CN1615698A - 复合抗菌剂 - Google Patents
复合抗菌剂 Download PDFInfo
- Publication number
- CN1615698A CN1615698A CN 200310113356 CN200310113356A CN1615698A CN 1615698 A CN1615698 A CN 1615698A CN 200310113356 CN200310113356 CN 200310113356 CN 200310113356 A CN200310113356 A CN 200310113356A CN 1615698 A CN1615698 A CN 1615698A
- Authority
- CN
- China
- Prior art keywords
- zinc oxide
- silica
- controlled
- sent
- homogenizing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种复合抗菌剂，它由以下重量百分比的原料组成，碳酸银48.76－50、氧化锌38.75－41.32、二氧化硅9.92－11.25。其制备方法是将碳酸银、氧化锌、二氧化硅按重量百分比配合在一起，然后放入球磨机内均化混合，将均化混合后的物料送入高温熔块电炉内煅烧，将煅烧后的物料送入震动搅拌研磨机内加工磨细，经过磨细后的粉状物料进入间歇式干燥器内进行烘干干燥，将干燥后的物料再送入筛网式制粉机内制粉，将制备的粉状物料避光包装即可。本发明组方及制备方法、加工工艺简单、先进合理，材料易购，投资小，生产成本低，适应范围广，无环境污染，抗菌抑菌效果稳定、作用时间长，是现有抗菌剂的理想替代品。
Description
技术领域：
本发明涉及一种抗菌剂，特别涉及一种复合抗菌剂。
背景技术：
随着人们生活水平的提高和保健意识的增强，人们对工作和家庭环境卫生日益重视，尽量减少周围环境滋生的细菌对人体的侵害，进入九十年代后期，世界各国开始积极研制抗菌剂及抗菌制品，使得抗菌陶瓷、抗菌布料、抗菌涂料、抗菌餐具等日常用品应运而生，并涉及到造纸、家电、汽车、油漆、涂料、陶瓷、日常用品等诸多行业，但现有的各种抗菌剂的组方及制备方法、加工工艺复杂，投资大，生产成本高，适应范围小，易造成环境污染，并且抗菌效果均不理想。
发明内容：
本发明的目的就在于克服现有技术中的不足之处，提供一种组方及制备方法、加工工艺简单，投资小，生产成本低，适应范围广，无环境污染，并且抗菌效果理想的复合抗菌剂。
本发明的目的是这样实现的，它由以下重量百分比的原料组成，碳酸银48.76-50、氧化锌38.75-41.32、二氧化硅9.92-11.25。其制备方法包括以下工艺步骤：用电子秤将碳酸银、氧化锌、二氧化硅按重量百分比配合在一起，将配好的物料放入球磨机内均化混合，将均化混合后的物料送入高温熔块电炉内煅烧，煅烧温度控制在1000℃-1200℃，时间控制在10小时-14小时，将煅烧后的物料送入震动搅拌研磨机内加工磨细，经过磨细后的粉状物料进入间歇式干燥器内进行烘干干燥，使其水分含量在3％以下，将干燥后的物料再送入筛网式制粉机内制粉，粒度控制在5um-45um，将制备的粉状物料避光包装即可。
本实用新型的目的也可以通过以下技术措施来实现，其成品氧化物含量为：氧化银42％-46％、氧化锌36％-44％、二氧化硅8％-10％。
相比现有技术，本发明具有组方及制备方法、加工工艺简单、先进合理，材料易购，投资小，生产成本低，适应范围广，无环境污染，抗菌抑菌效果稳定、作用时间长等优点。
附图说明：
附图为本发明工艺流程图
具体实施方式：
下面结合附图及实施例详述本发明，它由以下重量百分比的原料组成，碳酸银48.76-50、氧化锌38.75-41.32、二氧化硅9.92-11.25。其制备方法包括以下工艺步骤：用电子秤将碳酸银、氧化锌、二氧化硅按重量百分比配合在一起，将配好的物料放入球磨机内均化混合，将均化混合后的物料送入高温熔块电炉内煅烧，煅烧温度控制在1000℃-1200℃，时间控制在10小时-14小时，将煅烧后的物料送入震动搅拌研磨机内加工磨细，经过磨细后的粉状物料进入间歇式干燥器内进行烘干干燥，使其水分含量在3％以下，将干燥后的物料再送入筛网式制粉机内制粉，粒度控制在5um-45um，将制备的粉状物料避光包装即可。其成品氧化物含量为：氧化银42％-46％、氧化锌36％-44％、二氧化硅8％-10％。
下面是本发明1000g的具体实施例：(表一)
表一：
| 组分 | 实施例1 | 实施例2 | 实施例3 | |||
| 重量百分比％ | 重量g | 重量百分比％ | 重量g | 重量百分比％ | 重量g | |
| 碳酸银 | 50 | 500 | 50 | 500 | 48.76 | 487.6 |
| 氧化锌 | 38.75 | 387.5 | 40 | 400 | 41.32 | 413.2 |
| 二氧化硅 | 11.25 | 112.5 | 10 | 100 | 9.92 | 99.2 |
| 合计 | 100 | 1000 | 100 | 1000 | 100 | 1000 |
将表一中各组分用电子秤将碳酸银、氧化锌、二氧化硅按重量百分比配合在一起，然后将配好的物料放入球磨机内均化混合，将均化混合后的物料送入高温熔块电炉内煅烧，煅烧温度控制在1100℃，时间控制在12小时，然后取出、降温，将煅烧后的物料送入震动搅拌研磨机内加工磨细，经过磨细后的粉状物料进入间歇式干燥器内进行烘干干燥，使其水分含量在3％以下，将干燥后的物料再送入筛网式制粉机内制粉，粒度控制在5um-45um，将制备的粉状物料避光包装即可。其成品氧化物含量为：氧化银42％-46％、氧化锌36％-44％、二氧化硅8％-10％。满足不同行业的需求，本发明可广泛用于造纸、家电、汽车、油漆、涂料、陶瓷、日常用品等诸多行业，制作各种抗菌制品，有效保证人身健康，将本发明用在陶瓷行业既赋予了陶瓷用品的自洁功能，具有抗菌、抑菌作用，还可有效的提高陶瓷釉面的质量，增加釉面光泽度和平整度，本发明组方及制备方法、加工工艺简单、先进合理，材料易购，投资小，生产成本低，适应范围广，无环境污染，抗菌抑菌效果稳定、作用时间长，是现有抗菌剂的理想替代品。
Claims (3)
1.一种复合抗菌剂，其特征在于：它由以下重量百分比的原料组成，碳酸银48.76-50、氧化锌38.75-41.32、二氧化硅9.92-11.25。
2.根据权利要求1所述复合抗菌剂的制备方法，其特征在于：它包括以下工艺步骤：
a.配料：用电子秤将碳酸银、氧化锌、二氧化硅按重量百分比配合在一起；
b.均化混合：将配好的物料放入球磨机内均化混合；
c.煅烧：将均化混合后的物料送入高温熔块电炉内煅烧，煅烧温度控制在1000℃-1200℃，时间控制在10小时-14小时；
d.研磨：将煅烧后的物料送入震动搅拌研磨机内加工磨细；
e.干燥：经过磨细后的粉状物料进入间歇式干燥器内进行烘干干燥，使其水分含量在3％以下；
f.制粉：将干燥后的物料送入筛网式制粉机内制粉，粒度控制在5um-45um；
g.包装：将制备的粉状物料避光包装即可；
3.根据权利要求1所述复合抗菌剂，其特征在于：其成品氧化物含量为：氧化银42％-46％、氧化锌36％-44％、二氧化硅8％-10％。