層如表1所示進行更動外，垂直配向模式液晶顯示器是按實例1的相同方式來製造。
*聚醯亞胺補償膜：此聚醯亞胺補償膜包括用化學式1表示的共聚物，其同一平面的x方向和y方向的折射率nx
、ny
與厚度方向的折射率nz
滿足以下關係nz
>nx
>ny
，Re
為40 nm至100 nm，且Rth
為100 nm至150 nm。實例1、實例3及實例7中所用的聚醯亞胺補償膜是波長為550 nm時滿足Re
/Rth
=50/135 nm的補償膜。實例2、實例4至實例6中所用的聚醯亞胺補償膜是波長為550 nm時滿足Re
/Rth
=40/125 nm的補償膜。
*雙軸補償膜：使用符合以下條件的雙軸膜(Zeon公司)，其同一平面的x方向和y方向的折射率nx
和ny
與厚度方向的折射率nz
滿足以下關係nx
>ny
>nz
，Re
>0，且Rth
<0。
*C板補償膜：使用符合以下條件的補償膜(JSR公司)，其同一平面的x方向和y方向的折射率nx
、ny
與厚度方向的折射率(nz
)滿足以下關係nx
=ny
<nz
，且Rth
>0。
*A板補償膜：使用符合以下條件的補償膜(JSR公司)，其同一平面的x方向和y方向的折射率nx
、ny
與厚度方向的折射率nz
滿足以下關係nx
>ny
=nz
，且Re
>0。
光學性質評估
將表1所示之實例1~7與比較例1~4中所用的補償膜附著在垂直配向模式液晶面板上，並對其光學性質進行評估。使用SR3裝置來測量白場及黑場亮度(white and black brightness)。此外，根據白場/黑場亮度來計算方位角(azimuth angle)(φ)為45°且極角(polar angle)(θ)為60°時的側面對比度。結果總結於表2中。
圖3與圖4繪示為當使用白光來進行模擬時實例1與實例2中的垂直配向模式液晶顯示器在每個共界角(coterminal angle)處的對比度模擬結果。
從表2可以清楚看到，實例1至7中所用的液晶顯示
器的平均側面對比度為137.4，且比較例1至4中所用的液晶顯示器的平均側面對比度為92.3，也就是說，實例1至7中所用的液晶顯示器的平均側面對比度高於比較例1至4中所用的液晶顯示器的平均側面對比度約49%。
雖然本文已揭露一些實施例，然而容易為所屬技術領域中具有通常知識者所理解的是，提供這些實施例只是為了舉例說明，在不脫離本發明之精神和範圍的前提下，當可作各種改良、更動與潤飾，故本發明之保護範圍僅以後附之申請專利範圍及其等同部分所界定者為準。
100‧‧‧液晶顯示器
102‧‧‧液晶層
104‧‧‧第一基板
106‧‧‧第二基板
110‧‧‧第一光學膜
112‧‧‧第一補償層
112a、122a‧‧‧慢軸
114‧‧‧第一偏光層
114a、124a‧‧‧吸收軸
116‧‧‧第一保護層
120‧‧‧第二光學膜
122‧‧‧第二補償層
124‧‧‧第二偏光層
126‧‧‧第二保護層
圖1是依照本發明之一實施例的一種液晶顯示器的剖面圖。
圖2是依照本發明之一實施例來解釋液晶顯示器之光軸的概念圖。
圖3與圖4繪示為當使用白光來進行模擬時實例1與實例2中的垂直配向模式液晶顯示器在每個經度角(longitude angle)處的對比度模擬結果。
100‧‧‧液晶顯示器
102‧‧‧液晶層
104‧‧‧第一基板
106‧‧‧第二基板
110‧‧‧第一光學膜
112‧‧‧第一補償層
114‧‧‧第一偏光層
116‧‧‧第一保護層
120‧‧‧第二光學膜
122‧‧‧第二補償層
124‧‧‧第二偏光層
126‧‧‧第二保護層
Claims (13)
- 一種液晶顯示器，包括：液晶面板，其包括封裝在第一基板與第二基板之間的垂直配向液晶；第一補償層，其堆疊在所述第一基板的一側；第一偏光層，其堆疊在所述第一補償層的一側；第二補償層，其堆疊在所述第二基板的一側；以及第二偏光層，其堆疊在所述第二補償層的一側，其中所述第一補償層包括聚醯亞胺共聚物，且所述聚醯亞胺共聚物是含有馬來醯亞胺化合物、芳香族乙烯基化合物、順丁烯二酐與丙烯腈化合物的單體混合物的共聚物，其中當波長為550nm時所述第一補償層的Re 介於40nm至100nm範圍內。
- 如申請專利範圍第1項所述之液晶顯示器，其中所述聚醯亞胺共聚物包括用化學式1-1表示的單元、用化學式1-2表示的單元、用化學式1-3表示的單元以及用化學式1-4表示的單元：
- 如申請專利範圍第1項所述之液晶顯示器，其中所述聚醯亞胺共聚物是用化學式1來表示：
- 如申請專利範圍第1項所述之液晶顯示器，其中所述第一補償層具有反波長色散特性。
- 如申請專利範圍第1項所述之液晶顯示器，其中所述第一補償層具有-0.7至-0.2的Cs 。
- 如申請專利範圍第1項所述之液晶顯示器，其中當波長為550nm時Rth 介於100nm至150nm範圍內。
- 如申請專利範圍第1項所述之液晶顯示器，其中所述第二補償層是雙軸膜或C板。
- 如申請專利範圍第7項所述之液晶顯示器，其中所述雙軸膜的同一平面的x方向和y方向的折射率(nx ,ny )與厚度方向的折射率(nz )滿足以下關係nx >ny >nz ，Re 大於0(Re >0)，且Rth 小於0(Rth <0)。
- 如申請專利範圍第7項所述之液晶顯示器，其中所述雙軸膜是環烯聚合物、三乙酸纖維素或聚醚碸補償膜。
- 如申請專利範圍第7項所述之液晶顯示器，其中所述C板是環烯聚合物或丙烯酸補償膜，其同一平面的x方向及y方向的折射率(nx ,ny )與厚度方向的折射率(nz )滿足以下關係nx =ny <nz ，且Rth 大於0(Rth >0)。
- 如申請專利範圍第1項所述之液晶顯示器，其中所述第一補償層的慢軸垂直於所述第二補償層的慢軸，所述第一補償層的慢軸垂直於所述第一偏光層的吸收軸，所述第二補償層的慢軸垂直於所述第二偏光層的吸收軸。
- 一種補償膜，包括由馬來醯亞胺衍生的重複單元、由芳香族乙烯基衍生的重複單元、由順丁烯二酐衍生 的重複單元以及由丙烯腈化合物衍生的重複單元，其中波長為550nm時所述補償膜的Re 為40nm至100nm。
- 如申請專利範圍第12項所述之補償膜，其中所述補償膜具有：Cs 為-0.7至-0.2；以及波長為550nm時Rth 為100nm至150nm。